The Mo-N surface modified layer on Ti6Al4V alloy was obtained by the plasma surface alloying technique. The structure and composition of the Mo-N modified Ti6Al4V alloy were investigated by X-ray diffraction （XRD） a...The Mo-N surface modified layer on Ti6Al4V alloy was obtained by the plasma surface alloying technique. The structure and composition of the Mo-N modified Ti6Al4V alloy were investigated by X-ray diffraction （XRD） and glow discharge optical emission spectroscopy （GDOES）. The Mo-N modified layer contains Mo-N coating on subsurface and diffusion layers between the subsurface and substrate. The X- ray diffraction analysis of the Mo-N modified Ti6Al4V alloy reveals that the outmost surface of the Mo-N modified Ti6Al4V alloy is composed of phase Mo2N （fcc） and Mo2N （tetr）. The electrochemical corrosion performance of the Mo-N modified Ti6Al4V alloy in 0.5 mol/L HCl solution was investigated and compared with that of Ti6Al4V alloy. The chemical corrosion performance of the Mo-N modified Ti6Al4V alloy in boiling 37% HCl solution was investigated and compared with that of Ti6Al4V alloy. Results indicate that self-corroding electric potentials and corrosion-rate of the Mo-N modified Ti6Al4V alloy are higher than that of Ti6Al4V alloy in 0.5 mol/L HCl solution. The corrosion-rate of the Mo-N modified Ti6Al4V alloy is lower than that of Ti6Al4V alloy in boiling 37% HCl solution.展开更多
基金Funded by the 863 Program(No.2007AA03Z521)the National Natural Science Foundation of China(No.50771070)the Program for the Top Young and Middle-aged Innovative Talents of Higher Learning Institutions of Shanxi and the Scientific Foundationfor Returned Overseas Scholars of Shanxi Province(No.2006-27)
文摘The Mo-N surface modified layer on Ti6Al4V alloy was obtained by the plasma surface alloying technique. The structure and composition of the Mo-N modified Ti6Al4V alloy were investigated by X-ray diffraction （XRD） and glow discharge optical emission spectroscopy （GDOES）. The Mo-N modified layer contains Mo-N coating on subsurface and diffusion layers between the subsurface and substrate. The X- ray diffraction analysis of the Mo-N modified Ti6Al4V alloy reveals that the outmost surface of the Mo-N modified Ti6Al4V alloy is composed of phase Mo2N （fcc） and Mo2N （tetr）. The electrochemical corrosion performance of the Mo-N modified Ti6Al4V alloy in 0.5 mol/L HCl solution was investigated and compared with that of Ti6Al4V alloy. The chemical corrosion performance of the Mo-N modified Ti6Al4V alloy in boiling 37% HCl solution was investigated and compared with that of Ti6Al4V alloy. Results indicate that self-corroding electric potentials and corrosion-rate of the Mo-N modified Ti6Al4V alloy are higher than that of Ti6Al4V alloy in 0.5 mol/L HCl solution. The corrosion-rate of the Mo-N modified Ti6Al4V alloy is lower than that of Ti6Al4V alloy in boiling 37% HCl solution.