Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, hig...Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T of 20.57 ℃, MFT or5.0 ℃, and good stability, had good stability of film forming.展开更多
Graft-modified polybutadiene(PB) latex was synthesized and used as an admixture to improve the performance of oilwell cement. Results showed that the addition of latex to pure cement slurry can significantly reduce th...Graft-modified polybutadiene(PB) latex was synthesized and used as an admixture to improve the performance of oilwell cement. Results showed that the addition of latex to pure cement slurry can significantly reduce the fluid loss of the cement slurry. When the dosage was 8%, the fluid loss was only 38 mL, and the fluidity of the cement slurry was improved. With an increasing amount of latex, the fluidity of the cement slurry increased continuously. The toughness of cement was significantly enhanced, whose average elastic modulus was 4.2 GPa. Scanning electron microscopy revealed that the filter cake of the cement slurry with latex was thin and dense, and the surface was coated with a layer of latex film. The microstructure of the cement stone showed a high density, and an interweaving mesh network formed in the cement. The results of cement hydration heat analysis and X-ray diffraction showed that latex inhibited the hydration of cement; the effect was stronger under a larger amount of latex. It is indicated that the graft-modified PB latex has great potential to replace the conventional styrene-butadiene rubber(SBR) latex for cementing in the future.展开更多
The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different type...The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.展开更多
文摘Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T of 20.57 ℃, MFT or5.0 ℃, and good stability, had good stability of film forming.
基金supported by the National Science and Technology Major Project of China (No. 2016ZX05020-004)
文摘Graft-modified polybutadiene(PB) latex was synthesized and used as an admixture to improve the performance of oilwell cement. Results showed that the addition of latex to pure cement slurry can significantly reduce the fluid loss of the cement slurry. When the dosage was 8%, the fluid loss was only 38 mL, and the fluidity of the cement slurry was improved. With an increasing amount of latex, the fluidity of the cement slurry increased continuously. The toughness of cement was significantly enhanced, whose average elastic modulus was 4.2 GPa. Scanning electron microscopy revealed that the filter cake of the cement slurry with latex was thin and dense, and the surface was coated with a layer of latex film. The microstructure of the cement stone showed a high density, and an interweaving mesh network formed in the cement. The results of cement hydration heat analysis and X-ray diffraction showed that latex inhibited the hydration of cement; the effect was stronger under a larger amount of latex. It is indicated that the graft-modified PB latex has great potential to replace the conventional styrene-butadiene rubber(SBR) latex for cementing in the future.
文摘The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.