TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure ti...TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.展开更多
HZSM-5, Al_2O_3, TiO_2 and SiO_2 supported CeO_2-ZrO_2-CrO_x catalysts were prepared by deposition-precipitation method and tested for deep catalytic oxidation of 1,2-dichloroethane（DCE）, as one of the common chlori...HZSM-5, Al_2O_3, TiO_2 and SiO_2 supported CeO_2-ZrO_2-CrO_x catalysts were prepared by deposition-precipitation method and tested for deep catalytic oxidation of 1,2-dichloroethane（DCE）, as one of the common chlorinated organic pollutants. All the catalysts were characterized by means of N_2 adsorption-desorption, X-ray photoelectron spectroscopy（XPS）, ammonia-temperatureprogrammed desorption（NH_3-TPD） and hydrogen temperature-programmed reduction（H2-TPR）. The characterization results revealed that there was strongly synergistic effect between the oxidizability of CZCr species and the acidity of supports, which obviously promoted the catalytic activity for DCE degradation. 20% CZCr/HZSM-5 showed the highest activity and good durability during the long-term continuous test. The catalytic activity decreased in the order： 20%CZCr/HZSM-5〉CZCr〉20%CZCr/TiO_2〉20%CZCr/Al_2O_3〉20%CZCr/SiO_2.展开更多
To reveal the influence of substrate/coating interdiffusion on the cyclic oxidation property of a metallic coating, cyclic oxida- tion behavior of an EB-PVD CoCrAIY coating on directionally solidified Ni-based superal...To reveal the influence of substrate/coating interdiffusion on the cyclic oxidation property of a metallic coating, cyclic oxida- tion behavior of an EB-PVD CoCrAIY coating on directionally solidified Ni-based superalloy DZ125 at 1 050℃ is investigated. The 40 μm thick CoCrA1Y coating has a cyclic oxidation life of around 160 h, and the oxidation constant is 1.915× 10^-7 mg4.cm^-8.s-1. However, severe spallation of the oxides containing Co, Cr, Ni, Ta and Ti occurs with longer cyclic oxidation. The degradation in oxidation resistance for the coating is related to the depletion of A1 due to the oxide spallation and interdiffu- sion. Severe interdiffusion between the coating and underlying substrate occurs at 1 050 ℃. The composition of the substrate has an important effect on the thermal cycling lifetime of the coating. The influencing mechanism is discussed.展开更多
基金supports from the National Natural Science Foundation of China(Nos.52075472,52004242)the National Key Research and Development Program of China(No.2018YFA0707300)the Natural Science Foundation of Hebei Province,China(No.E2020203001)。
文摘TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.
文摘利用Kirkendall效应,在溶剂热条件下成功制备了复合氧化物Ce1-xTixO2的纳米空心球,并通过XRD,TEM和XPS等测试手段进行了表征.结果表明,Ce1-xTixO2纳米空心球的粒径为65 nm,小于初始状态的CeO2纳米球,并且Ce1-xTixO2纳米空心球的结构与前驱体CeO2晶体结构相同,均为面心立方结构.Ti/Ce摩尔比和温度是影响产物形貌和结构的重要因素,通过实验得出最佳反应条件为n(Ti)∶n(Ce)=8∶10,于190℃反应8 h.
基金Project supports from National Nature Science Foundation of China(21177110)
文摘HZSM-5, Al_2O_3, TiO_2 and SiO_2 supported CeO_2-ZrO_2-CrO_x catalysts were prepared by deposition-precipitation method and tested for deep catalytic oxidation of 1,2-dichloroethane（DCE）, as one of the common chlorinated organic pollutants. All the catalysts were characterized by means of N_2 adsorption-desorption, X-ray photoelectron spectroscopy（XPS）, ammonia-temperatureprogrammed desorption（NH_3-TPD） and hydrogen temperature-programmed reduction（H2-TPR）. The characterization results revealed that there was strongly synergistic effect between the oxidizability of CZCr species and the acidity of supports, which obviously promoted the catalytic activity for DCE degradation. 20% CZCr/HZSM-5 showed the highest activity and good durability during the long-term continuous test. The catalytic activity decreased in the order： 20%CZCr/HZSM-5〉CZCr〉20%CZCr/TiO_2〉20%CZCr/Al_2O_3〉20%CZCr/SiO_2.
基金National Natural Science Foundation of China (50731001, 51071013, 51001032)National Basic Research Program of China (2010CB631200)
文摘To reveal the influence of substrate/coating interdiffusion on the cyclic oxidation property of a metallic coating, cyclic oxida- tion behavior of an EB-PVD CoCrAIY coating on directionally solidified Ni-based superalloy DZ125 at 1 050℃ is investigated. The 40 μm thick CoCrA1Y coating has a cyclic oxidation life of around 160 h, and the oxidation constant is 1.915× 10^-7 mg4.cm^-8.s-1. However, severe spallation of the oxides containing Co, Cr, Ni, Ta and Ti occurs with longer cyclic oxidation. The degradation in oxidation resistance for the coating is related to the depletion of A1 due to the oxide spallation and interdiffu- sion. Severe interdiffusion between the coating and underlying substrate occurs at 1 050 ℃. The composition of the substrate has an important effect on the thermal cycling lifetime of the coating. The influencing mechanism is discussed.