Quantitative Detection of Corrosion State of Concrete Internal Reinforcement Based on Metal Magnetic Memory

Corrosion can be very harmful to the service life and several properties of reinforced concrete structures.The metal magnetic memory(MMM)method,as a newly developed spontaneous magnetic flux leakage(SMFL)non-destructive testing(NDT)technique,is considered a potentially viable method for detecting corrosion damage in reinforced concrete members.To this end,in this paper,the indoor electrochemical method was employed to accelerate the corrosion of outsourced concrete specimens with different steel bar diameters,and the normal components Bz and its gradient of the SMFL fields on the specimen surfaces were investigated based on the metal magnetic memory(MMM)method.The experimental results showed that the SMFL experimental Bz curves are consistent with the analytical results of the theoretical model.Furthermore,the crest-to-trough behavior on the Bz signal curve and its zero-point gradient spacing can more accurately indicate the corroded area’s extent.Then,a magnetic characteristic parameter W based on a large amount of experimental data was established to characterize the degree of corrosion of the steel bars.The magnetic characteristic parameter W is linearly related to the maximum cross-sectional area loss rate
of the corroded reinforcement.This paper will lay the foundation for future research on corrosion detection of reinforced concrete structures based on the MMM method and provide a feasible way for non-destructive detection of corrosion independent of the influence of reinforcement diameter and magnetization history.

Metal magnetic memory field characterization at early fatigue damage based on modified Jiles-Atherton model

In order to propel the development of metal magnetic memory （MMM） technique in fatigue damage detection, the Jiles-Atherton model （J-A model） was modified to describe MMM mechanism in elastic stress stage. A series of rotating bending fatigue experiments were conducted to study the stress-magnetization relationship and verify the correctness of modified J-A model. In MMM detection, the magnetization of material irreversibly approaches to the local equilibrium state Mo instead of global equilibrium state M^n under cyclic stress, and the M0-a curves are loops around the Mar,-a curve. The modified J-A model is constructed by replacing M~ in J-A model with M0, and it can describe the magnetomechanical effect well at low external magnetic field. In the rotating bending fatigue experiments, the MMM field distribution in normal direction around cylinder specimen is similar to the stress distribution, and the calculation result of model coincides with experiment result after some necessary modifications. The MMM field variation with time at a certain point in fatigue process is divided into three stages with the variation of stable stress-stain hysteresis loop, and the calculation results of model can explain not only the three stages of MMM field changes, but also the different change laws when the applied magnetic field and initial magnetic field are different. The MMM field distribution in normal direction along specimen axis reflects stress concentration effect at artificial defect, and the magnetic signal fluctuates around the defect at late fatigue stage. The calculation results coincide with the initial MMM principle and can explain signal fluctuates around the defect. The modified J-A model can explain experiment results well, and it is fit for MMM field characterization.

Fatigue damage evaluation by metal magnetic memory testing

Tension-compression fatigue test was performed on 0.45% C steel specimens.Normal and tangential components of magnetic memory testing signals,Hp(y) and Hp(x) signals,with their characteristics,K of Hp(y) and Hp(x)M of Hp(x),throughout the fatigue process were presented and analyzed.Abnormal peaks of Hp(y) and peak of Hp(x) reversed after loading; Hp(y) curves rotated clockwise and Hp(x) curves elevated significantly with the increase of fatigue cycle number at the first a few fatigue cycles,both Hp(y) and Hp(x) curves were stable after that,the amplitude of abnormal peaks of Hp(y) and peak value of Hp(x) increased more quickly after fatigue crack initiation.Abnormal peaks of Hp(y) and peak of Hp(x) at the notch reversed again after failure.The characteristics were found to exhibit consistent tendency in the whole fatigue life and behave differently in different stages of fatigue.In initial and crack developing stages,the characteristics increased significantly due to dislocations increase and crack propagation,respectively.In stable stage,the characteristics remained constant as a result of dislocation blocking,K value ranged from 20 to 30 A/(m·mm)-1,and Hp(x)M ranged from 270 to 300 A/m under the test parameters in this work.After failure,both abnormal peaks of Hp(y) and peak of Hp(x) reversed,K value was 133 A/(m·mm)-1 and Hp(x)M was-640 A/m.The results indicate that the characteristics of Hp(y) and Hp(x) signals were related to the accumulation of fatigue,so it is feasible and applicable to monitor fatigue damage of ferromagnetic components using metal magnetic memory testing(MMMT).

Characterization of Stress Concentration by Tangential Component Hp(x) of Metal Magnetic Memory Signals

The correlation between the stress concentration and the spontaneous magnetic signals of metal magnetic memory(MMM) was investigated via tensile tests. Sheet specimens of the Q235 steel were machined into standard bars with rectangular holes to obtain various stress concentration factors. The tangential component Hp(x) of MMM signals and its related magnetic characteristic parameters throughout the loading process were presented and analyzed. It is found that the tangential component Hp(x) is sensitive to the abnormal magnetic changes caused by the local stress concentration in the defect area. The minimum magnetic field is positively correlated to the magnitude of the load and the distance from the notch. The tangential magnetic stress concentration factor presents good numerical stability during the entire loading process, and can be used to evaluate the stress concentration factor. The results obtained will be a complement to the MMM technique.

Metal magnetic memory signals from surface of low-carbon steel and low-carbon alloyed steel

In order to investigate the regularity of metal magnetic signals of ferromagnetic materials under the effect of applied load, the static tensile test of Q235 steel and 18CrNiWA steel plate specimens were conducted and metal magnetic memory signals of specimens were measured during the test process. The influencing factors of metal magnetic memory signals and the relationship between axial applied load and signals were analyzed. The fracture and microstructure of the specimens were observed. The results show that the magnetic signals corresponding to the measured points change linearly approximately with increasing axial load. The microstructure of Q235 steel is ferrite and perlite, whereas that of 18CrNiWA steel is bainite and low-carbon martensite. The fracture of these two kinds of specimens is ductile rupture; carbon content of specimen materials and dislocation glide give much contribution to the characteristics of magnetic curves.

Micro-mechanism of metal magnetic memory signal variation during fatigue

Tensile fatigue tests were designed to study the relation between the tangential magnetic memory signal and dislocations. According to experimental results, in the early stage of fatigue, the magnetic signal and the dislocation density rapidly increase; while in the middle stage, the magnetic signal gradually increases, the dislocation density remains steady, and only the dislocation structure develops. On the other hand, in the later stage, the magnetic signal once again increases rapidly, the dislocation structure continues to develop, and microscopic cracks are formed. Analysis reveals that the dislocations block the movement of the domain wall, and the area of dislocation accumulation thus becomes an internal magnetic source and scatters a field outward. In addition, the magnetic memory field strengthens with increasing dislocation density and complexity of the dislocation structure. Accordingly, the dislocation pinning factor related with the dislocation density and the dislocation structure has been proposed to characterize the effect of dislocations on the magnetic memory signal. The magnetic signal strengthens with an increase in the dislocation pinning factor.

Quantitative Metal Magnetic Memory Reliability Modeling for Welded Joints

Metal magnetic memory（MMM） testing has been widely used to detect welded joints. However, load levels, environmental magnetic field, and measurement noises make the MMM data dispersive and bring difficulty to quantitative evaluation. In order to promote the development of quantitative MMM reliability assessment, a new MMM model is presented for welded joints. Steel Q235 welded specimens are tested along the longitudinal and horizontal lines by TSC-2M-8 instrument in the tensile fatigue experiments. The X-ray testing is carried out synchronously to verify the MMM results. It is found that MMM testing can detect the hidden crack earlier than X-ray testing. Moreover, the MMM gradient vector sum K_（vs） is sensitive to the damage degree, especially at early and hidden damage stages. Considering the dispersion of MMM data, the K_（vs） statistical law is investigated, which shows that K_（vs） obeys Gaussian distribution. So K_（vs） is the suitable MMM parameter to establish reliability model of welded joints. At last, the original quantitative MMM reliability model is first presented based on the improved stress strength interference theory. It is shown that the reliability degree R gradually decreases with the decreasing of the residual life ratio T, and the maximal error between prediction reliability degree R_1 and verification reliability degree R_2 is 9.15%. This presented method provides a novel tool of reliability testing and evaluating in practical engineering for welded joints.

Variation regularity of metal magnetic memory signals with inspecting time-interval and location

Influences of inspecting time-interval and location on varying behavior of metal magnetic memory (MMM) signals of defects were studied. Different areas in two precracked weldments were inspected at different time-intervals by type TSC-1M-4 stress-concentration magnetic inspector to obtain MMM signals. Mechanisms of MMM signals varying behavior with inspecting time and space were analyzed and discussed respectively. It is found that MMM signals don't change with inspecting time-interval, since stress field and magnetic leakage field maintain unchanged at any time after welding. On the other hand, MMM signals differ greatly for different inspecting locations, because stress field and magnetic leakage field are unevenly distributed in defective ferromagnetic materials.

Classified recognition for metal magnetic memory signals of welding defects in API 5L X65 pipeline steel

Feature extraction and selection from signals is a key issue for metal magnetic memory testing technique. In order to realize the classification of metal magnetic memory signals of welding defects, four fractal analysis methods, such as box- counting, detrended fluctuation, minimal cover and rescaled-range analysis, were used to extract the feature signal after the original metal magnet memory signal was de-noising and differential processing, then the Karhunen-Lo^e transformation was adopted as classification tool to identify the defect signals. The result shows that this study can provide an efficient classification method for metal magnetic memory signal of welding defects.

Study on magnetic memory signals of medium carbon steel specimens with surface crack precut during loading process

Static tensile test and tensile-tensile fatigue test of medium carbon steel sheet specimens with surface crack precut were performed on MTS810 hydraulic testing machine to clear the meaning of the point of Hp(y) value zero. Magnetic memory signals were measured during the test process. The results show that only one point of Hp(y) zero value exists in all measured magnetic signal curves during the loading process, which should be a sign of intersection of positive-negative magnetic poles after magnetic ordered state appears and does not indicate the position of surface crack precut. The analysis shows that the surface crack precut can not interrupt the magnetic ordered state occurred during the test completely, hence its Hp(y) value is not zero. However, the crack extending to a penetrated defect at the instant of specimen′s fracture leads to the discontinuance of magnetic ordered state.

Characterization of the Elastic-plastic Region Based on Magnetic Memory Effect

Detecting stress concentration, especially critical stress state leading to structure damage or failure, is one of the most important tasks of equipment diagnosis. Metal magnetic memory technique needs further research to evaluate stress concentration quantitatively due to ambiguous physical mechanism, though it has potential to detect early defects in ferromagnetic materials. Mild Q235 steel defective specimens in demagnetization state were loaded in tension up to visible necking, with magnetic memory signals measurement made at increasing stress levels. Magnetic signals varied greatly under first several loadings and subsequently tended to stability in the elastic region, which showed that the magnetization always approaches the anhysteretic magnetization curve and was explained by the theory of magnetomechanical effect. In the plastic stage, an abnormal wave occurred in the stress concentration zone and its height value was sensitive to plastic deformation levels and dependent on the distance between the probe and defect, in accordance with the simulation results based on the magnetic dipole model. Different magnetic signal characteristics in the elastic-plastic region indicate that the magnetic memory technique can identify macroyielding and early damage, which is of profound significance for ensuring safe operation of equipment in service.

Application of empirical mode decomposition in early diagnosis of magnetic memory signal

In order to eliminate noise interference of metal magnetic memory signal in early diagnosis of stress concentration zones and metal defects, the empirical mode decomposition method combined with the magnetic field gradient characteristic was proposed. A compressive force periodically acting upon a casing pipe led to appreciable deformation, and magnetic signals were measured by a magnetic indicator TSC-1M-4. The raw magnetic memory signal was first decomposed into different intrinsic mode functions and a residue, and the magnetic field gradient distribution of the subsequent reconstructed signal was obtained. The experimental results show that the gradient around 350 mm represents the maximum value ignoring the marginal effect, and there is a good correlation between the real maximum field gradient and the stress concentration zone. The wavelet transform associated with envelop analysis also exhibits this gradient characteristic, indicating that the proposed method is effective for early identifying critical zones.

Analysis of stress-magnetic coupling effect in weak magnetic environment

Metal magnetic memory （MMM） signals are difficult to be analyzed due to noise interfer- ence, which limits its practical engineering application. A method of improving the magnetic signals is proposed in this paper by placing the excitation device which generates a weak external magnetic field about 100 A/re. The effect of the external magnetic field on the magnetic signals is studied using both finite element method （FEM） and uniaxial tensile tests. Comparison of the test data with the simulation ones of stress-magnetic coupling shows that the magnetic signals are strengthened and the measurement sensitivity of the detection system is greatly improved through the external magnetic excitation. Moreover, the FEM result has a good agreement with the testing results of No. 20 steel plate. The proposed method has laid a foundation for further practical engineering application.

Influence of stress on the stray field signals of ferromagnetic materials

To investigate the influence of stress alone on the stray field signals of ferromagnetic materials,the static tensile tests of 0.45%C steel and 45CrNiMoVA steel flat-shaped specimens were performed on an MTS810 hydraulic testing machine. Hp（y） signals,the normal component of spontaneous stray field,were measured during the testing process by an EMS-2003 metal magnetic memory diagnostic apparatus cooperated with a non-magnetic electric control displacement instrument. Fracture and microstructure were observed by a scanning electronic microscope and a transmission electron microscope,respectively. The relationships between axial applied stress or residual stress measured by X-ray diffraction method and Hp（y） were analyzed. The results indicate that some regular pattern of the magnetic curve is displayed only between applied stress and stray field signals. The magnetic ordering process stops due to dislocation pinning magnetic domain structure,and Hp（y） value unvaried nearly with applied load increasing in the plastic deformation stage.

MMM testing and failure analysis of fastening bolts on reciprocating compressor cylinder cover

To avoid the serious accidents caused by the failure fastening bolts on reciprocating compressor cylinder cover,a new nondestructive testing(NDT) technology,metal magnetic memory(MMM) testing,was applied to safety evaluating and failure analyzing for the fastening bolts.Based on the dynamic stress calculation of the failure bolts,MMM testing was carried out at workshop.Given are the MMM stress distribution characteristics of the failure bolts and fracture faces.It has been found that the MMM signal variation amplitude of the crack transition zone in the fracture surface is minimal,that of the crack initiation zone is in the middle,and that of the tear fracture zone is maximal.The failure reasons were analyzed with MMM effect.The results of the metallographic examination showed that the validity and feasibility of MMM testing and failure analysis.This means MMM technology is a new,fast and validity method of failure analysis.

EFFECT OF TENSILE STRESS AND RESIDUAL STRESS ON THE SPONTANEOUS STRAY FIELD SIGNALS FROM THE SURFACE OF 0.45%C STEEL

In order to explore the quantitative method of metal magnetic memory testing（MMMT） and clarify the relationship between Hp（y）, the normal component of spontaneous stray field, and applied stress or residual stress, the static tensile tests of 0.45%C steel sheet specimens are carried out on a servo hydraulic MTS810 machine. Hp（y） values are measured during the test process by an EMS-2003 metal magnetic memory diagnostic apparatus and a non-magnetic electric control displacement instrument. Residual stresses of some points on the surface of a specimen are measured by a Stress Tech X-Stress 3000 X-ray diffraction instrument. The results show that the same variation rules of Hp（y） value versus applied tensile stress are presented under the different conditions of load-on and load-off. However, the same rule does not exist between the Hp（y） value and residual stress. The variation of Hp（y） value reflects the history of applied tensile stress.

Development of remaining life prediction of crankshaft remanufacturing core

This paper reviewed the main research work in the field of remaining life prediction of crankshaft remanufacturing core by Science and Technology on Remanu- facturing Laboratory. Based on the results of finite element analysis, the R angle zone of crankshaft was determined as a major measuring position. A special measuring probe is developed, and bending fatigue bench tests were carried out to collect electromagnetic damage information during fatigue process. A neural network model was established to identify damage degree of crankshaft core, and a damage evaluation equipment for crankshaft core was developed.