Influence of acid leaching and calcination on iron removal of coal kaolin

Calcination and acid leaching of coal kaolin were studied to determine an effective and economical preparation method of calcined kaolin. Thermogravimetric-differential thermal analysis （TG-DTA） and X-ray diffraction （XRD） demonstrated that 900＆#176;C was the suitable temperature for the calcination. Leaching tests showed that hydrochloric acid was more effective for iron dissolution from raw coal kaolin （RCK）, whereas oxalic acid was more effective on iron dissolution from calcined coal kaolin （CCK）. The iron dissolution from CCK was 28.78wt%, which is far less effective than the 54.86wt% of RCK under their respective optimal conditions. Through analysis by using M？ssbauer spectroscopy, it is detected that nearly all of the structural ferrous ions in RCK were removed by hydrochloric acid. However, iron sites in CCK changed slightly by oxalic acid leaching because nearly all ferrous ions were transformed into ferric species after firing at 900＆#176;C. It can be concluded that it is difficult to remove the structural ferric ions and ferric oxides evolved from the structural ferrous ions. Thus, iron removal by acids should be conducted prior to calcination.

Short range order transformation and magnetostriction of Fe_(83)Ga_(17) ribbons

The relationship between magnetostriction and structure of melt-spun Fes3Ga17 ribbons are investigated by XRD and M5ssbauer spectrum technique （MS）. As the heat-treatment temperature increases from 650℃ to 800℃, the magnetostriction coefficient of Fes3Ga17 ribbon first increases and then decreases. The largest magnetostriction coeiffcient （-578.4 ppm） is achieved in those specimens quenched at 750oc. According to the XRD and MSssbauer spectrum anal- ysis, a small quantity of DO3 phase is precipitated in Fe83Ga17 ribbons when quenched from 650℃ and the DO3 phase is gradually transformed into B2-1ike phase if quenched at higher temperature. However, both DO3 and B2-1ike phases disappear when the temperature increases up to 800℃. From this point of view, B2-1ike phase might be beneficial to the enhancement of magnetostrictive properties of melt-spun ribbons.

Defects and hyperfine interactions in binary Fe-Al alloys studied by positron annihilation and Mssbauer spectroscopies

The defects, the behavior of 3d electrons and the hyperfine interactions in binary Fe-Al alloys with different Al contents have been studied by measurements of positron lifetime spectra, coincidence Doppler broadening spectra of positron annihilation radiation and M？ssbauer spectra. The results show that on increasing the Al content in Fe-Al alloys, the mean positron lifetime of the alloys increase, while the mean electron density of the alloys decrease. The increase of Al content in binary Fe-Al alloys will decrease the amount of unpaired 3d electrons; as a consequence the probability of positron annihilation with 3d electrons and the hyperfine field decrease rapidly. M？ssbauer spectra of binary Fe-Al alloys with Al content less than 25 at.% show discrete sextets and these alloys make a ferromagnetic contribution at room temperature. The M？ssbauer spectrum of Fe70Al30 shows a broad singlet. As Al content higher than 40 at.%, the M？ssbauer spectra of these alloys are singlet, that is, the alloys are paramagnetic. The behavior of a 3d electron and its effect on the hyperfine field of the binary Fe-Al alloy has been discussed.