Mg PSZ ceramics doped with Y 2O 3 and CeO 2 was prepared using traditional processing method. The fine grain PSZ ceramics( d c10 μm) sintered at low temperature(1550 ℃) was obtained by means of composition ...Mg PSZ ceramics doped with Y 2O 3 and CeO 2 was prepared using traditional processing method. The fine grain PSZ ceramics( d c10 μm) sintered at low temperature(1550 ℃) was obtained by means of composition design. The effects of co stabilization of Y 2O 3, CeO 2 and annealing at 1100 ℃ on material composition, microstructure and mechanical properties were studied. The results show that Y 2O 3 and CeO 2 during annealing at 1100 ℃ can inhibit subeutectoid decomposition reaction effectively, and optimize nucleation and growth of t ZrO 2 precipitates in c ZrO 2 matrix phase. The materials show transgranular and intergranular fracture characteristics, and exhibit better mechanical properties owing to the cooperative effect of stress induced transformation toughening and microcrack toughening.展开更多
文摘Mg PSZ ceramics doped with Y 2O 3 and CeO 2 was prepared using traditional processing method. The fine grain PSZ ceramics( d c10 μm) sintered at low temperature(1550 ℃) was obtained by means of composition design. The effects of co stabilization of Y 2O 3, CeO 2 and annealing at 1100 ℃ on material composition, microstructure and mechanical properties were studied. The results show that Y 2O 3 and CeO 2 during annealing at 1100 ℃ can inhibit subeutectoid decomposition reaction effectively, and optimize nucleation and growth of t ZrO 2 precipitates in c ZrO 2 matrix phase. The materials show transgranular and intergranular fracture characteristics, and exhibit better mechanical properties owing to the cooperative effect of stress induced transformation toughening and microcrack toughening.