Layered double hydroxide(LDH)coatings on magnesium(Mg)alloys shine brightly in the field of corrosion protection because of their special ion-exchange function.State-of-the-art steam coating as a type of LDH film prep...Layered double hydroxide(LDH)coatings on magnesium(Mg)alloys shine brightly in the field of corrosion protection because of their special ion-exchange function.State-of-the-art steam coating as a type of LDH film preparation technique has emerged in recent years because only pure water is required as the steam source and its environmentally friendly LDH coating fits the current need for green development.Moreover,this coating can effectively inhibit the corrosion of the Mg alloy substrate due to the chemical bonding between the coating and the Mg alloy substrate.This review systematically explains cutting-edge advancements in the growth mechanism and corrosion behavior of LDH steam coatings,and analyzes the advantages and limitations of the steam-coating method.The influencing factors including pressure,CO_(2)/CO_(3)^(2-),aluminum content of the substrate alloy,solution type,and acid-pickling pretreatment,as well as the post-treatment of steam-coating defects,are comprehensively elucidated,providing new insights into the development of the in situ steam-coating technique.Finally,existing issues and future prospects are discussed to further accelerate the widespread application of Mg alloys.展开更多
Three-dimensional(3D) flower-like Co–Al layered double hydroxide(Co–Al-LDH) architectures composed of atomically thin nanosheets were successfully synthesized via a hydrothermal method in a mixed solvent of water an...Three-dimensional(3D) flower-like Co–Al layered double hydroxide(Co–Al-LDH) architectures composed of atomically thin nanosheets were successfully synthesized via a hydrothermal method in a mixed solvent of water and butyl alcohol. Owing to the unique hierarchical structure and modification by butyl alcohol, the electrochemical stability and the charge/mass transport of the Co–Al-LDHs was improved. When used in supercapacitors, the obtained Co–Al-LDHs deliver a high specific capacitance of 838 Fg^(-1) at a current density of 1 Ag^(-1)and excellent rate performance(753 Fg^(-1) at 30 Ag^(-1) and 677 Fg^(-1) at 100 Ag^(-1)), as well as excellent cycling stability with 95% retention of the initial capacitance even after 20,000 cycles at a current density of 5 Ag^(-1). This work provides a promising alternative strategy to enhance the electrochemical properties of supercapacitors.展开更多
The preparation of self-assembling organomodified Co/Al-layered double hydroxide(LDH)via one-step route was studied. A common surfactant,sodium dodecylbenzenesulfonate(DBS),was employed as an organic modifier.The beha...The preparation of self-assembling organomodified Co/Al-layered double hydroxide(LDH)via one-step route was studied. A common surfactant,sodium dodecylbenzenesulfonate(DBS),was employed as an organic modifier.The behavior and structure of self-assembled intercalated organic Co/Al-LDH were investigated by FTIR,SEM,WAXS,element analysis and TGA.Based upon the WAXS results and calculation by Bragg equation,the interlayer distance(d value)for organic Co/Al-LDH is enlarged from 0.75 nm to 3.10 nm,showing that the self-assembling behavior has been carried out successfully.Considering the observation from SEM, the product shows the morphology of organic Co/Al-LDH of a layered structure.In addition,FTIR,element analysis and TGA analysis show that the modifier is intercalated into the gallery of the Co/Al-LDH.Since organic modification for nanofiller is deemed to be necessary before applying it into polymer,the successful preparation of organomodified Co/Al-LDH will be significantly beneficial to the preparation and investigation of novel polymer/LDH nanocomposite.展开更多
Adsorption of 2, 4, 6-trichlorophenol(TCP) onto the calcined Mg/Al-CO_3 layered double hydroxide(CLDH) was investigated. The prepared Mg/Al-CO_3 layered double hydroxide(LDH) and CLDH were characterized by powde...Adsorption of 2, 4, 6-trichlorophenol(TCP) onto the calcined Mg/Al-CO_3 layered double hydroxide(CLDH) was investigated. The prepared Mg/Al-CO_3 layered double hydroxide(LDH) and CLDH were characterized by powder X-ray diffraction(XRD) and thermo gravimetric analyzer-differential scanning calorimeters(TG-DSC). Moreover, 2,4,6-trichlorophenol(TCP) was removed effectively(94.7% of removal percentage in 9h) under the optimized experimental conditions. The adsorption kinetics data fitted the pseudosecond-order model well. The Freundlich, Langmuir, and Tempkin adsorption models were applied to the experimental equilibrium adsorption data at different temperatures of solution. The adsorption data fitted the Freundlieh adsorption isotherm with good values of the correlation coefficient. A mechanism of the adsorption process is proposed according to the intraparticle diffusion model, which indicates that the overall rate of adsorption can be described as three steps.展开更多
1 Introduction In the present paper,MgCl2·6H2O,FeCl3·6H2O,and CeCl3·6H2O were used as raw materials in the precipitationhydrothermal method to synthesize MgF eC e hydrotalcite.The effects of the Fe:Ce m...1 Introduction In the present paper,MgCl2·6H2O,FeCl3·6H2O,and CeCl3·6H2O were used as raw materials in the precipitationhydrothermal method to synthesize MgF eC e hydrotalcite.The effects of the Fe:Ce molar ratio on the composition,crystal structure,and thermal stability of hydrotalcite are examined.Energy-dispersive X-ray spectroscopy(EDS),X-展开更多
The self-assembly of hybrid inorganic-organic materials on stationary platforms plays a critical role in improving their structural stability and wide usability.In this work,a novel two-step hydrothermal approach is p...The self-assembly of hybrid inorganic-organic materials on stationary platforms plays a critical role in improving their structural stability and wide usability.In this work,a novel two-step hydrothermal approach is proposed for synthesizing stable and advanced hybrid coatings on metal-oxide platforms through the surface modification of layered double hydroxide(LDH)films using novel metal-organic frameworks(MOFs).Initially,Mg-Al LDH nanocontainers,grown on a magnesium oxide layer produced through plasma electrolytic oxidation(PEO)of AZ31 Mg alloy substrate,were intercalated with cobalt via an oxidation route,providing the metallic coordination center for the MOF formation.In the subsequent step,a pioneering technique is introduced,utilizing tryptophan as the organic linker for the first time at a pH of 10.The self-assembly of cobalt-tryptophan complex,driven by the strong bonding between electrophilic sites of monomers and nucleophilic sites,facilitated the formation of a MOF network having a cloud-like structure on the surface of MgAl LDH's film.The resulting MOF-LDH encapsulation containers demonstrate exceptional electrochemical stability when exposed to a 3.5 wt.%NaCl solution,surpassing the performance of PEO and pure LDH coatings.This enhanced stability is attributed to the development of a dense top layer and a stable composition within the self-assembled MOF,effectively sealing flaws and preventing the infiltration of corrosive ions into the underlying metallic substrate.The formation mechanism of MOFs on LDH galleries is investigated using density functional theory calculations.展开更多
A clean method for preparing layered double hydroxides (LDHs) has been developed, featured by using the hydroxides of two different metals as starting materials by atom-economic reactions. The reactions were carried...A clean method for preparing layered double hydroxides (LDHs) has been developed, featured by using the hydroxides of two different metals as starting materials by atom-economic reactions. The reactions were carried out under hydrothermal conditions in either a high pressure autoclave or a microwave digester. The compositions, structural parameters and thermal behavior of the resulting LDHs are very similar to those of materials produced by using the separate nucleation and aging steps (SNAS) method. The major advantage of the new method is that no by-product is produced, so that filtration and washing processes are unnecessary. The consequent reduction in water consumption is beneficial to the environment.展开更多
基金This work was supported by the National Natural Science Foundation of China through the projects 51601108 and 52071191。
文摘Layered double hydroxide(LDH)coatings on magnesium(Mg)alloys shine brightly in the field of corrosion protection because of their special ion-exchange function.State-of-the-art steam coating as a type of LDH film preparation technique has emerged in recent years because only pure water is required as the steam source and its environmentally friendly LDH coating fits the current need for green development.Moreover,this coating can effectively inhibit the corrosion of the Mg alloy substrate due to the chemical bonding between the coating and the Mg alloy substrate.This review systematically explains cutting-edge advancements in the growth mechanism and corrosion behavior of LDH steam coatings,and analyzes the advantages and limitations of the steam-coating method.The influencing factors including pressure,CO_(2)/CO_(3)^(2-),aluminum content of the substrate alloy,solution type,and acid-pickling pretreatment,as well as the post-treatment of steam-coating defects,are comprehensively elucidated,providing new insights into the development of the in situ steam-coating technique.Finally,existing issues and future prospects are discussed to further accelerate the widespread application of Mg alloys.
基金supported by the National Basic Research Program of China(2014CB239702)Research project of environmental protection in Jiangsu province(2016060)Science and Technology Commission of Shanghai Municipality(14DZ2250800)
文摘Three-dimensional(3D) flower-like Co–Al layered double hydroxide(Co–Al-LDH) architectures composed of atomically thin nanosheets were successfully synthesized via a hydrothermal method in a mixed solvent of water and butyl alcohol. Owing to the unique hierarchical structure and modification by butyl alcohol, the electrochemical stability and the charge/mass transport of the Co–Al-LDHs was improved. When used in supercapacitors, the obtained Co–Al-LDHs deliver a high specific capacitance of 838 Fg^(-1) at a current density of 1 Ag^(-1)and excellent rate performance(753 Fg^(-1) at 30 Ag^(-1) and 677 Fg^(-1) at 100 Ag^(-1)), as well as excellent cycling stability with 95% retention of the initial capacitance even after 20,000 cycles at a current density of 5 Ag^(-1). This work provides a promising alternative strategy to enhance the electrochemical properties of supercapacitors.
基金Project(50703026)supported by the National Natural Science Foundation of Chinaproject(F/4285-1)supported by International Foundation for Science(IFS)+1 种基金project(20080440182,200902615)supported by China Postdoctoral Science Foundationproject supported by Guest-Scientist Research Fellowship granted by Leibniz Institute of Polymer Research Dresden,Germany
文摘The preparation of self-assembling organomodified Co/Al-layered double hydroxide(LDH)via one-step route was studied. A common surfactant,sodium dodecylbenzenesulfonate(DBS),was employed as an organic modifier.The behavior and structure of self-assembled intercalated organic Co/Al-LDH were investigated by FTIR,SEM,WAXS,element analysis and TGA.Based upon the WAXS results and calculation by Bragg equation,the interlayer distance(d value)for organic Co/Al-LDH is enlarged from 0.75 nm to 3.10 nm,showing that the self-assembling behavior has been carried out successfully.Considering the observation from SEM, the product shows the morphology of organic Co/Al-LDH of a layered structure.In addition,FTIR,element analysis and TGA analysis show that the modifier is intercalated into the gallery of the Co/Al-LDH.Since organic modification for nanofiller is deemed to be necessary before applying it into polymer,the successful preparation of organomodified Co/Al-LDH will be significantly beneficial to the preparation and investigation of novel polymer/LDH nanocomposite.
基金Funded by the National Natural Science Foundation of China(No.21476269)
文摘Adsorption of 2, 4, 6-trichlorophenol(TCP) onto the calcined Mg/Al-CO_3 layered double hydroxide(CLDH) was investigated. The prepared Mg/Al-CO_3 layered double hydroxide(LDH) and CLDH were characterized by powder X-ray diffraction(XRD) and thermo gravimetric analyzer-differential scanning calorimeters(TG-DSC). Moreover, 2,4,6-trichlorophenol(TCP) was removed effectively(94.7% of removal percentage in 9h) under the optimized experimental conditions. The adsorption kinetics data fitted the pseudosecond-order model well. The Freundlich, Langmuir, and Tempkin adsorption models were applied to the experimental equilibrium adsorption data at different temperatures of solution. The adsorption data fitted the Freundlieh adsorption isotherm with good values of the correlation coefficient. A mechanism of the adsorption process is proposed according to the intraparticle diffusion model, which indicates that the overall rate of adsorption can be described as three steps.
基金supported by China Postdoctoral Science Foundation(No.118918)West Light Foundation of the Chinese Academy of Science
文摘1 Introduction In the present paper,MgCl2·6H2O,FeCl3·6H2O,and CeCl3·6H2O were used as raw materials in the precipitationhydrothermal method to synthesize MgF eC e hydrotalcite.The effects of the Fe:Ce molar ratio on the composition,crystal structure,and thermal stability of hydrotalcite are examined.Energy-dispersive X-ray spectroscopy(EDS),X-
基金supported by the National Research Foundation of Korea(NRF)funded by the Korean government(MSIT)(no.2022R1A2C1006743)。
文摘The self-assembly of hybrid inorganic-organic materials on stationary platforms plays a critical role in improving their structural stability and wide usability.In this work,a novel two-step hydrothermal approach is proposed for synthesizing stable and advanced hybrid coatings on metal-oxide platforms through the surface modification of layered double hydroxide(LDH)films using novel metal-organic frameworks(MOFs).Initially,Mg-Al LDH nanocontainers,grown on a magnesium oxide layer produced through plasma electrolytic oxidation(PEO)of AZ31 Mg alloy substrate,were intercalated with cobalt via an oxidation route,providing the metallic coordination center for the MOF formation.In the subsequent step,a pioneering technique is introduced,utilizing tryptophan as the organic linker for the first time at a pH of 10.The self-assembly of cobalt-tryptophan complex,driven by the strong bonding between electrophilic sites of monomers and nucleophilic sites,facilitated the formation of a MOF network having a cloud-like structure on the surface of MgAl LDH's film.The resulting MOF-LDH encapsulation containers demonstrate exceptional electrochemical stability when exposed to a 3.5 wt.%NaCl solution,surpassing the performance of PEO and pure LDH coatings.This enhanced stability is attributed to the development of a dense top layer and a stable composition within the self-assembled MOF,effectively sealing flaws and preventing the infiltration of corrosive ions into the underlying metallic substrate.The formation mechanism of MOFs on LDH galleries is investigated using density functional theory calculations.
文摘A clean method for preparing layered double hydroxides (LDHs) has been developed, featured by using the hydroxides of two different metals as starting materials by atom-economic reactions. The reactions were carried out under hydrothermal conditions in either a high pressure autoclave or a microwave digester. The compositions, structural parameters and thermal behavior of the resulting LDHs are very similar to those of materials produced by using the separate nucleation and aging steps (SNAS) method. The major advantage of the new method is that no by-product is produced, so that filtration and washing processes are unnecessary. The consequent reduction in water consumption is beneficial to the environment.
基金supported by the Natural Science Foundation of Shanxi Province(201601D102006)the Key Science and Technology Program of Shanxi Province,China(MD2014-09,MD2014-10)~~