Effects of additives on corrosion and wear resistance of micro-arc oxidation coatings on TiAl alloy

Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures and compositions were analyzed by SEM,EDX and XRD.The corrosion and wear properties of the coatings were investigated by potentiodynamic polarization and ball-on-disc wear test,respectively.The results show that the MAO coatings consist of WO3,Ti2O3,graphite and Al2O3 besides Al2TiO5 and Al2SiO5.With additives in the electrolyte,the working voltage at the micro-arc discharge stage decreases,and the ceramic coating gets smoother and more compact.The corrosion current density of MAO coating is much lower than that of TiAl substrate.It can be reduced from 9.81×10-8A/cm 2to 3.02×10-10A/cm 2 .The MAO coatings composed of hard Al2O3,WO3 and Ti2O3 obviously improve the wear resistance of TiAl alloy.The wear rate is-3.27×10-7g/(N·m).

Micro-arc oxidation coatings on Mg-Li alloys

Micro-arc oxidation (MAO) method was used for the surface modification of an Mg-5wt.%Li alloy. Ceramic coatings were in-situ fabricated on the Mg-Li alloy. The morphology feature,phase composition,and corrosion-resistance of the formed ceramic coatings were studied by SEM,XRD,and electrochemical methods,respectively. The results showed that the coatings produced in a sodium silicate solution system were composed of MgO and Mg2SiO4. The ceramic coating became thicker and the content of Mg2SiO4 phase increase...

Characterization of ceramic coating on ZK60 magnesium alloy prepared in a dual electrolyte system by micro-arc oxidation

Micro-arc oxidation （MAO） process was cartied out in an optimized dual electrolyte system to fabricate a compact, smooth, and corrosion resistant coating on ZK60 Mg alloy. The microstructural characteristics of coating were investigated by scanning electron microscopy （SEM） coupled with an energy dispersive spectrometer （EDS） and X-ray diffraction （XRD）. Test of mass loss was conducted at a 3.5 % NaCl solution to assess the resistance to corrosion. The bonding strength between the coating and ZK60 substrate was evaluated using scratch experiment. The results reveal that MgA1204 and MgO are the main phases of ceramic coating obtained in the dual electrolyte system. The corrosion rate of coating prepared in the optimized dual electrolyte is only 0.0061 g.m-2.h-1, which demonstrates excellent corrosion resistance. This is mainly due to the compact, uniform coating with high bonding strength.

Preparation of micro-arc oxidation coatings on magnesium alloy and its thermal shock resistance property

In the NaAlO2-Na2SiO3 compound system, the ceramic coatings were prepared on magnesium alloy by micro-arc oxidation. The morphology, phase composition, and thermal shock resistance of the ceramic coatings were studied by scanning electron microscope, X-ray diffraction and thermal shock tests, respectively. The results showed that the ceramic coating contains MgO, MgAl2O4, as well as a little amount of MgESiO4. The thickness of the ceramic coatings increases with the current density increasing, when the current density is 12 A·dm^-2, the thermal shock resistance of the produced ceramic coating is the best. The hardness of the ceramic coating is up to 10 GPa or so.

Preparation technology and anti-corrosion performances of black ceramic coatings formed by micro-arc oxidation on aluminum alloys

In order to prepare ornamental and anti-corrosive coating on aluminum alloys, preparation technology of black micro-arc ceramic coatings on Al alloys in silicate based electrolyte was studied. The influence of content of Na2WO4 and combination additive in solution on the performance of black ceramic coatings was studied; the anticorrosion performances of black ceramic coatings were evaluated through whole-immersion test and electrochemical method in 3.5% NaCl solution at different pH value; SEM and XRD were used to analyze the surface morphology and phase constitutes of the black ceramic coatings. Experimental results indicated that, without combination additives, with the increasing of Na2WO4 content in the electrolyte, ceramic coating became darker and thicker, but the color was not black; after adding combination additive, the coating turned to be black; the black ceramic coating was multi-hole form in surface. There was a small quantity of tungsten existing in the black ceramic coating beside α-Al2O3 phase and β-Al2O3 phase. And aluminum alloy with black ceramic coating exhibited excellent anti-corrosion property in acid, basic and neutral 3.5% NaCl solution.

Preparation and corrosion resistance of the micro-arc oxidation coating on Al_2O_3f/ZL109 composites

A ceramic layer was prepared on the surface of Al2O3f/ZL109 composites by means of micro-arc oxidation （MAO） technique. The surface morphology and phase constituent of the ceramic layer were analyzed using scanning electron microscope and X-ray diffraction. The polarization curves of the composites before and after MAO treatment were measured and analyzed. The results showed that after Al2O3f/ZL109 composites were treated using MAO technique in silicate solution, the ceramic layer formed, and it was composed of Al, Si, and mullite phase. Al and Si came from Al alloy matrix of the composites, and the mullite phase formed in process of MAO. Al2O3 fiber in the composites affects the electric conductivity of the composites, the MAO reaction is promoted, and the cera- mic layer forming on the composite material side is slightly thicker than that on the Al alloy side. After Al2O3f/ZL109 composites were treated using MAO technique, the corro- sion resistance of the composites is significantly improved.

Optimizing the micro-arc oxidation (MAO) parameters to attain coatings with minimum porosity and maximum hardness on the friction stir welded AA6061 aluminium alloy welds

Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relationships were derived to evaluate the MAO coating properties(porosity and hardness) by incorporating very important MAO parameters(current density, inter-electrode distance and oxidation time). MAO parameters were also optimized to achieve coatings with minimum porosity and maximum hardness. Further, the effect of MAO parameters on coating characteristics was analysed. From the results, it is found that the current density has greater influence on the responses than the other two parameters.

Fretting wear of micro-arc oxidation coating prepared on Ti6Al4V alloy

Micro-arc oxidation(MAO)coating was prepared on Ti6Al4V alloy surface and its characterizations were detected by Vickers hardness tester,profilometer,scanning electric microscope(SEM),energy dispersive X-ray spectrometer(EDX)and X-ray diffractometer(XRD).Fretting wear behaviors of the coating and its substrate were comparatively tested without lubrication under varied displacement amplitudes(D)in a range of 3-40μm,constant normal load(Fn)of 300 N and frequency of 5 Hz.The results showed that the MAO coating,presenting rough and porous surface and high hardness,mainly consisted of rutile and anatase TiO2 phases.Compared with the substrate,the MAO coating could shift the mixed fretting regime(MFR)and slip regime(SR)to a direction of smaller displacement amplitude.In the partial slip regime(PSR),lower friction coefficients and slight damage appeared due to the coordination of elastic deformation of contact zones.In the MFR,the friction coefficient of the coating was lower than that of the substrate as a result of the prevention of plastic deformation by the hard ceramic surface.With the increase of the displacement amplitude,the degradation of the MAO coating and the substrate increased extremely.The fretting wear mechanisms of the coating were abrasive wear and delamination with some material transfer of specimen.In addition,the coating presented a better property for alleviating fretting wear.

Growth process and corrosion resistance of micro-arc oxidation coating on Mg-Zn-Gd magnesium alloys

A Mg-6Zn-3Gd(mass fraction,%) alloy,noted as ZG63,was coated by different micro-arc oxidation(MAO) processes,and the coating structure and corrosion resistance of the alloy were studied using scanning electron microscopy(SEM),glancing angle X-ray diffractometry(GAXRD) and various electrochemical methods.The micro-arc oxidation process consists of three stages and corresponds with different coating structures.In the initial stage,the coating thickness is linearly increased and is controlled by electrochemical polarization.In the second stage,the coating grows mainly inward and accords with parabolic regularity.In the third stage,the loose coating forms and is controlled by local arc light.The looser coating is mainly composed of MgSiO3 and the compact coating is mainly composed of MgO.From micro-arc oxidation stage to local arc light stage,the corrosion resistance of the coated alloy firstly increases and then decreases.The satisfied corrosion resistance corresponds to the coating time ranging from 6 to10 min.

Characterization of bioactive ceramic coatings prepared on titanium implants by micro-arc oxidation

Micro-arc oxidation （MAO） is an enhanced chemical technology in an electrolyte medium to obtain coating structures on valve-metal surfaces. Titanium oxide films obtained by MAO in the sodium phosphate electrolyte were investigated. The films were composed mainly of TiO2 phases in the form of anatase and mille and enriched with Na and P elements at the surface. Their apafite-inducing ability was evaluated in a simulated body fluid （SBF）. When immersing in SBF for over 30 d, a preferential carbonated-hydroxyapatite was formed on the surfaces of the films, which suggests that the MAO-treated titanium has a promising positive biological response.

Evolution of Residual Stresses in Micro-arc Oxidation Ceramic Coatings on 6061 Al Alloy

Most researches on micro-arc oxidation mainly focus on the application rather than discovering the evolution of residual stresses. However, residual stresses in the surface coatings of structural components have adverse effects on their properties, such as fatigue life, dimensional stability and corrosion resistance, etc. The micro-arc oxidation ceramic coatings are produced on the surfaces of 6061 aluminum alloy by a homemade asymmetric AC type of micro-arc oxidation equipment of 20 kW. A constant current density of 4.4___0.1 A/dm2 and a self-regulated composite electrolyte are used. The micro-arc oxidation treatment period ranges from 10 min to 40 min, and the thickness of the ceramic coatings is more than 20 Bin. Residual stresses attributed to 7-A1203 constituent in the coatings at different micro-arc oxidation periods are analyzed by an X-ray diffractometer using the sin2~u method. The analysis results show that the residual stress in the ceramic coatings is compressive in nature, and it increases first and then decreases with micro-arc oxidation time increase. The maximum stress value is 1 667_＋20 MPa for period of 20 min. Through analyzing the coating thickness, surface morphology and phase composition, it is found that the residual stress in the ceramic coatings is linked closely with the coating growth, the phase composition and the micro cracks formed. It is also found that both the heat treatment and the ultrasonic action release remarkably the residual compressive stress. The heat treatment makes the residual compressive stress value decrease 1 378 MPa. The ultrasonic action even alters the nature of the residual stress, making the residual compressive stress change into a residual tensile stress.

Preparation and properties of a cerium-containing hydroxyapatite coating on commercially pure titanium by micro-arc oxidation

A porous cerium-containing hydroxyapatite coating on commercially pure titanium was prepared by micro-arc oxidation （MAO） in an electrolytic solution containing calcium acetate, p-glycerol phosphate disodium salt pentahydrate （β-GP）, and cerium nitrate. The thickness, phase, composition morphology, and biocompatibility of the oxide coating were characterized by X-ray diffraction （XRD）, electron probe microanalysis （EPMA）, scanning electron microscopy （SEM） with energy dispersive X-ray spectrometer （EDS）, and cell culture. The thickness of the MAO film is about 15-25 ~tm, and the coating is porous and uneven, without any apparent interface to the titanium substrates. The results of XRD and EDS show that the porous coating is made up of hydroxyapatite （HA） film containing Ce. The favorable osteoblast cell affinity makes the Ce-HA film have a good biocompatibility. The Ce-HA film is expected to have significant medical applications as dental implants and artificial bone joints.

Micro-arc Oxidation Inverter Power Supply Based on the Limited Bipolar Soft-switch Control Method

In order to overcome many limitations of the conventional power supplies, such as ponderosity, big wastage, and simplex output characteristic, a dual-inverter power supply is designed to meet the different requirements of micro-arc oxidation. The main circuit structure and principle of the dual-inverter power supply for micro-arc oxidation is described, the control system and the control adjustment method are also introduced. The dual-inverter technology is adopted in micro-arc oxidation power supply. The limited bipolar control mode is applied in the power inverter circuit for adjusting the voltage, and various voltage waveform can be obtained by controlling the chopper circuit. Meanwhile, the control accuracy and response speed are improved greatly because of the higher inverter frequency. The power supply can output direct current（DC） waveform, DC pulse waveform, symmetry alternating current（AC） waveform, asymmetry AC waveform, and so on. Besides, the parameters such as pulse width, range, frequency, duty cycle can be adjusted. The experimental result shows that the power supply has many advantages, such as stable output, wonderful waveform consistency and obvious advantage in technique, and it can meet the requirements of micro-arc oxidation process fully.

Influence of Electrolyte Composition on the Calcium-Phosphorus compound Coating on Titanium Substrate by Micro-arc Oxidation

The compound bioceramic coating containing calcium (Ca) and phosphorus (P) on titanium alloy substrate was prepared by means of micro-arc oxidation (MAO) treatment. The results show that under the different electrolyte the coating with the color of gray or black and surface morphology of cauliflower or honeycomb, where Ca content and P contain can attain 30% and 20% respectively, can be obtained. Meanwhile, the influences of electrolyte temperature, current density and discharge time on morphology and thickness of coating are also discussed here.

Synthesis of tetragonal BaTiO_3 film on Ti substrate by micro-arc oxidation

BaTiO3 films on Ti substrate were fabricated by alternative current(AC) and direct current(DC) micro arc oxidation (MAO).Microstructures of films were investigated by means of SEM,XRD and TEM.The results show that the amorphous phase and primitive cubic phase are the main phases in the films prepared by AC MAO.Even after being annealed at 1 200 ℃ for 8 h,only a few tetragonal phases can be observed in films prepared by AC MAO.However,tetragonal BaTiO3 phase can be produced by DC MAO directly.In the films prepared by DC MAO,a mixture of cubic phase and tetragonal phase is formed.After sparking spacious distribution,sparking duration and temperature gradient near sparking sites were taken into account,and a mechanism of synthesis of tetragonal BaTiO3 phase by DC MAO was proposed.

Effects of increase extent of voltage on wear and corrosion resistance of micro-arc oxidation coatings on AZ91D alloy

The effects of increase extent of voltage on the wear resistance and corrosion resistance of micro-arc oxidation(MAO) coatings on AZ91D magnesium alloy were investigated in silicate electrolyte.The results show that with increasing extent of voltage, both of the thickness and bonding force of MAO coatings first increase,and then decrease.These parameters are all up to their maximum values when the increase extent of voltage is 20 V.The roughness of the coatings always increases.The coating has the best corrosion resistance when the increase extent of voltage is not below 25 V,and the coating has the best wear resistance when the increase extent of voltage is 10 V.The wear mechanisms for the micro-arc oxidation are abrasive wear and micromachining wear. These are related to their microstructures.

Wear resistance of ceramic coating on AZ91 magnesium alloy by micro-arc oxidation

The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation (MAO) was characterized. The results show that the ceramic coating(3.4-23μm in thickness)on the surface of AZ91 alloy was attained under different micro-arc oxidation treatment conditions, which consist mainly of MgO, Mg2SiO4 and MgSiO3 phases. Nano-hardness in a cross-sectional specimen was determined by nano-indentation experiment. The MAO coatings exhibit higher hardness than the substrate. Dry sliding wear tests for the MAO coatings and AZ91 alloy were also carried out using an oscillating friction and wear tester in a ball-on-disc contact configuration. The wear resistance of the MAO coatings is improved respectively under different treatment time as a result of different structures of ceramic coatings formed on AZ91 alloy.

Preparation of narrow band gap V_2O_5/TiO_2 composite films by micro-arc oxidation

V2Os/TiO2 composite films were prepared on pure titanium substmtes via micro-arc oxidation （MAO） in electrolytes consisting of NaVO3. Their morphology and dements were characterized by scanning electron microscopy （SEM） and energy-dispersive X-ray （EDX） analysis. Phase composition and valence states of species in the films were characterized by X-ray diffraction （XRD） and X-ray photoelec- tron spectroscopy （XPS）. Ultraviolet-visible diffuse reflectance spectra （UV-Vis DRS） were also employed to evaluate the photophysical property of the films. The VEOs/TiO2 composite films show a sheet-like morphology. Not only V205 phase appears in the films when the NaVO3 concentration of the electrolyte is higher than 6,10 g/L and is loaded at the surface of anatase, but also V4＋ is incorporated into the crystal lattice of anatase. In comparison with pure TiO2 films the V2Os/TiO2 composite films exhibit significantly narrow band gap energy. The film prepared in an electrolyte consisting of NaVO3 with a concentration of 8.54 g/L exhibits the narrowest band gap energy, which is approximately 1.89 eV. The V2Os/TiO2 composite films also have the significantly enhanced visible light photocatalytic activity. The film prepared in an electrolyte consisting of NaVO3 with a concentration of 8.54 g/L exhibits the best photocatalytic activity and about 93% of rhodamine is degraded after 14 h visible light radiation.

Early Osseointegration of Implants with Cortex-like TiO2 Coatings Formed by Micro-arc Oxidation:A Histomorphometric Study in Rabbits

In our previous studies, a novel cortex-like Ti O2 coating was prepared on Ti surface through micro-arc oxidation（MAO） by using sodium tetraborate as electrolyte, and the effects of the coating on cell attachment were testified. This study aimed to investigate the effects of this cortex-like MAO coating on osseointegration. A sand-blasting and acid-etching（SLA） coating that has been widely used in clinical practice served as control. Topographical and chemical characterizations were conducted by scanning electron microscopy, energy dispersive X-ray spectrometer, X-ray diffraction, contact angle meter, and step profiler. Results showed that the cortex-like coating had microslots and nanopores and it was superhydrophilic, whereas the SLA surface was hydrophobic. The roughness of MAO was similar to that of SLA. The MAO and SLA implants were implanted into the femoral condyles of New Zealand rabbits to evaluate their in-vivo performance through micro-CT, histological analysis, and fluorescent labeling at the bone-implant interface four weeks after surgery. The micro-CT showed that the bone volume ratio and mean trabecular thickness were similar between MAO and SLA groups four weeks after implantation. Histological analysis and fluorescent labeling showed no significant differences in the bone-implant contact between the MAO and SLA surfaces. It was suggested that with micro/nanostructure and superhydrophilicity, the cortex-like MAO coating causes excellent osseointegration, holding a promise of an application to implant modification.

Adhesive strength and structure of micro-arc oxidation ceramic coatings grown in-situ on LY12 aluminum alloy

The ceramic coatings containing zirconium dioxide were grown in-situ on LY12 aluminium alloy by micro-arc oxidation in mixed zirconate and phosphate solution. The phase composition and morphology of the coatings were studied by XRD and SEM. The adhesive strength of ceramic coatings was assessed by thermal shock test and tensile test. The results show that the coating is composed of m-ZrO2,t-ZrO2, and a littleγ-Al2O3. Along the section of the coating, t-ZrO2 is more on both sides than that in the middle, while m-ZrO2 is more in the middle than that on both sides. Meantime the coating is also composed of a dense layer and a loose layer. The coating has excellent thermal shock resistance under 550℃and 600℃. And tensile tests show the adhesive strength of the dense layer of the coating with the substrate is more than 17.5 MPa.