The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristi...The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.展开更多
A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations we...A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations were characterized with an optical microscope(OM), X-ray diffractometer(XRD), scanning electron microscope(SEM) equipped with energy dispersive spectroscope(EDS), transmission electron microscope(TEM) and mechanical tests at room temperature, respectively. The experimental results show that the as-cast alloy mainly consists of α-Mg, eutectic Mg_2Zn_3, MgZnSm and Mg_(41)Sm_5. These eutectic phases with continuous or semicontinuous morphology principally distribute along grain boundaries. Almost all the eutectic compounds dissolve in α-Mg and the grains have no obvious growth trend after optimum solution treatment at 490 °C for 18 h. Meanwhile, the ultimate tensile strength(UTS) of 229 MPa and elongation(EL) to rupture of 9.78% can be achieved through the optimal solution treatment, which increase by 37 MPa and 57.74%, respectively, compared with that of the as-cast alloy. Further aging treatments at 200 °C for different durations lead to the conspicuous increment of mechanical properties and prominent age-hardening response. Peak-aged alloy(treated at 200 °C for 12 h) reveals better mechanical properties(UTS 258 MPa, EL 9.42%, hardness 73.4 HV) compared with the same alloy treated in other aging conditions, which is mainly ascribed to precipitated Mg_2Zn_3 and MgZn_2 phases. Fracture analysis demonstrates that the as-cast alloy belongs to inter-granular and cleavage fracture patterns, while the solutionized alloy(treated at 490 °C for 18 h) reveals trans-granular and quasi-cleavage fracture modes. For the peak-aged alloy, the fracture pattern obeys the mixture of trans-granular and cleavage modes.展开更多
Mg-8Li-3Al-xCe(x=0, 1.0, 3.0) alloys were prepared. And the effects of cerium content on the microstructure and mechanical properties were studied. Results show that the as-cast alloy is composed of α(Mg), β(Li) and...Mg-8Li-3Al-xCe(x=0, 1.0, 3.0) alloys were prepared. And the effects of cerium content on the microstructure and mechanical properties were studied. Results show that the as-cast alloy is composed of α(Mg), β(Li) and Al2Ce. Cerium has obvious refining effect on α(Mg). And the strength and elongation of alloys were improved.展开更多
The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression...The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression deformation behavior at room-temperature was studied. The results showed that the microstructure of Mg-8Zn-1Y alloy solidified under ambient pressure and super-high pressure was both mainly composed of ■-Mg and quasicrystal I-Mg3Zn6 Y. Solidification under super-high pressure contributed to refining solidified microstructure and changing morphology of the intergranular second phase. The morphology of intergranular second phase（quasicrystal I-Mg3Zn6Y） was transformed from continuous network（ambient pressure） to long island（high pressure） and finally to granular（super-high pressure） with the increase in pressure. The compressive strength, yield strength and rupture strain of the samples solidified under ambient pressure were significantly improved from 262.6 MPa, 244.4 MPa and 13.3% to 437.3 MPa, 368.9 MPa and 24.7% under the pressure of 6 GPa, respectively. Under ambient pressure, cleavage plane on compressive fracture was large and smooth. When it was solidified under the pressure ranging from 4 to 6 GPa, cleavage plane on compressive fracture was small and coarse. In addition, dimple, tear ridge and lobate patterns existed.展开更多
文摘The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.
基金Project(51141007)supported by the National Natural Science Foundation of ChinaProject(E2013501096)supported by Hebei Province Natural Science Foundation,China
基金financially supported by the National Nature Science Foundations of China(51464032)National Basic Research Program of China(Grant No.2010CB635106)
文摘A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations were characterized with an optical microscope(OM), X-ray diffractometer(XRD), scanning electron microscope(SEM) equipped with energy dispersive spectroscope(EDS), transmission electron microscope(TEM) and mechanical tests at room temperature, respectively. The experimental results show that the as-cast alloy mainly consists of α-Mg, eutectic Mg_2Zn_3, MgZnSm and Mg_(41)Sm_5. These eutectic phases with continuous or semicontinuous morphology principally distribute along grain boundaries. Almost all the eutectic compounds dissolve in α-Mg and the grains have no obvious growth trend after optimum solution treatment at 490 °C for 18 h. Meanwhile, the ultimate tensile strength(UTS) of 229 MPa and elongation(EL) to rupture of 9.78% can be achieved through the optimal solution treatment, which increase by 37 MPa and 57.74%, respectively, compared with that of the as-cast alloy. Further aging treatments at 200 °C for different durations lead to the conspicuous increment of mechanical properties and prominent age-hardening response. Peak-aged alloy(treated at 200 °C for 12 h) reveals better mechanical properties(UTS 258 MPa, EL 9.42%, hardness 73.4 HV) compared with the same alloy treated in other aging conditions, which is mainly ascribed to precipitated Mg_2Zn_3 and MgZn_2 phases. Fracture analysis demonstrates that the as-cast alloy belongs to inter-granular and cleavage fracture patterns, while the solutionized alloy(treated at 490 °C for 18 h) reveals trans-granular and quasi-cleavage fracture modes. For the peak-aged alloy, the fracture pattern obeys the mixture of trans-granular and cleavage modes.
基金Project supported by Heilongjiang Province Key Technologies R&D Project (GC06A212)
文摘Mg-8Li-3Al-xCe(x=0, 1.0, 3.0) alloys were prepared. And the effects of cerium content on the microstructure and mechanical properties were studied. Results show that the as-cast alloy is composed of α(Mg), β(Li) and Al2Ce. Cerium has obvious refining effect on α(Mg). And the strength and elongation of alloys were improved.
基金Project supported by National Natural Science Foundation of China(51475486)Natural Science Foundation of Hebei Province(E2013501096)
文摘The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression deformation behavior at room-temperature was studied. The results showed that the microstructure of Mg-8Zn-1Y alloy solidified under ambient pressure and super-high pressure was both mainly composed of ■-Mg and quasicrystal I-Mg3Zn6 Y. Solidification under super-high pressure contributed to refining solidified microstructure and changing morphology of the intergranular second phase. The morphology of intergranular second phase（quasicrystal I-Mg3Zn6Y） was transformed from continuous network（ambient pressure） to long island（high pressure） and finally to granular（super-high pressure） with the increase in pressure. The compressive strength, yield strength and rupture strain of the samples solidified under ambient pressure were significantly improved from 262.6 MPa, 244.4 MPa and 13.3% to 437.3 MPa, 368.9 MPa and 24.7% under the pressure of 6 GPa, respectively. Under ambient pressure, cleavage plane on compressive fracture was large and smooth. When it was solidified under the pressure ranging from 4 to 6 GPa, cleavage plane on compressive fracture was small and coarse. In addition, dimple, tear ridge and lobate patterns existed.