Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to st...Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.展开更多
采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及...采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及分析。结果表明:成功合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)荧光粉且均为纯相;样品的粒径为1~2μm;La_(2)MgTiO_(6)∶Mn^(4+)在650~750 nm的红光发射是来自Mn^(4+)的2 E 1→4 A 2跃迁,La_(2)MgTiO_(6)∶Pr^(3+)在红光区域600~660 nm具有强烈的发射,归属为Pr^(3+)的3 P 0→3 H 6和3 P 0→3 F 2跃迁。当Mn^(4+)与Pr^(3+)共同掺杂于La_(2)MgTiO_(6)时,来自Mn^(4+)、Pr^(3+)不同波段的红光发射使荧光粉的发射光谱与植物光敏色素P r与P fr吸收光谱的重叠程度大幅增加,表明Mn^(4+)、Pr^(3+)共掺有效拓宽了La_(2)MgTiO_(6)荧光粉的红光发射区域,更符合植物照明的需求,在LED植物照明领域具有更明显的潜在应用价值。展开更多
文摘Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.
文摘采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及分析。结果表明:成功合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)荧光粉且均为纯相;样品的粒径为1~2μm;La_(2)MgTiO_(6)∶Mn^(4+)在650~750 nm的红光发射是来自Mn^(4+)的2 E 1→4 A 2跃迁,La_(2)MgTiO_(6)∶Pr^(3+)在红光区域600~660 nm具有强烈的发射,归属为Pr^(3+)的3 P 0→3 H 6和3 P 0→3 F 2跃迁。当Mn^(4+)与Pr^(3+)共同掺杂于La_(2)MgTiO_(6)时,来自Mn^(4+)、Pr^(3+)不同波段的红光发射使荧光粉的发射光谱与植物光敏色素P r与P fr吸收光谱的重叠程度大幅增加,表明Mn^(4+)、Pr^(3+)共掺有效拓宽了La_(2)MgTiO_(6)荧光粉的红光发射区域,更符合植物照明的需求,在LED植物照明领域具有更明显的潜在应用价值。
