The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage allo...The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.展开更多
In order to improve the cycle stability of La-Mg-Ni-Co type alloy electrode, rapid quenching technology was employed. The effects of rapid quenching on the microstructure and cycle stability of the alloy were investig...In order to improve the cycle stability of La-Mg-Ni-Co type alloy electrode, rapid quenching technology was employed. The effects of rapid quenching on the microstructure and cycle stability of the alloy were investigated. The obtained results show that the La2Mg(Ni0.85Co0.15)9M0.1 (M=B, Cr) alloy electrodes are composed of (La, Mg)Ni3 phase, LaNi5 phase and a small amount of the LaNi2 phase. A trace of the Ni2B phase exists in the as-cast MB alloy, and the Ni2B phase in the alloy nearly disappears after rapid quenching. Rapid quenching technology can slightly improve the cycling life of the alloy. When the quenching rate increases from 0 m·s-1 (As-cast is defined as quenching rate of 0 m·s-1) to 30 m·s-1, the cycle lives of the MB, MCr alloys enhance from 86 and 87 cycles to 106 and 119 cycles, respectively. On the other hand, the average capacity decay rates of the MB, MCr alloys decrease from 1.7172 and 1.7178 mAh·g-1·cycle-1 to 1.5751 and 1.3060 mAh·g-1·cycle-1 after 86 charge-discharges cycling, respectively.展开更多
In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 ...In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 (x=0, 2) alloys were synthesized by melt-spinning technique. The microstructures of the as-spun alloys were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The electrochemical hydrogen storage properties of the experimental alloys were tested. The results show that no amorphous phase is detected in the as-spun Mg20Ni10 alloy, but the as-spun Mg18La2Ni10 alloy holds a major amorphous phase. As La content increases from 0 to 2, the maximum discharge capacity of the as-spun (20 m/s) alloys rises from 96.5 to 387.1 mA·h/g, and the capacity retaining rate (S20) at the 20th cycle grows from 31.3% to 71.7%. Melt-spinning engenders an impactful effect on the electrochemical hydrogen storage performances of the alloys. With the increase in the spinning rate from 0 to 30 m/s, the maximum discharge capacity increases from 30.3 to 135.5 mA·h/g for the Mg20Ni10 alloy, and from 197.2 to 406.5 mA·h/g for the Mg18La2Ni10 alloy. The capacity retaining rate (S20) of the Mg20Ni10 alloy at the 20th cycle slightly falls from 36.7% to 27.1%, but it markedly mounts up from 37.3% to 78.3% for the Mg18La2Ni10 alloy.展开更多
The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox (x = 0, 0.1, 0.2, 0.3, 0.4) alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD,...The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox (x = 0, 0.1, 0.2, 0.3, 0.4) alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD, SEM and HRTEM. The gaseous hydrogen storage kinetics of the alloys was measured using an automatically controlled Sieverts apparatus. The alloy electrodes were charged and discharged with a constant current density in order to investigate the electrochemical hydrogen storage kinetics of the alloys. The results demonstrate that the substitution of Co for Ni results in the formation of secondary phases MgCo2 and Mg instead of altering the major phase Mg2Ni. No amorphous phase is detected in the as-quenched Co- ffee alloy, however, a certain amount of amorphous phase is clearly found in the as-quenched alloys substituted by Co. Furthermore, both the rapid quenching and the Co substitution significantly improve the gaseous and electrochemical hydrogen storage kinetics of the alloys, for which the notable increase of the hydrogen diffusion coefficient (D) along with the limiting current density (IL) and the obvious decline of the electrochemical impedance generated by both the Co substitution and the rapid quenching are basically responsible.展开更多
Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were char...Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were characterized by XRD,SEM and HRTEM.The electrochemical hydrogen storage performances were tested by an automatic galvanostatic system.The hydriding and dehydriding kinetics of the alloys were measured using an automatically controlled Sieverts apparatus.The results show that all the as-quenched alloys hold the typical nanocrystalline structure and the rapid quenching does not change the major phase Mg2Ni.The rapid quenching significantly improves the electrochemical hydrogen storage capacity of the alloys,whereas it slightly impairs the cycling stability of the alloys.Additionally,the hydrogen absorption and desorption capacities of the alloys significantly increase with rising quenching rate.展开更多
Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is ...Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity (378 mAh·g^-1), and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability (S270 = 81%).展开更多
Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hy...Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hydrogen and enhance the utilization of borohydride, Ti/Zr metal powders has been added into the parent LmNi4.78Mn0.22 (where Lm is La-richened mischmetal) alloy (LNM) by ball milling and heat treatment methods. It is found that the addition of Ti/Zr metal powders lowers the electrochemical catalytic activity of the electrodes, at the same time, restrains the generation of hydrogen and enhances the utilization of the fuel. All the results show that the hydrogen generation rate or the utilization of the fuel is directly relative to the electrochemical catalytic activity or the discharge capability of the electrodes. The utilization of the fuel increases with discharge current density. It is very important to find a balance between the discharge capability and the utilization of the fuel.展开更多
Low-temperature performance and high-rate discharge capability of AB5-type non-stoichiometric hydrogen storage are studied. X-ray diffraction(XRD),pressure-composition-temperature(PCT) curves and electrochemical imped...Low-temperature performance and high-rate discharge capability of AB5-type non-stoichiometric hydrogen storage are studied. X-ray diffraction(XRD),pressure-composition-temperature(PCT) curves and electrochemical impedance spectroscopy(EIS) are applied to characterize the electrochemical properties of ABx(x=4.8,4.9,5.0,5.1,5.2) alloys. The results show that the non-stoichiometric alloys exhibit better electrochemical properties compared with that of the AB5 alloy.展开更多
Nanocrystalline and amorphous Mg-Nd-Ni-Cu quaternary alloys with a composition of(Mg_(24)Ni_(10)Cu_2)_(100-x)Nd_x(x=0, 5, 10, 15, 20) were prepared by melt spinning technology and their structures as well as gaseous h...Nanocrystalline and amorphous Mg-Nd-Ni-Cu quaternary alloys with a composition of(Mg_(24)Ni_(10)Cu_2)_(100-x)Nd_x(x=0, 5, 10, 15, 20) were prepared by melt spinning technology and their structures as well as gaseous hydrogen storage characteristics were investigated. The XRD, TEM and SEM linked with EDS detections reveal that the as-spun Nd-free alloy holds an entire nanocrystalline structure but a nanocrystalline and amorphous structure for the as-spun Nd-added alloy, implying that the addition of Nd facilitates the glass forming in the Mg_2Ni-type alloy. Furthermore, the degree of amorphization of the as-spun Nd-added alloy and thermal stability of the amorphous structure clearly increase with the spinning rate rising. The melt spinning ameliorates the hydriding and dehydriding kinetics of the alloys dramatically. Specially, the rising of the spinning rate from 0(the as-cast was defined as the spinning rate of 0 m/s) to 40 m/s brings on the hydrogen absorption saturation ratio(R_5~a)(a ratio of the hydrogen absorption quantity in 5 min to the saturated hydrogen absorption capacity) increasing from 36.9% to 91.5% and the hydrogen desorption ratio(R_(1 0)~d)(a ratio of the hydrogen desorption quantity in 10 min to the saturated hydrogen absorption capacity) rising from 16.4% to 47.7% for the(x=10) alloy, respectively.展开更多
A series of hydrogen storage Co-free AB3-type alloys were directly synthesized with vacuum mid-frequency melting method,within which Ni of La0.7Mg0.3Ni3 alloy was substituted by Fe,B and(FeB) alloy,respectively.Alloys...A series of hydrogen storage Co-free AB3-type alloys were directly synthesized with vacuum mid-frequency melting method,within which Ni of La0.7Mg0.3Ni3 alloy was substituted by Fe,B and(FeB) alloy,respectively.Alloys were characterized by XRD,EDS and SEM to investigate the effects of B and Fe substitution for Ni on material structure.The content of LaMg2Ni9 phase within La0.7Mg0.3Ni3 alloy reaches 37.9% and that of La0.7Mg0.3Ni2.9(FeB)0.1 alloys reduces to 23.58%.Among all samples,ground particles with different shapes correspond to different phases.The major substitution occurs in LaMg2Ni9 phase.Electrochemical tests indicate that substituted alloys have different electrochemical performance,which is affected by phase structures of alloy.The discharge capacity of La0.7Mg0.3Ni3 alloy reaches 337.3 mA·h/g,but La0.7Mg0.3Ni2.9(FeB)0.1 alloy gets better high rate discharge(HRD) performance at the discharge rate of 500 mA/g with a high HRD value of 73.19%.展开更多
Perovskite-type SrTiO3 powders were prepared by using strontium acetate, tetrabutyl titanate and sodium hydroxide via direct hydrolysis-precipitation process. AB5-type hydrogen storage alloy(HSA) electrodes modified...Perovskite-type SrTiO3 powders were prepared by using strontium acetate, tetrabutyl titanate and sodium hydroxide via direct hydrolysis-precipitation process. AB5-type hydrogen storage alloy(HSA) electrodes modified with SrTiO3 powders were prepared and the photoelectrochemical characteristics of the as-prepared electrodes were investigated. The results of cyclic voltammograph show that the current of reduction peak increases remarkably under the light irradiation. The obvious photochargeable properties are obtained for the hydrogen storage alloys modified with Perovskite-type SrTiO3 powders. During photocharging process, the potential of the electrode shifts quickly to negative direction and a potential plateau occurs. HSA electrode modified with SrTiO3 powders prepared by direct hydrolysis-precipitation process gives the higher potential of about -0.90V(vs Hg/HgO) under the light irradiation. SEM observation discloses that a large amount of microcracks occur on the surface of the electrode after photocharging process, which is caused by the formation of hydride in the bulk of electrode.展开更多
Structure and electrochemical properties of (La, Ce, Pr, Nd)_2MgNi_9 hydrogen storage alloys were investigated through orthogonal design experiments, and the alloys were obtained through induction melting followed by ...Structure and electrochemical properties of (La, Ce, Pr, Nd)_2MgNi_9 hydrogen storage alloys were investigated through orthogonal design experiments, and the alloys were obtained through induction melting followed by annealing treatment. The structure of main phase in alloys belongs to PuNi_3-type with a space group R3m. Rare earth elements, as a substitute of lanthanum, have a significant effect on phase structure of alloys, elements of cerium and neodymium are beneficial to the formation of Gd_2Co_7-type phase with a space group P 6_3/mmc. Rare earth elements can decrease the unit cell volume of main phase of alloys dramatically, and increase the axis ratio. The results of electrochemical experiment showed that the discharge capacity of alloy electrodes ranged from 342.97 to 380.68 mAh·g -1, and elements of cerium and neodymium can reduce the discharge capacity of alloy electrodes significantly. Compared to the electrode of La_2MgNi_9 alloy, the substitution of lanthanum by rare earth elements did not improve the cyclic stability of alloy electrodes due to the anisotropic structure change of unit cell. While rare-earth elements can improve the high rate dischargeability of alloy electrodes, the high rate dischargeability of alloy electrodes could reach the maximum when the unit cell volume of PuNi_3-type structure was about 0532 nm.展开更多
The influences of the ratio of the radius of atom A(rA) to radius of atom B(rB), electronegativity and electron number were discussed on the Laves phase formation and the characteristics of Zr-based AB2 type hydro...The influences of the ratio of the radius of atom A(rA) to radius of atom B(rB), electronegativity and electron number were discussed on the Laves phase formation and the characteristics of Zr-based AB2 type hydrogen storage alloy. An enthalpy model of Zr-based AB2 alloy was obtained from known data and twelve Zr-based alloys were designed to test the model. The results show that the predicted values are in good agreement with the experimental values. The model can be used for predicting enthalpy values of Zr-based hydrogen storage alloys and settles a foundation for experiments.展开更多
In order to improve the gaseous and electrochemical hydrogen storage kinetics of the M2Nitype alloy, the elements Cu and Nd were added in the alloy. The nanocrystalline and amorphous Mg2Ni-type alloys with the composi...In order to improve the gaseous and electrochemical hydrogen storage kinetics of the M2Nitype alloy, the elements Cu and Nd were added in the alloy. The nanocrystalline and amorphous Mg2Ni-type alloys with the composition of(Mg24Ni10Cu2)100-xNdx(x = 0, 5, 10, 15, 20) were prepared by melt spinning technology. The effects of Nd content on the structures and hydrogen storage kinetics of the alloys were investigated. The characterization by X-ray diffraction(XRD), transmission electron microscopy(TEM) and scanning electron microscopy(SEM) reveals that all the as-cast alloys hold multiphase structures, containing Mg2Ni-type major phase as well as some secondary phases Mg6Ni, Nd5Mg41, and Nd Ni, whose amounts clearly grow with increasing Nd content. Furthermore, the as-spun Nd-free alloy displays an entire nanocrystalline structure, whereas the as-spun Nd-added alloys hold a mixed structure of nanocrystalline and amorphous structure and the amorphization degree of the alloys visibly increases with the rising of the Nd content, suggesting that the addition of Nd facilitates the glass forming in the Mg2Ni-type alloy. The measurement of the hydrogen storage kinetics indicates that the addition of Nd significantly improves the gaseous and electrochemical hydrogen storage kinetics of the alloys. The addition of Nd enhances the diffusion ability of hydrogen atoms in the alloy, but it impairs the charge-transfer reaction on the surface of the alloy electrode, which makes the high rate discharge ability(HRD) of the alloy electrode fi rst mount up and then go down with the growing of Nd content.展开更多
A partial substitution of Ni by Cu has been carried out in order to improve the hydrogen storage characteristics of the Mg2Ni-type alloys. The nanocrystalline Mg20Ni10-xCux (x = 0, 1, 2, 3, 4) alloys are synthesized b...A partial substitution of Ni by Cu has been carried out in order to improve the hydrogen storage characteristics of the Mg2Ni-type alloys. The nanocrystalline Mg20Ni10-xCux (x = 0, 1, 2, 3, 4) alloys are synthesized by the melt-spinning technique. The structures of the as-cast and spun alloys have been characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and high resolution transmission electron microscope (HRTEM). The electrochemical performances were evaluated by an automatic galvanostatic system. The hydrogen absorption and desorption kinetics of the alloys were determined by using an automatically controlled Sieverts apparatus. The results indicate that the substitution of Cu for Ni does not alter the major phase Mg2Ni. The Cu substitution significantly ameliorates the electrochemical hydrogen storage performances of alloys, involving both the discharge capacity and the cycle stability. The hydrogen absorption capacity of alloys has been observed to be first increase and then decrease with an increase in the Cu contents. However, the hydrogen desorption capacity of the alloys exhibit a monotonous growth with an increase in the Cu contents.展开更多
The Mg2Ni-type alloys with nominal compositions of Mg20Ni10-xCox(x=0,1,2,3,4,%,mass fraction) were prepared by melt-spinning technology.The structures of the alloys were studied by XRD,SEM and HRTEM.The hydrogen absor...The Mg2Ni-type alloys with nominal compositions of Mg20Ni10-xCox(x=0,1,2,3,4,%,mass fraction) were prepared by melt-spinning technology.The structures of the alloys were studied by XRD,SEM and HRTEM.The hydrogen absorption/desorption kinetics and the electrochemical performances of the alloys were measured.The results show that no amorphous phase forms in the as-spun Co-free alloy,but the as-spun alloys containing Co show a certain amount of amorphous phase.The hydrogen absorption capacities of the as-cast alloys first increase and then decrease with the incremental change of Co content.The hydrogen desorption capacities of as-cast and spun alloys rise with increasing Co content.The melt spinning significantly improves the hydrogenation and dehydrogenation capacities and kinetics of the alloys.The substitution of Co for Ni clearly enhances the discharge capacities of the alloys and the cycle stability of the as-spun alloys.展开更多
LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was ...LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.展开更多
In this work,a comprehensive comparison regarding the impacts of M(M=Cu,Co,Mn)substitution for Ni on the structures and the hydrogen storage kinetics of the nanocrystalline and amorphous Mg20Ni10-xMx(M=Cu,Co,Mn; x=0-4...In this work,a comprehensive comparison regarding the impacts of M(M=Cu,Co,Mn)substitution for Ni on the structures and the hydrogen storage kinetics of the nanocrystalline and amorphous Mg20Ni10-xMx(M=Cu,Co,Mn; x=0-4)alloys prepared by melt spinning has been carried out.The analysis of XRD and TEM reveals that the as-spun(M=None,Cu)alloys display an entire nanocrystalline structure,whereas the as-spun(M=Co,Mn)alloys hold a mixed structure of nanocrystalline and amorphous structure when M content x=4,indicating that the substitution of M(M=Co,Mn)for Ni facilitates the glass formation in the Mg2Ni-type alloy.Besides,all the as-spun alloys have a major phase of Mg2Ni but M(M=Co,Mn)substitution brings on the formation of some secondary phases,MgCo2 and Mg phases for M=Co as well as MnNi and Mg phases for M=Mn.Based upon the measurements of the automatic Sieverts apparatus and the automatic galvanostatic system,the impacts engendered by M(M=Cu,Co,Mn)substitution on the gaseous and electrochemical hydrogen storage kinetics of the alloys appear to be evident.The gaseous hydriding kinetics of the alloys first rises and then declines with the growing of M(M=Cu,Co,Mn)content.Particularly,the M(M= Mn)substitution results in a sharp drop in the hydriding kinetics when x=4.The M(M=Cu,Co,Mn)substitution ameliorates the dehydriding kinetics dramatically in the order(M=Co)>(M=Mn)>(M=Cu).The electrochemical kinetics of the alloys visibly grows with M content rising for(M=Cu,Co),while it first increases and then declines for(M=Mn).展开更多
The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the ...The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.展开更多
In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied system...In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied systematically. X-ray diffraction (XRD) and scanning electron microscope (SEM) showed that LaNi5 and La2Ni7 phases were invariably present in all alloy samples, and when x >= 0.4, (Fe, Ni) phase was observed. Electrochemical studies revealed that the discharge capacity reached a maximum value of 306.4 mAh/g when x=0.2 and the cycling stability decreased with the increase of x. With the increase of Mn content, hydrogen diffusion coefficient decreased, whereas high rate discharge-ability (HRD) and exchange current density first increased slowly when x <= 0.2 and then decreased markedly when x=0.8, indicating that electrochemical reaction on the surface of alloy electrodes had strong influence on kinetic property.展开更多
文摘The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.
基金This work was financially supported by National Natural Science Foundations of China (No.50131040)Key Technologies R & D Program of Inner Mongolia (No.20050205)College Scientific Research Project of Inner Mongolia (No.NJ05064).
文摘In order to improve the cycle stability of La-Mg-Ni-Co type alloy electrode, rapid quenching technology was employed. The effects of rapid quenching on the microstructure and cycle stability of the alloy were investigated. The obtained results show that the La2Mg(Ni0.85Co0.15)9M0.1 (M=B, Cr) alloy electrodes are composed of (La, Mg)Ni3 phase, LaNi5 phase and a small amount of the LaNi2 phase. A trace of the Ni2B phase exists in the as-cast MB alloy, and the Ni2B phase in the alloy nearly disappears after rapid quenching. Rapid quenching technology can slightly improve the cycling life of the alloy. When the quenching rate increases from 0 m·s-1 (As-cast is defined as quenching rate of 0 m·s-1) to 30 m·s-1, the cycle lives of the MB, MCr alloys enhance from 86 and 87 cycles to 106 and 119 cycles, respectively. On the other hand, the average capacity decay rates of the MB, MCr alloys decrease from 1.7172 and 1.7178 mAh·g-1·cycle-1 to 1.5751 and 1.3060 mAh·g-1·cycle-1 after 86 charge-discharges cycling, respectively.
基金Projects(50871050, 50961009) supported by the National Natural Science Foundation of ChinaProject(2010ZD05) supported by the Natural Science Foundation of Inner Mongolia, ChinaProject(NJzy08071) supported by the Higher Education Science Research Project of Inner Mongolia, China
文摘In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 (x=0, 2) alloys were synthesized by melt-spinning technique. The microstructures of the as-spun alloys were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The electrochemical hydrogen storage properties of the experimental alloys were tested. The results show that no amorphous phase is detected in the as-spun Mg20Ni10 alloy, but the as-spun Mg18La2Ni10 alloy holds a major amorphous phase. As La content increases from 0 to 2, the maximum discharge capacity of the as-spun (20 m/s) alloys rises from 96.5 to 387.1 mA·h/g, and the capacity retaining rate (S20) at the 20th cycle grows from 31.3% to 71.7%. Melt-spinning engenders an impactful effect on the electrochemical hydrogen storage performances of the alloys. With the increase in the spinning rate from 0 to 30 m/s, the maximum discharge capacity increases from 30.3 to 135.5 mA·h/g for the Mg20Ni10 alloy, and from 197.2 to 406.5 mA·h/g for the Mg18La2Ni10 alloy. The capacity retaining rate (S20) of the Mg20Ni10 alloy at the 20th cycle slightly falls from 36.7% to 27.1%, but it markedly mounts up from 37.3% to 78.3% for the Mg18La2Ni10 alloy.
基金Funded by National Natural Science Foundations of China(Nos.51161015 and 50961009)Natural Science Foundation of Inner Mongolia,China(Nos.2011ZD10 and 2010ZD05)Higher Education Science Research Project of Inner Mongolia,China(No.NJzy08071)
文摘The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox (x = 0, 0.1, 0.2, 0.3, 0.4) alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD, SEM and HRTEM. The gaseous hydrogen storage kinetics of the alloys was measured using an automatically controlled Sieverts apparatus. The alloy electrodes were charged and discharged with a constant current density in order to investigate the electrochemical hydrogen storage kinetics of the alloys. The results demonstrate that the substitution of Co for Ni results in the formation of secondary phases MgCo2 and Mg instead of altering the major phase Mg2Ni. No amorphous phase is detected in the as-quenched Co- ffee alloy, however, a certain amount of amorphous phase is clearly found in the as-quenched alloys substituted by Co. Furthermore, both the rapid quenching and the Co substitution significantly improve the gaseous and electrochemical hydrogen storage kinetics of the alloys, for which the notable increase of the hydrogen diffusion coefficient (D) along with the limiting current density (IL) and the obvious decline of the electrochemical impedance generated by both the Co substitution and the rapid quenching are basically responsible.
基金Project(2007AA03Z227) supported by High-tech Research and Development Program of ChinaProjects(50871050,50701011) supported by the National Natural Science Foundation of China+1 种基金Project(200711020703) supported by the Natural Science Foundation of Inner Mongolia,ChinaProject(NJzy08071) supported by High Education Science Research Project of Inner Mongolia,China
文摘Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were characterized by XRD,SEM and HRTEM.The electrochemical hydrogen storage performances were tested by an automatic galvanostatic system.The hydriding and dehydriding kinetics of the alloys were measured using an automatically controlled Sieverts apparatus.The results show that all the as-quenched alloys hold the typical nanocrystalline structure and the rapid quenching does not change the major phase Mg2Ni.The rapid quenching significantly improves the electrochemical hydrogen storage capacity of the alloys,whereas it slightly impairs the cycling stability of the alloys.Additionally,the hydrogen absorption and desorption capacities of the alloys significantly increase with rising quenching rate.
文摘Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity (378 mAh·g^-1), and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability (S270 = 81%).
文摘Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hydrogen and enhance the utilization of borohydride, Ti/Zr metal powders has been added into the parent LmNi4.78Mn0.22 (where Lm is La-richened mischmetal) alloy (LNM) by ball milling and heat treatment methods. It is found that the addition of Ti/Zr metal powders lowers the electrochemical catalytic activity of the electrodes, at the same time, restrains the generation of hydrogen and enhances the utilization of the fuel. All the results show that the hydrogen generation rate or the utilization of the fuel is directly relative to the electrochemical catalytic activity or the discharge capability of the electrodes. The utilization of the fuel increases with discharge current density. It is very important to find a balance between the discharge capability and the utilization of the fuel.
基金Project(2006AA11A151) supported by the National Hi-Tech Research and Development Program of China
文摘Low-temperature performance and high-rate discharge capability of AB5-type non-stoichiometric hydrogen storage are studied. X-ray diffraction(XRD),pressure-composition-temperature(PCT) curves and electrochemical impedance spectroscopy(EIS) are applied to characterize the electrochemical properties of ABx(x=4.8,4.9,5.0,5.1,5.2) alloys. The results show that the non-stoichiometric alloys exhibit better electrochemical properties compared with that of the AB5 alloy.
基金Projects(51161015,51371094)supported by the National Natural Science Foundation of China
文摘Nanocrystalline and amorphous Mg-Nd-Ni-Cu quaternary alloys with a composition of(Mg_(24)Ni_(10)Cu_2)_(100-x)Nd_x(x=0, 5, 10, 15, 20) were prepared by melt spinning technology and their structures as well as gaseous hydrogen storage characteristics were investigated. The XRD, TEM and SEM linked with EDS detections reveal that the as-spun Nd-free alloy holds an entire nanocrystalline structure but a nanocrystalline and amorphous structure for the as-spun Nd-added alloy, implying that the addition of Nd facilitates the glass forming in the Mg_2Ni-type alloy. Furthermore, the degree of amorphization of the as-spun Nd-added alloy and thermal stability of the amorphous structure clearly increase with the spinning rate rising. The melt spinning ameliorates the hydriding and dehydriding kinetics of the alloys dramatically. Specially, the rising of the spinning rate from 0(the as-cast was defined as the spinning rate of 0 m/s) to 40 m/s brings on the hydrogen absorption saturation ratio(R_5~a)(a ratio of the hydrogen absorption quantity in 5 min to the saturated hydrogen absorption capacity) increasing from 36.9% to 91.5% and the hydrogen desorption ratio(R_(1 0)~d)(a ratio of the hydrogen desorption quantity in 10 min to the saturated hydrogen absorption capacity) rising from 16.4% to 47.7% for the(x=10) alloy, respectively.
基金Project(2007AA11A104) supported by the High-tech Research and Development Program of ChinaProject(2009CB220100) supported by the National Basic Research Program of China
文摘A series of hydrogen storage Co-free AB3-type alloys were directly synthesized with vacuum mid-frequency melting method,within which Ni of La0.7Mg0.3Ni3 alloy was substituted by Fe,B and(FeB) alloy,respectively.Alloys were characterized by XRD,EDS and SEM to investigate the effects of B and Fe substitution for Ni on material structure.The content of LaMg2Ni9 phase within La0.7Mg0.3Ni3 alloy reaches 37.9% and that of La0.7Mg0.3Ni2.9(FeB)0.1 alloys reduces to 23.58%.Among all samples,ground particles with different shapes correspond to different phases.The major substitution occurs in LaMg2Ni9 phase.Electrochemical tests indicate that substituted alloys have different electrochemical performance,which is affected by phase structures of alloy.The discharge capacity of La0.7Mg0.3Ni3 alloy reaches 337.3 mA·h/g,but La0.7Mg0.3Ni2.9(FeB)0.1 alloy gets better high rate discharge(HRD) performance at the discharge rate of 500 mA/g with a high HRD value of 73.19%.
基金Project(50201016) supported by the National Natural Science Foundation of China Project(Y404044) supported by theNatural Science Foundation of Zhejiang Province
文摘Perovskite-type SrTiO3 powders were prepared by using strontium acetate, tetrabutyl titanate and sodium hydroxide via direct hydrolysis-precipitation process. AB5-type hydrogen storage alloy(HSA) electrodes modified with SrTiO3 powders were prepared and the photoelectrochemical characteristics of the as-prepared electrodes were investigated. The results of cyclic voltammograph show that the current of reduction peak increases remarkably under the light irradiation. The obvious photochargeable properties are obtained for the hydrogen storage alloys modified with Perovskite-type SrTiO3 powders. During photocharging process, the potential of the electrode shifts quickly to negative direction and a potential plateau occurs. HSA electrode modified with SrTiO3 powders prepared by direct hydrolysis-precipitation process gives the higher potential of about -0.90V(vs Hg/HgO) under the light irradiation. SEM observation discloses that a large amount of microcracks occur on the surface of the electrode after photocharging process, which is caused by the formation of hydride in the bulk of electrode.
文摘Structure and electrochemical properties of (La, Ce, Pr, Nd)_2MgNi_9 hydrogen storage alloys were investigated through orthogonal design experiments, and the alloys were obtained through induction melting followed by annealing treatment. The structure of main phase in alloys belongs to PuNi_3-type with a space group R3m. Rare earth elements, as a substitute of lanthanum, have a significant effect on phase structure of alloys, elements of cerium and neodymium are beneficial to the formation of Gd_2Co_7-type phase with a space group P 6_3/mmc. Rare earth elements can decrease the unit cell volume of main phase of alloys dramatically, and increase the axis ratio. The results of electrochemical experiment showed that the discharge capacity of alloy electrodes ranged from 342.97 to 380.68 mAh·g -1, and elements of cerium and neodymium can reduce the discharge capacity of alloy electrodes significantly. Compared to the electrode of La_2MgNi_9 alloy, the substitution of lanthanum by rare earth elements did not improve the cyclic stability of alloy electrodes due to the anisotropic structure change of unit cell. While rare-earth elements can improve the high rate dischargeability of alloy electrodes, the high rate dischargeability of alloy electrodes could reach the maximum when the unit cell volume of PuNi_3-type structure was about 0532 nm.
文摘The influences of the ratio of the radius of atom A(rA) to radius of atom B(rB), electronegativity and electron number were discussed on the Laves phase formation and the characteristics of Zr-based AB2 type hydrogen storage alloy. An enthalpy model of Zr-based AB2 alloy was obtained from known data and twelve Zr-based alloys were designed to test the model. The results show that the predicted values are in good agreement with the experimental values. The model can be used for predicting enthalpy values of Zr-based hydrogen storage alloys and settles a foundation for experiments.
基金Funded by the National Natural Science Foundations of China(Nos.51161015 and 51371094)
文摘In order to improve the gaseous and electrochemical hydrogen storage kinetics of the M2Nitype alloy, the elements Cu and Nd were added in the alloy. The nanocrystalline and amorphous Mg2Ni-type alloys with the composition of(Mg24Ni10Cu2)100-xNdx(x = 0, 5, 10, 15, 20) were prepared by melt spinning technology. The effects of Nd content on the structures and hydrogen storage kinetics of the alloys were investigated. The characterization by X-ray diffraction(XRD), transmission electron microscopy(TEM) and scanning electron microscopy(SEM) reveals that all the as-cast alloys hold multiphase structures, containing Mg2Ni-type major phase as well as some secondary phases Mg6Ni, Nd5Mg41, and Nd Ni, whose amounts clearly grow with increasing Nd content. Furthermore, the as-spun Nd-free alloy displays an entire nanocrystalline structure, whereas the as-spun Nd-added alloys hold a mixed structure of nanocrystalline and amorphous structure and the amorphization degree of the alloys visibly increases with the rising of the Nd content, suggesting that the addition of Nd facilitates the glass forming in the Mg2Ni-type alloy. The measurement of the hydrogen storage kinetics indicates that the addition of Nd significantly improves the gaseous and electrochemical hydrogen storage kinetics of the alloys. The addition of Nd enhances the diffusion ability of hydrogen atoms in the alloy, but it impairs the charge-transfer reaction on the surface of the alloy electrode, which makes the high rate discharge ability(HRD) of the alloy electrode fi rst mount up and then go down with the growing of Nd content.
文摘A partial substitution of Ni by Cu has been carried out in order to improve the hydrogen storage characteristics of the Mg2Ni-type alloys. The nanocrystalline Mg20Ni10-xCux (x = 0, 1, 2, 3, 4) alloys are synthesized by the melt-spinning technique. The structures of the as-cast and spun alloys have been characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and high resolution transmission electron microscope (HRTEM). The electrochemical performances were evaluated by an automatic galvanostatic system. The hydrogen absorption and desorption kinetics of the alloys were determined by using an automatically controlled Sieverts apparatus. The results indicate that the substitution of Cu for Ni does not alter the major phase Mg2Ni. The Cu substitution significantly ameliorates the electrochemical hydrogen storage performances of alloys, involving both the discharge capacity and the cycle stability. The hydrogen absorption capacity of alloys has been observed to be first increase and then decrease with an increase in the Cu contents. However, the hydrogen desorption capacity of the alloys exhibit a monotonous growth with an increase in the Cu contents.
基金Project(2006AA05Z132) supported by the National High-tech Research and Development Program of ChinaProjects(50871050,50701011) supported by the National Natural Science Foundation of China+1 种基金Project(200711020703) supported by Natural Science Foundation of Inner Mongolia,ChinaProject(NJzy08071) supported by High Education Science Research Program of Inner Mongolia,China
文摘The Mg2Ni-type alloys with nominal compositions of Mg20Ni10-xCox(x=0,1,2,3,4,%,mass fraction) were prepared by melt-spinning technology.The structures of the alloys were studied by XRD,SEM and HRTEM.The hydrogen absorption/desorption kinetics and the electrochemical performances of the alloys were measured.The results show that no amorphous phase forms in the as-spun Co-free alloy,but the as-spun alloys containing Co show a certain amount of amorphous phase.The hydrogen absorption capacities of the as-cast alloys first increase and then decrease with the incremental change of Co content.The hydrogen desorption capacities of as-cast and spun alloys rise with increasing Co content.The melt spinning significantly improves the hydrogenation and dehydrogenation capacities and kinetics of the alloys.The substitution of Co for Ni clearly enhances the discharge capacities of the alloys and the cycle stability of the as-spun alloys.
文摘LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.
基金Projects(51161015,51371094)supported by National Natural Science Foundations of ChinaProject(2011ZD10)supported by Natural Science Foundation of Inner Mongolia,China
文摘In this work,a comprehensive comparison regarding the impacts of M(M=Cu,Co,Mn)substitution for Ni on the structures and the hydrogen storage kinetics of the nanocrystalline and amorphous Mg20Ni10-xMx(M=Cu,Co,Mn; x=0-4)alloys prepared by melt spinning has been carried out.The analysis of XRD and TEM reveals that the as-spun(M=None,Cu)alloys display an entire nanocrystalline structure,whereas the as-spun(M=Co,Mn)alloys hold a mixed structure of nanocrystalline and amorphous structure when M content x=4,indicating that the substitution of M(M=Co,Mn)for Ni facilitates the glass formation in the Mg2Ni-type alloy.Besides,all the as-spun alloys have a major phase of Mg2Ni but M(M=Co,Mn)substitution brings on the formation of some secondary phases,MgCo2 and Mg phases for M=Co as well as MnNi and Mg phases for M=Mn.Based upon the measurements of the automatic Sieverts apparatus and the automatic galvanostatic system,the impacts engendered by M(M=Cu,Co,Mn)substitution on the gaseous and electrochemical hydrogen storage kinetics of the alloys appear to be evident.The gaseous hydriding kinetics of the alloys first rises and then declines with the growing of M(M=Cu,Co,Mn)content.Particularly,the M(M= Mn)substitution results in a sharp drop in the hydriding kinetics when x=4.The M(M=Cu,Co,Mn)substitution ameliorates the dehydriding kinetics dramatically in the order(M=Co)>(M=Mn)>(M=Cu).The electrochemical kinetics of the alloys visibly grows with M content rising for(M=Cu,Co),while it first increases and then declines for(M=Mn).
文摘The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.
基金Project supported by the National Nature Science Foundation of China (NSFC50571072)GD-MOE Coordination Project of Industry Academic and Research (2008B090500274)
文摘In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied systematically. X-ray diffraction (XRD) and scanning electron microscope (SEM) showed that LaNi5 and La2Ni7 phases were invariably present in all alloy samples, and when x >= 0.4, (Fe, Ni) phase was observed. Electrochemical studies revealed that the discharge capacity reached a maximum value of 306.4 mAh/g when x=0.2 and the cycling stability decreased with the increase of x. With the increase of Mn content, hydrogen diffusion coefficient decreased, whereas high rate discharge-ability (HRD) and exchange current density first increased slowly when x <= 0.2 and then decreased markedly when x=0.8, indicating that electrochemical reaction on the surface of alloy electrodes had strong influence on kinetic property.