Magnesium aluminate spinel -corundum composite was prepared with waste slide plate and magnesia carbon brick. Microstructure and sintering ability of as-prepared magnesium aluminate spinel -corundum composite were inv...Magnesium aluminate spinel -corundum composite was prepared with waste slide plate and magnesia carbon brick. Microstructure and sintering ability of as-prepared magnesium aluminate spinel -corundum composite were investigated with XRD, SEM, and DSC/TG. With the addition of waste slide plate increasing or synthesis tem- perature rising, the bulk density of the specimen increases and the apparent porosity decreases, but the crystallinity of the specimen decreases and the magnesium alaminate spinel phase increases. The obtained composite contains 72% spinel and 26% corundum. Primary phase and secondary phase are bonded by glass phase. The results show that it is feasible to synthesis magnesium aluminate spinel - corundum material with waste slide plate and magnesia carbon brick.展开更多
In some steel making workshops, the existed inher- ent weaknesses of traditional carbon containing brick working lining, such as joint opening, vertical cracking of lining, and excessive erosion of brick edge, made it...In some steel making workshops, the existed inher- ent weaknesses of traditional carbon containing brick working lining, such as joint opening, vertical cracking of lining, and excessive erosion of brick edge, made it hard to satis]~ the demands of advanced steel produc- tion. A new-type carbon free corundum spinel brick and castable were developed based on the matrix optimized analysis, successfully applied for ultra-low carbon steel production. The advantages of the newly developed car- bon free working lining are mainly as follows： I ） the inherent weaknesses of joint opening, vertical cracking of lining, excessive erosion of brick edge, etc. are sur- mounted successfully, which improves the operational safety of ladles; 2 ） the outer temperature of the ladle shell decreases by 45 -50 ℃ compared with that of the traditional carbon containing brick lining; 3） the service life of new-type working lining is 150 -170 heats, near- ly doubling that of the traditional carbon containing brick lining; the specific eonaumption of refractories per ton steel decreases by about 20% ; 4） the carbon pickup of mohen steel is not obvious which is merely 5 - 10 ppm, which satisfies the demands of low ＆ ultra low carbon steel production.展开更多
为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和...为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和α-氧化铝微粉加入量分别为3%和8%时,试验砖的性能最佳。该砖在太钢90 t LF钢包熔池及包底部位使用,其寿命达到105炉。展开更多
文摘Magnesium aluminate spinel -corundum composite was prepared with waste slide plate and magnesia carbon brick. Microstructure and sintering ability of as-prepared magnesium aluminate spinel -corundum composite were investigated with XRD, SEM, and DSC/TG. With the addition of waste slide plate increasing or synthesis tem- perature rising, the bulk density of the specimen increases and the apparent porosity decreases, but the crystallinity of the specimen decreases and the magnesium alaminate spinel phase increases. The obtained composite contains 72% spinel and 26% corundum. Primary phase and secondary phase are bonded by glass phase. The results show that it is feasible to synthesis magnesium aluminate spinel - corundum material with waste slide plate and magnesia carbon brick.
文摘In some steel making workshops, the existed inher- ent weaknesses of traditional carbon containing brick working lining, such as joint opening, vertical cracking of lining, and excessive erosion of brick edge, made it hard to satis]~ the demands of advanced steel produc- tion. A new-type carbon free corundum spinel brick and castable were developed based on the matrix optimized analysis, successfully applied for ultra-low carbon steel production. The advantages of the newly developed car- bon free working lining are mainly as follows： I ） the inherent weaknesses of joint opening, vertical cracking of lining, excessive erosion of brick edge, etc. are sur- mounted successfully, which improves the operational safety of ladles; 2 ） the outer temperature of the ladle shell decreases by 45 -50 ℃ compared with that of the traditional carbon containing brick lining; 3） the service life of new-type working lining is 150 -170 heats, near- ly doubling that of the traditional carbon containing brick lining; the specific eonaumption of refractories per ton steel decreases by about 20% ; 4） the carbon pickup of mohen steel is not obvious which is merely 5 - 10 ppm, which satisfies the demands of low ＆ ultra low carbon steel production.
文摘为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和α-氧化铝微粉加入量分别为3%和8%时,试验砖的性能最佳。该砖在太钢90 t LF钢包熔池及包底部位使用,其寿命达到105炉。