In this paper, a compression-to-tension conversion technique is developed by applying predominant mode I loading test, using a servo-controlled compression system. The technique is applied to thin mortar plate specime...In this paper, a compression-to-tension conversion technique is developed by applying predominant mode I loading test, using a servo-controlled compression system. The technique is applied to thin mortar plate specimens of different widths that include a prefabricated crack on either a single side to facilitate unilateral crack propagation, or prefabricated cracks positioned on both sides asymmetrically with respect to the specimen midpoint to facilitate bilateral crack propagation under direct tensile stress with a loading rate of 0.001 mm/s. The results show that the main pathways of unilateral crack propagation governing specimen failure are fluctuated locally, but present an approximately straight line overall in the absence of pre-existing internal defects. However, the pathways of bilateral crack propagation are relatively complex, although they present similar characteristics. Analysis results suggest that bilateral crack propagation can be basically divided into three stages, i.e. a stage of linear propagation, a stage representing deviation from the other crack, and a stage where one crack approaches either the other crack or approaches the opposite edge of the specimen, and thereby forming a continuous crack through the specimen. In addition, the stressestrain curves of bilateral crack specimens do not vary significantly around the point of peak stress prior to specimen failure, which means that the specimens do not fail instantaneously.展开更多
In order to study the size effect on the AE rate ’a’ value,three kinds of mix ratios were set up by different particle sizes and water cement ratios,45 cement mortar specimens with five different heights were tested...In order to study the size effect on the AE rate ’a’ value,three kinds of mix ratios were set up by different particle sizes and water cement ratios,45 cement mortar specimens with five different heights were tested under axial compression.And the whole damage processes were monitored by full-digital acoustic emission acquisition system,followed by an analysis of mechanical behavior and AE activity.The experimental results show that the height of the cement specimen has significant effects on the compressive strength and the acoustic emission rate ’a’ value,but a slight effect on the accumulated AE hits number,which is analyzed from aspects of failure process of cement mortar specimens.展开更多
When the filler-bitumen ratio of asphalt mortar changes, its adhesion and viscoelasticity will also change, as well as its performance at the high and low temperatures, fatigue durability, and ductility. Thus, the app...When the filler-bitumen ratio of asphalt mortar changes, its adhesion and viscoelasticity will also change, as well as its performance at the high and low temperatures, fatigue durability, and ductility. Thus, the appropriate fillerbitumen ratio directly affects the asphalt mortar＇s performance. This paper tested the physical indexes of the No. 70 matrix asphalt mortar modified by additive Sasobit （SB） and Sasowam （SW） through dynamic shear rheometer and bending beam rheometer under different temperature conditions, and comprehensively analyzed the high-temperature anti-rutting and fatigue performance, low-temperature crack resistance performance, and ductility of asphalt mortar. The results show that ore powder not only can increase the antirutting factor but also can increase the aging resistance of asphalt. SB has better performances than SW at high temperatures. As for the filler-bitumen ratio of asphalt mortar with additive SB, the recommended value is between 0.8 and 1.2, and the value may be a little larger for that with SW.展开更多
Quality of cement is evaluated via group of tests. The most important, and close to understanding, is the compressive strength test. Recently, Egyptian standards adopted the European standards EN-196 and EN-197 for sp...Quality of cement is evaluated via group of tests. The most important, and close to understanding, is the compressive strength test. Recently, Egyptian standards adopted the European standards EN-196 and EN-197 for specifying and evaluating quality of cements. This was motivated by the large European investments in the local production of cement. The current study represents a comparative investigation, experimental and numerical, of the effect of different parameters on evaluation of compressive strength. Main parameters are shape of specimens and type of sand used for producing tested mortars. Three sets of specimens were made for ten types of cements. First set were 70.6 mm cubes molded according to old standards using single sized sand. Second group were prisms molded from standard sand (CEN sand) according to the recent standards. Third group were prisms molded from local sand sieved and regenerated to simulate same grading of CEN sand. All specimens were cured according to relevant standards and tested at different ages (2,3,7,10 and 28 days). Results show that CEM-I Type of cement does not fulfill, in all of its grades, the strength requirements of Ordinary Portland cement OPC specified in old standards. Also, the use of simulated CEN sand from local source gives strengths lower than those obtained using standard certified CEN sand. A limited number of tests were made on concrete specimens from two most common CEM-I types to investigate effect on concrete strength and results were also reported. Numerical investigation of the effect of specimen shape and type of sand on evaluation of compressive strength of mortar specimens, presented in the current study, applies one of the artificial intelligence techniques to simulate and predict the strength behavior at different ages. The Artificial Neural Network (ANN) technique is introduced in the current study to simulate the strength behavior using the available experimental data and predict the strength value at any age in the range of the experiments or in the future. The results of the numerical study showed that the ANN method with less effort was very efficiently capable of simulating the effect of specimen shape and type of sand on the strength behavior of tested mortar with different cement types.展开更多
基金support provided by the Strategic Program of Chinese Academy of Sciences (Grant No. XDB10030400)the Hundred Talent Program of Chinese Academy of Sciences (Grant No. Y323081C01)
文摘In this paper, a compression-to-tension conversion technique is developed by applying predominant mode I loading test, using a servo-controlled compression system. The technique is applied to thin mortar plate specimens of different widths that include a prefabricated crack on either a single side to facilitate unilateral crack propagation, or prefabricated cracks positioned on both sides asymmetrically with respect to the specimen midpoint to facilitate bilateral crack propagation under direct tensile stress with a loading rate of 0.001 mm/s. The results show that the main pathways of unilateral crack propagation governing specimen failure are fluctuated locally, but present an approximately straight line overall in the absence of pre-existing internal defects. However, the pathways of bilateral crack propagation are relatively complex, although they present similar characteristics. Analysis results suggest that bilateral crack propagation can be basically divided into three stages, i.e. a stage of linear propagation, a stage representing deviation from the other crack, and a stage where one crack approaches either the other crack or approaches the opposite edge of the specimen, and thereby forming a continuous crack through the specimen. In addition, the stressestrain curves of bilateral crack specimens do not vary significantly around the point of peak stress prior to specimen failure, which means that the specimens do not fail instantaneously.
基金Funded by the National Natural Science Foundation of China(No.51009058)the Postdoctoral Science Foundation of China(No.2011M501160)
文摘In order to study the size effect on the AE rate ’a’ value,three kinds of mix ratios were set up by different particle sizes and water cement ratios,45 cement mortar specimens with five different heights were tested under axial compression.And the whole damage processes were monitored by full-digital acoustic emission acquisition system,followed by an analysis of mechanical behavior and AE activity.The experimental results show that the height of the cement specimen has significant effects on the compressive strength and the acoustic emission rate ’a’ value,but a slight effect on the accumulated AE hits number,which is analyzed from aspects of failure process of cement mortar specimens.
文摘When the filler-bitumen ratio of asphalt mortar changes, its adhesion and viscoelasticity will also change, as well as its performance at the high and low temperatures, fatigue durability, and ductility. Thus, the appropriate fillerbitumen ratio directly affects the asphalt mortar＇s performance. This paper tested the physical indexes of the No. 70 matrix asphalt mortar modified by additive Sasobit （SB） and Sasowam （SW） through dynamic shear rheometer and bending beam rheometer under different temperature conditions, and comprehensively analyzed the high-temperature anti-rutting and fatigue performance, low-temperature crack resistance performance, and ductility of asphalt mortar. The results show that ore powder not only can increase the antirutting factor but also can increase the aging resistance of asphalt. SB has better performances than SW at high temperatures. As for the filler-bitumen ratio of asphalt mortar with additive SB, the recommended value is between 0.8 and 1.2, and the value may be a little larger for that with SW.
文摘Quality of cement is evaluated via group of tests. The most important, and close to understanding, is the compressive strength test. Recently, Egyptian standards adopted the European standards EN-196 and EN-197 for specifying and evaluating quality of cements. This was motivated by the large European investments in the local production of cement. The current study represents a comparative investigation, experimental and numerical, of the effect of different parameters on evaluation of compressive strength. Main parameters are shape of specimens and type of sand used for producing tested mortars. Three sets of specimens were made for ten types of cements. First set were 70.6 mm cubes molded according to old standards using single sized sand. Second group were prisms molded from standard sand (CEN sand) according to the recent standards. Third group were prisms molded from local sand sieved and regenerated to simulate same grading of CEN sand. All specimens were cured according to relevant standards and tested at different ages (2,3,7,10 and 28 days). Results show that CEM-I Type of cement does not fulfill, in all of its grades, the strength requirements of Ordinary Portland cement OPC specified in old standards. Also, the use of simulated CEN sand from local source gives strengths lower than those obtained using standard certified CEN sand. A limited number of tests were made on concrete specimens from two most common CEM-I types to investigate effect on concrete strength and results were also reported. Numerical investigation of the effect of specimen shape and type of sand on evaluation of compressive strength of mortar specimens, presented in the current study, applies one of the artificial intelligence techniques to simulate and predict the strength behavior at different ages. The Artificial Neural Network (ANN) technique is introduced in the current study to simulate the strength behavior using the available experimental data and predict the strength value at any age in the range of the experiments or in the future. The results of the numerical study showed that the ANN method with less effort was very efficiently capable of simulating the effect of specimen shape and type of sand on the strength behavior of tested mortar with different cement types.