Poly(ethylene terephthalate) (PET)/carbon black (CB) masterbatch was prepared by melt blending using a separate feeding technique and its homogeneous dispersion morphology was confirmed by transmission electron micros...Poly(ethylene terephthalate) (PET)/carbon black (CB) masterbatch was prepared by melt blending using a separate feeding technique and its homogeneous dispersion morphology was confirmed by transmission electron microscope (TEM). The Avrami and Hoffman-Lauritzen secondary nucleation theories were employed to analyze the effect of high CB content on crystallization kinetics of PET, providing theoretical support for the development of masterbatch with high content of functional components. The Avrami exponents,average values of n,for PET and PET/CB masterbatch are both greater than 3, which indicates three-dimensional growth of crystals. In addition,no significant evidence for regime transition of PET is found applying Hoffman-Lauritzen secondary nucleation theory,though such observations have been reported previously in the literature. Furthermore,appropriate U* value for PET is determined to be 12 800 J/mol. For PET/CB masterbatch,a transition from regime I to regime II around 225℃ is observed with appropriate U* value (12 800 J/mol) . This phenomenon is consistent with a transition point in plot of G versus Tc . The fold surface free energy σe (100. 3 mJ/m 2) of PET is much greater than that of PET/CB masterbatch (48. 3 mJ/m 2) ,which indicates heterogeneous nucleation effect of CB particles.展开更多
In order to effectively control the drug-release rate of medical textiles,biodegradable polycaprolactone(PCL) and polyglycolic acid(PGA) were blended at various mass ratios to prepare composite masterbatches for medic...In order to effectively control the drug-release rate of medical textiles,biodegradable polycaprolactone(PCL) and polyglycolic acid(PGA) were blended at various mass ratios to prepare composite masterbatches for medical textiles.The surface morphology and the chemical structure of the masterbatches were analyzed.The crystallization,mass losses,strengths and drug-release rates of the composite masterbatches at different PCL/PGA mass ratios were explored.The results show that the degradation rate of the PGA carrier is obvious higher than that of the PCL carrier,and PCL,PGA and the tea polyphenol(TP) drug just physically mix without chemical reaction.During the degradation,the strength of the composite masterbatches gradually decreases.In addition,the drug-release rates of composite masterbatches at different mass ratios are different,and the more the PGA in the composite masterbatches,the faster the drug release of the composite masterbatches.The drug-release rate of the composite masterbatches can be controlled by adjusting the contents of PCL and PGA.展开更多
为降低紫外线对聚丙烯(Polyethylene,PP)非织造土工布的影响,选择ES(Ethylene-Propylene Side By Side)纤维和含有抗老化母粒的PP纤维为原料,TiO_(2)浸轧处理为后整理工序,采用针刺加固和热黏合加固技术制备了具有抗紫外老化功能的PP/E...为降低紫外线对聚丙烯(Polyethylene,PP)非织造土工布的影响,选择ES(Ethylene-Propylene Side By Side)纤维和含有抗老化母粒的PP纤维为原料,TiO_(2)浸轧处理为后整理工序,采用针刺加固和热黏合加固技术制备了具有抗紫外老化功能的PP/ES高强非织造土工布。研究了抗老化工艺对PP/ES土工布力学性能和抗紫外老化性能的影响。结果表明:添加抗老化母粒和TiO_(2)浸轧后整理的PP/ES土工布力学性能少许上升;该土工布紫外老化后的羰基吸收峰强度最弱,T 5%仅下降4.73℃,纵向和横向的断裂强度保留率仅下降26.55%和26.76%,表现出最佳的抗紫外老化性能。展开更多
文摘Poly(ethylene terephthalate) (PET)/carbon black (CB) masterbatch was prepared by melt blending using a separate feeding technique and its homogeneous dispersion morphology was confirmed by transmission electron microscope (TEM). The Avrami and Hoffman-Lauritzen secondary nucleation theories were employed to analyze the effect of high CB content on crystallization kinetics of PET, providing theoretical support for the development of masterbatch with high content of functional components. The Avrami exponents,average values of n,for PET and PET/CB masterbatch are both greater than 3, which indicates three-dimensional growth of crystals. In addition,no significant evidence for regime transition of PET is found applying Hoffman-Lauritzen secondary nucleation theory,though such observations have been reported previously in the literature. Furthermore,appropriate U* value for PET is determined to be 12 800 J/mol. For PET/CB masterbatch,a transition from regime I to regime II around 225℃ is observed with appropriate U* value (12 800 J/mol) . This phenomenon is consistent with a transition point in plot of G versus Tc . The fold surface free energy σe (100. 3 mJ/m 2) of PET is much greater than that of PET/CB masterbatch (48. 3 mJ/m 2) ,which indicates heterogeneous nucleation effect of CB particles.
基金Transformation and Guidance of Scientific and Technological Achievements in Shanxi Province,China(No.202104021301053)Fundamental Research Program of Shanxi Province,China(Nos. 20210302123114 and 202203021211146)+1 种基金Transformation of Scientific and Technological Achievements Programs of Higher Education Institutions in Shanxi Province,China(TSTAP)(No. 2020CG014)Open Project Program of Key Lab for Sport Shoes Upper Materials of Fujian Province,Fujian Huafeng New Material Co.,Ltd.,China(No.S SUM213)。
文摘In order to effectively control the drug-release rate of medical textiles,biodegradable polycaprolactone(PCL) and polyglycolic acid(PGA) were blended at various mass ratios to prepare composite masterbatches for medical textiles.The surface morphology and the chemical structure of the masterbatches were analyzed.The crystallization,mass losses,strengths and drug-release rates of the composite masterbatches at different PCL/PGA mass ratios were explored.The results show that the degradation rate of the PGA carrier is obvious higher than that of the PCL carrier,and PCL,PGA and the tea polyphenol(TP) drug just physically mix without chemical reaction.During the degradation,the strength of the composite masterbatches gradually decreases.In addition,the drug-release rates of composite masterbatches at different mass ratios are different,and the more the PGA in the composite masterbatches,the faster the drug release of the composite masterbatches.The drug-release rate of the composite masterbatches can be controlled by adjusting the contents of PCL and PGA.
文摘为降低紫外线对聚丙烯(Polyethylene,PP)非织造土工布的影响,选择ES(Ethylene-Propylene Side By Side)纤维和含有抗老化母粒的PP纤维为原料,TiO_(2)浸轧处理为后整理工序,采用针刺加固和热黏合加固技术制备了具有抗紫外老化功能的PP/ES高强非织造土工布。研究了抗老化工艺对PP/ES土工布力学性能和抗紫外老化性能的影响。结果表明:添加抗老化母粒和TiO_(2)浸轧后整理的PP/ES土工布力学性能少许上升;该土工布紫外老化后的羰基吸收峰强度最弱,T 5%仅下降4.73℃,纵向和横向的断裂强度保留率仅下降26.55%和26.76%,表现出最佳的抗紫外老化性能。