It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of gr...It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of grains has its own domain and dislocation structure. There are mono- and polydomains with and without dislocations. The grains of the main phase of monoand polydomains without dislocations and polydomains with dislocations were formed by diffusion in the solid phase. In these conditions NiAl3 phase is located on the grain boundary of the main phase. The Ni2Al3 phase is located at the triple joints of the main phase.展开更多
After milling in a high energy ball miller for various times, the synthesis reaction process of the Al Ti C powder mixture were investigated by difference thermal analysis (DTA) and X ray diffractometry (XRD). Accordi...After milling in a high energy ball miller for various times, the synthesis reaction process of the Al Ti C powder mixture were investigated by difference thermal analysis (DTA) and X ray diffractometry (XRD). According to the patterns of reaction peaks on the DTA curves, the activation energy of each reaction was calculated. The experimental results of DTA show that the synthesis reaction of Al Ti C powder mixture can be enhanced after high energy milling. The longer the milling time, the lower the reaction temperature. The synthesis reaction of TiC is transformed from Ti+C→TiC to Al 3Ti+C→TiC+3Al with long period milling. Meanwhile, the activation energy of the reaction reduces with increasing milling time. The effect of milling time on reduced activation energy for low temperature region is more significant than that for high temperature region.展开更多
The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles o...The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.展开更多
In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM...In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM) was used for extinguishing the propagating combustion wave, and the microstructures on the quenched sample were observed with scanning electron microscope (SEM) and analyzed with energy dispersive spectrometry (EDS). In addition, the combustion temperature of the reaction was measured, and the phase constituent of the synthesized product was inspected by X-ray diffraction (XRD). The results showed that the combustion reaction started from melting of the Al particles, and the melting resulted in dissolving of the Ti particles and forming of Al3Ti grains. As the Al liquid was depleted, the combustion reaction proceeded through solid-state diffusion between the solid Al3Ti and the solid Ti. This led to the forming of TiAl and Ti3Al diffusing layers. In addition, the combustion reaction is incomplete besides TiAl, there are a large amount of Ti3Al and TiAl3 and a small amount of Ti in the final product. This incompleteness chiefly results from the using of coarser Ti powder.展开更多
Objective:To study the protective effect of the Mixture of Shengmai Powder and Danshen Decoction(生脉散丹参饮合剂,abbreviated as the Mixture) in the rat model with type 2 diabetic cardiomyopathy (DCM).Methods:Fo...Objective:To study the protective effect of the Mixture of Shengmai Powder and Danshen Decoction(生脉散丹参饮合剂,abbreviated as the Mixture) in the rat model with type 2 diabetic cardiomyopathy (DCM).Methods:Forty-two SD rats with DCM model,established by the combination of insulin resistance by a high-fat diet with the damage of pancreatic islet p cells by intraperitoneal injection of high dose streptozotocin (50 mg/kg) once,were evaluated in the damage of the myocardium by electrocardiogram at the end of 12 weeks of grouping and intervention administration;the extent of damage in the myocardial subcellular structure was observed by electron microscopy;the content of myocardial collagen in the left cardiac ventricle was quantified by Masson staining test;the myocardial cell apoptosis was determined by TUNEL;the changes in the mRNA expression levels of thrombospodin-1(TSP-1) and tribbles homolog 3(TRB-3) by real-time quantitative PCR,the expression levels of myocardial TSP-1,tumor growth factorβ1(TGF-β1),TRB-3,and chymase were detected by immunohistochemistry,and the changes in the expression levels of myocardial TSP-1,active-TGF-β1 (A-TGF-β1) and latent-TGF-β1(L-TGF-β1) protein were tested by Western blotting.Results:Compared with the control group,the myocardial tissue was less damaged,and the extent of damage in the myocardial subcellular structure was less;the collagen fiber content and the cell apoptosis were reduced;the expression levels of TSP-1 mRNA and TRB-3 mRNA,the expression levels of myocardial TSP-1,TGF-β1,TRB-3,and chymase,as well as the average expression levels of the myocardial TSP-1,A-TGFβ1,and L-TGF-β1 protein were decreased in the Mixture group.Conclusion:The Mixture of Shengmai Powder and Danshen Decoction could inhibit the process of myocardial fibrosis in the rat myocardium of DCM through multiple pathways and significantly delay the genesis and progress of DCM in hyperglycemic rats.展开更多
文摘It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of grains has its own domain and dislocation structure. There are mono- and polydomains with and without dislocations. The grains of the main phase of monoand polydomains without dislocations and polydomains with dislocations were formed by diffusion in the solid phase. In these conditions NiAl3 phase is located on the grain boundary of the main phase. The Ni2Al3 phase is located at the triple joints of the main phase.
文摘After milling in a high energy ball miller for various times, the synthesis reaction process of the Al Ti C powder mixture were investigated by difference thermal analysis (DTA) and X ray diffractometry (XRD). According to the patterns of reaction peaks on the DTA curves, the activation energy of each reaction was calculated. The experimental results of DTA show that the synthesis reaction of Al Ti C powder mixture can be enhanced after high energy milling. The longer the milling time, the lower the reaction temperature. The synthesis reaction of TiC is transformed from Ti+C→TiC to Al 3Ti+C→TiC+3Al with long period milling. Meanwhile, the activation energy of the reaction reduces with increasing milling time. The effect of milling time on reduced activation energy for low temperature region is more significant than that for high temperature region.
文摘The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.
文摘In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM) was used for extinguishing the propagating combustion wave, and the microstructures on the quenched sample were observed with scanning electron microscope (SEM) and analyzed with energy dispersive spectrometry (EDS). In addition, the combustion temperature of the reaction was measured, and the phase constituent of the synthesized product was inspected by X-ray diffraction (XRD). The results showed that the combustion reaction started from melting of the Al particles, and the melting resulted in dissolving of the Ti particles and forming of Al3Ti grains. As the Al liquid was depleted, the combustion reaction proceeded through solid-state diffusion between the solid Al3Ti and the solid Ti. This led to the forming of TiAl and Ti3Al diffusing layers. In addition, the combustion reaction is incomplete besides TiAl, there are a large amount of Ti3Al and TiAl3 and a small amount of Ti in the final product. This incompleteness chiefly results from the using of coarser Ti powder.
基金Supported by the First Grade of China Postdoctoral Science Foundation(No.20070410129)the Special Fund by China Postdoctoral Science Foundation(No.200801166)+1 种基金the Major Project of Beijing Municipal Science and Technology Committee (No.H020920010330)the Subject of Science and Technology Plan of Beijng Municipal Science and Technology Committee(No.D08050703020802)
文摘Objective:To study the protective effect of the Mixture of Shengmai Powder and Danshen Decoction(生脉散丹参饮合剂,abbreviated as the Mixture) in the rat model with type 2 diabetic cardiomyopathy (DCM).Methods:Forty-two SD rats with DCM model,established by the combination of insulin resistance by a high-fat diet with the damage of pancreatic islet p cells by intraperitoneal injection of high dose streptozotocin (50 mg/kg) once,were evaluated in the damage of the myocardium by electrocardiogram at the end of 12 weeks of grouping and intervention administration;the extent of damage in the myocardial subcellular structure was observed by electron microscopy;the content of myocardial collagen in the left cardiac ventricle was quantified by Masson staining test;the myocardial cell apoptosis was determined by TUNEL;the changes in the mRNA expression levels of thrombospodin-1(TSP-1) and tribbles homolog 3(TRB-3) by real-time quantitative PCR,the expression levels of myocardial TSP-1,tumor growth factorβ1(TGF-β1),TRB-3,and chymase were detected by immunohistochemistry,and the changes in the expression levels of myocardial TSP-1,active-TGF-β1 (A-TGF-β1) and latent-TGF-β1(L-TGF-β1) protein were tested by Western blotting.Results:Compared with the control group,the myocardial tissue was less damaged,and the extent of damage in the myocardial subcellular structure was less;the collagen fiber content and the cell apoptosis were reduced;the expression levels of TSP-1 mRNA and TRB-3 mRNA,the expression levels of myocardial TSP-1,TGF-β1,TRB-3,and chymase,as well as the average expression levels of the myocardial TSP-1,A-TGFβ1,and L-TGF-β1 protein were decreased in the Mixture group.Conclusion:The Mixture of Shengmai Powder and Danshen Decoction could inhibit the process of myocardial fibrosis in the rat myocardium of DCM through multiple pathways and significantly delay the genesis and progress of DCM in hyperglycemic rats.