Alumina-magnesia dry materials are widely used in induction furnace linings, but they show different kinds of damage when melting different kinds of alloy steel. In this paper, the chemical composition, phase composit...Alumina-magnesia dry materials are widely used in induction furnace linings, but they show different kinds of damage when melting different kinds of alloy steel. In this paper, the chemical composition, phase composition, and microstructure of the post-use dry materials for the working liners melting different kinds of steel were evaluated. Furthermore, the corrosion mechanism of the steel on the furnace lining materials was comprehensively analyzed. The findings reveal a significant ability of the Mn element in the molten steel to diffuse and penetrate into the refractories. Mn oxidizes to form MnO at the steel-refractory interface, and then forms a liquid phase with Al_(2)O_(3). The Cr element is dissolved into corundum and spinel of the refractories, resulting in lattice defects and structural damage of the materials. TiO2reacts with Al_(2)O_(3) to form Al_(2)TiO_(5), which plays a crucial role in preventing crack formation and propagation. Part of Ti4+dissolves into magnesia-alumina(MA), densifying the materials. TiO2also slows down the reaction between the Cr element and refractory components, further improving the corrosion resistance of the materials.展开更多
For bone regenerative engineering,it is a promising method to form skeletal tissues differentiating from human bone morrow mesenchyme stem cells(hBMSCs).However,it is still a critical challenge to efficiently control ...For bone regenerative engineering,it is a promising method to form skeletal tissues differentiating from human bone morrow mesenchyme stem cells(hBMSCs).However,it is still a critical challenge to efficiently control ostogenesis and clearly reveal the influence factor.To this end,the fluorescent gold nanodots(Au NDs) with highly negative charges as osteogenic induction reagent are successfully synthesized,which display better than commercial osteogenic induction medium through the investigations of ALP activity(2.5 folds) and cytoskeleton staining(1.5 folds).Two kinds of oligopeptides with different bio-structures(cysteine,Cys and glutathione,GSH) are selected for providing surficial charges on Au NDs.It is revealed that Au-Cys with more negative charges(-51 mV) play better role than Au-GSH(-19 mV) in osteogenic differentiation,when both of them have same size(~2 nm),sphere shape and show similar cell uptake amount.To explore deeply,osteogenesis related signaling pathways are monitored,revealing that the enhancement of osteogenic differentiation was through autophagy signaling pathway triggered by Au-Cys.And the promotion of highly negative charges in osteogenic diffe rentiation was further proved via sliver nanodots(Ag NDs,Ag-Cys and Ag-GSH) and carbon nanodots(CDs,Cys-CDs and GSH-CDs).This work indicates part of insights during hBMSCs differentiation and provides a novel strategy in osteogenic differentiation process.展开更多
基金the National Natural Science Foundation of China(52272022)Key Program of Natural Science Foundation of Hubei Province(2021CFA071).
文摘Alumina-magnesia dry materials are widely used in induction furnace linings, but they show different kinds of damage when melting different kinds of alloy steel. In this paper, the chemical composition, phase composition, and microstructure of the post-use dry materials for the working liners melting different kinds of steel were evaluated. Furthermore, the corrosion mechanism of the steel on the furnace lining materials was comprehensively analyzed. The findings reveal a significant ability of the Mn element in the molten steel to diffuse and penetrate into the refractories. Mn oxidizes to form MnO at the steel-refractory interface, and then forms a liquid phase with Al_(2)O_(3). The Cr element is dissolved into corundum and spinel of the refractories, resulting in lattice defects and structural damage of the materials. TiO2reacts with Al_(2)O_(3) to form Al_(2)TiO_(5), which plays a crucial role in preventing crack formation and propagation. Part of Ti4+dissolves into magnesia-alumina(MA), densifying the materials. TiO2also slows down the reaction between the Cr element and refractory components, further improving the corrosion resistance of the materials.
基金supported by the National Nature Science Foundation of China(Nos.51861145311,22005338)Science Foundation of China University of Petroleum,Beijing(No.2462017YJRC027)Open Project of State Key Laboratory of Superhard Materials(Jilin University 201802)。
文摘For bone regenerative engineering,it is a promising method to form skeletal tissues differentiating from human bone morrow mesenchyme stem cells(hBMSCs).However,it is still a critical challenge to efficiently control ostogenesis and clearly reveal the influence factor.To this end,the fluorescent gold nanodots(Au NDs) with highly negative charges as osteogenic induction reagent are successfully synthesized,which display better than commercial osteogenic induction medium through the investigations of ALP activity(2.5 folds) and cytoskeleton staining(1.5 folds).Two kinds of oligopeptides with different bio-structures(cysteine,Cys and glutathione,GSH) are selected for providing surficial charges on Au NDs.It is revealed that Au-Cys with more negative charges(-51 mV) play better role than Au-GSH(-19 mV) in osteogenic differentiation,when both of them have same size(~2 nm),sphere shape and show similar cell uptake amount.To explore deeply,osteogenesis related signaling pathways are monitored,revealing that the enhancement of osteogenic differentiation was through autophagy signaling pathway triggered by Au-Cys.And the promotion of highly negative charges in osteogenic diffe rentiation was further proved via sliver nanodots(Ag NDs,Ag-Cys and Ag-GSH) and carbon nanodots(CDs,Cys-CDs and GSH-CDs).This work indicates part of insights during hBMSCs differentiation and provides a novel strategy in osteogenic differentiation process.