A series of Cr^(3+)-substituted Na_(1+x)Ti_(2−x)Cr_(x)P_(3)O_(12)(x=0.1,0.2,0.3,0.4,0.5,molar fraction)solid electrolytes were prepared by the solid-phase reaction method.The effects of Cr^(3+)ions on the phase compos...A series of Cr^(3+)-substituted Na_(1+x)Ti_(2−x)Cr_(x)P_(3)O_(12)(x=0.1,0.2,0.3,0.4,0.5,molar fraction)solid electrolytes were prepared by the solid-phase reaction method.The effects of Cr^(3+)ions on the phase composition,microstructure,and electrochemical ion conductivity of Na-based conductors were studied using X-ray powder diffraction,field emission scanning electron microscopy,and AC impedance measurement.The results show that the main crystal phase of NaTi_(2)(PO_(4))_(3) is formed in the solid electrolytes.The substitution of Ti4+sites by 15 at.%Cr^(3+)ions contributes to the enhancement of electrical conductivity,which is attributed to the combined effect of suppressing the formation of impurity phases,broadening ion channels,and improving the bonding degree of grains.Na_(1.3)Ti_(1.7)Cr_(0.3)P_(3)O_(12) electrolyte can obtain the best ionic conductivity of 6.13×10^(−6)S/cm at room temperature,which is 8 times that of the undoped NaTi_(2)(PO_(4))_(3) electrolyte.展开更多
基金supported by the National Natural Science Foundation of China(No.51972344)the Natural Science Foundation of Hunan Province,China(No.2018JJ3646).
文摘A series of Cr^(3+)-substituted Na_(1+x)Ti_(2−x)Cr_(x)P_(3)O_(12)(x=0.1,0.2,0.3,0.4,0.5,molar fraction)solid electrolytes were prepared by the solid-phase reaction method.The effects of Cr^(3+)ions on the phase composition,microstructure,and electrochemical ion conductivity of Na-based conductors were studied using X-ray powder diffraction,field emission scanning electron microscopy,and AC impedance measurement.The results show that the main crystal phase of NaTi_(2)(PO_(4))_(3) is formed in the solid electrolytes.The substitution of Ti4+sites by 15 at.%Cr^(3+)ions contributes to the enhancement of electrical conductivity,which is attributed to the combined effect of suppressing the formation of impurity phases,broadening ion channels,and improving the bonding degree of grains.Na_(1.3)Ti_(1.7)Cr_(0.3)P_(3)O_(12) electrolyte can obtain the best ionic conductivity of 6.13×10^(−6)S/cm at room temperature,which is 8 times that of the undoped NaTi_(2)(PO_(4))_(3) electrolyte.