First of all, the concept of γ_p_S a_S m_N (confidence level_reliability_stress amplitude_stress mean_fatigue life) surface is presented. Then the formulas of p_S a_S m_N surface and γ_p_S a_S m_N ...First of all, the concept of γ_p_S a_S m_N (confidence level_reliability_stress amplitude_stress mean_fatigue life) surface is presented. Then the formulas of p_S a_S m_N surface and γ_p_S a_S m_N surface are derived. In addition, fatigue strength distribution function and two_dimensional reliability Miner rule are obtained. At last, an example is given.展开更多
Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation ar...Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation are proposed from the viewpoint of both damagemechanics and fracture mechanics. Then the individual isodamage D-S_a-S_m-N surface under constantamplitude loading is constructed and the two-dimensional individual Miner's rule is derived.Consequently, the two-dimensional probabilistic Miner's rule (TPMiner) is established and proved fora population subjected to variable amplitude loading. Finally, with successfully experimentverification, TPMiner proves be to very useful and feasible in fatigue reliability theory.展开更多
Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic load...Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.展开更多
文摘First of all, the concept of γ_p_S a_S m_N (confidence level_reliability_stress amplitude_stress mean_fatigue life) surface is presented. Then the formulas of p_S a_S m_N surface and γ_p_S a_S m_N surface are derived. In addition, fatigue strength distribution function and two_dimensional reliability Miner rule are obtained. At last, an example is given.
基金This project is supported by National Natural Science Foundation of China(No.59605010,No.59979015)Selected from Proceedings of 2000 the First International Conference on Mechanical Engineering
文摘Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation are proposed from the viewpoint of both damagemechanics and fracture mechanics. Then the individual isodamage D-S_a-S_m-N surface under constantamplitude loading is constructed and the two-dimensional individual Miner's rule is derived.Consequently, the two-dimensional probabilistic Miner's rule (TPMiner) is established and proved fora population subjected to variable amplitude loading. Finally, with successfully experimentverification, TPMiner proves be to very useful and feasible in fatigue reliability theory.
基金supported by the National Natural Science Foundation of China(No.10377007)
文摘Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.