In order to investigate the microstructure of TiN and TiAlN coatings and their effect on the wear resistance of Mg alloy, TiN and TiAlN coatings were deposited on AZ91 magnesium alloy by multi-arc ion plating technolo...In order to investigate the microstructure of TiN and TiAlN coatings and their effect on the wear resistance of Mg alloy, TiN and TiAlN coatings were deposited on AZ91 magnesium alloy by multi-arc ion plating technology.TiN and Ti70Al30N coatings were prepared on the substrate,respectively,which exhibited dark golden color and compact microstructure.The microstructures of TiN and Ti70Al30N coatings were investigated by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).The micro-hardness and wear resistance of TiN and Ti70Al30N coatings were investigated in comparison with the uncoated AZ91 alloy. The XRD peaks assigned to TiN and TiAlN phases are found.The hardness of TiN coatings is two times as high as that of AZ91 alloy, and Ti70Al30N coating exhibits the highest hardness.The wear resistance of the hard coatings increases obviously as result of their high hardness.展开更多
To obtain large-volume non-thermal arc plasma(NTAP), a multiple NTAP generator with three pairs of electrodes has been developed. The arc plasma characteristics, including dynamic process, spatial distribution, and ro...To obtain large-volume non-thermal arc plasma(NTAP), a multiple NTAP generator with three pairs of electrodes has been developed. The arc plasma characteristics, including dynamic process, spatial distribution, and rotation velocity in the discharge zone, were investigated by high speed photograph and image processing methods. The results showed that the dynamic behaviors and spatial distribution of the arc plasma were strongly related to the electrode configuration.A swirl flow of multi-arc plasma was formed by adjusting the electrode configuration, and a steady luminance area was clearly observed in the center of the discharge zone. Moreover, the size of the luminance area increased by decreasing the gas flow rate. The electrical connection in series could be formed between/among these arc columns with their respective driving power supplies in the multi-arc dynamic evolution process. An approximately periodical process of acceleration and deceleration of the arc rotation velocity was observed in the multi-arc generator with swirl flow configuration. In general, the mean velocity of arc rotation was higher in the multi-arc generator with swirl flow configuration when a pair of electrodes driven by a power supply were opposite to each other rather than adjacent.展开更多
After 32CrMoV is selected to manufacture nitrided gears coated with TiN by multi-arc ion plating, all of these uncoated gears and coated gears run in the gearbox under the same initial conditions so as to compare thei...After 32CrMoV is selected to manufacture nitrided gears coated with TiN by multi-arc ion plating, all of these uncoated gears and coated gears run in the gearbox under the same initial conditions so as to compare their difference concerning properties and microstructure. Experiment results indicate that tooth surface of the coated-TiN gears does not suffer surface abnormalities in meshed zone. Instead, the gears with nitrided case exhibit an abrasion mark on the meshed zone of tooth surface, which results in more weight loss of nitrided gears. The morphology of the surface suggests TiN film with more than 2 000 HV is so dense and smooth that coated-TiN gears have higher wear resistance compared with the uncoated gears. The microstructure of coated-TiN gears is finer, hardness is higher and its distribution of coated-TiN gears is more reliable than uncoated ones, which makes nitride layer combined with TiN film tightly. Consequently, the wear-resistance of gears has been dramatically promoted.展开更多
CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and t...CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and tribological properties of the films were significantly affected by the nitrogen pressure and dc-pulsed bias voltage applied to the substrate. The CrTiA1N coatings with the smoothest surfaces were obtained at optimum conditions of nitrogen pressure of 5.0 Pa and bias voltage of -200 V. The samples were found to exhibit a hardness of 2900 HV0.05 with an average friction coefficient of 0.16 and wear rate of 1.5× 10^-16 m^3/N.m against cemented carbide.展开更多
The enhanced volume of thermal plasma is produced by a multi-arc thermal plasma generator with three pairs of discharge electrodes driven by three directed current power suppliers.Combined with a high-speed camera and...The enhanced volume of thermal plasma is produced by a multi-arc thermal plasma generator with three pairs of discharge electrodes driven by three directed current power suppliers.Combined with a high-speed camera and an oscilloscope,which acquire optical and electric signals synchronously,the dynamic behavior of different kinds of multi-arc discharge adjusted by the electrode arrangement is investigated.Also,the spatial distributions and instability of the arc discharge are analyzed in four electrode configurations using the gray value statistical method.It is found that the cathodic arcs mainly show a contracting state,while the anodic arcs have a trend of transition from shrinkage to a diffusion-like state with the increase of the discharge current.As a result of the adjustment of the electrode configuration,a high temperature region formed in the center of the discharge region in configurations of adjacent electrodes with opposite flow distribution and opposite electrodes with swirl flow distribution due to severe fluctuation of arcs.The discharge voltage rises with increased discharge current in this novel multi-arc plasma generator.It is also found that anode ablation mainly occurs on the conical surface at the copper electrode tip,while cathode erosion mainly occurs on the surface of the inserted tungsten and the nearby copper.展开更多
After Rodinia supercontinent was disintegrated in Late Proterozoic, an ocean, namely, Tethys Ocean, occurred between Gondwana continental group and Pan-Cathaysian continental group from Late Proterozoic to Mesozoic. F...After Rodinia supercontinent was disintegrated in Late Proterozoic, an ocean, namely, Tethys Ocean, occurred between Gondwana continental group and Pan-Cathaysian continental group from Late Proterozoic to Mesozoic. From Early Paleozoic to Mesozoic, Tethys Ocean was subducted toward Pan-Cathaysian block group, which results in backarc expansion, arc-land collision and forearc accretion. When the backarc basin expands and reaches the small oceanic basin, ophiolite melange will be generated. As accretion had already occurred in the south of the continental margin in the earlier stage, the succeeding backarc expansion and the frontal arc position were migrated toward south correspondingly. Therefore, multiple ophiolite belts and magmatic rock belts occurred, and show a trend of decreasing age from north toward south. As the continental margin was split and migrated toward south and reached a high latitude position, i.e., with the shortening and subduction of oceanic crust, the sedimentary bodies at high latitude was accreted continuously toward low latitude area together with the formation of oceanic island, mixing of cold-type and warm-type organism was generated. Moreover,blocks split and separated from Pan-Cathaysian or Gondwana continental group cannot traverse the oceanic median ridge and joins with another continental block. As a result, the Kunlun belt on the SW margin of the Pan-Cathaysian land was resulted from the multi-arc orogenesis such as the backarc seabed expansion, arc-arc collision, arc-land collision oceanic bed, and the continuous southward accretion process.展开更多
The multi-arc ion plating technology was employed to prepare the molybdenum films with thickness of 3 μm on the AISI 1045 steel. The wear and scuffing tests were carried out on the ball-on-disc tester. AFM and SEM eq...The multi-arc ion plating technology was employed to prepare the molybdenum films with thickness of 3 μm on the AISI 1045 steel. The wear and scuffing tests were carried out on the ball-on-disc tester. AFM and SEM equipped with EDS were adopted to observe and analyze the morphologies and element compositions of surface,cross-section and worn scar of the Mo film. The phase structure was studied by XRD and the bonding strength between Mo film and substrate was measured by scratching tester. The tribological experiments show that the Mo film possesses a good wear-resistance and an excellent anti-scuffing property. The failure mechanism of Mo film under extreme condition is flaking off.展开更多
This paper presents the formation of Cr-O thin films on an iron substrate by multi-arc ion plating, which are intended to be used as a thermal radiation absorbent in electronic vacuum devices. Only oxygen was used as ...This paper presents the formation of Cr-O thin films on an iron substrate by multi-arc ion plating, which are intended to be used as a thermal radiation absorbent in electronic vacuum devices. Only oxygen was used as a reaction gas during deposition, the Cr-O thin film, must have high adhesion and low outgassing rate. The scratch test shows that the critical load, for an applicable Cr-O thin film deposited in oxygen atmosphere alone at a pressure of 8×10<sup>-1</sup> Pa, was as high as 6kg.展开更多
NCoCrAlSiYHf and CoNiCrAlTaY coatings which belong to protective Al 2O 3 scale forming type were deposited by multi arc ion plating technique . The effect of deposition process parameters on qualities of the coat...NCoCrAlSiYHf and CoNiCrAlTaY coatings which belong to protective Al 2O 3 scale forming type were deposited by multi arc ion plating technique . The effect of deposition process parameters on qualities of the coatings was discussed. The high temperature oxidation performances isothermal oxidation with 950℃ / 500h and 1100℃ / 100h were studied. And also, the hot corrosion performances at 700℃ and 800℃, with molten mixed salt composed of 75%wt Na 2SO 4 and 25%wt NaCl were investigated. Then the high temperature protection decaying mechanisms were proposed.展开更多
CrN/（Ti,Al,Zr,Cr） N bilayer films were successfully deposited on cemented carbide（ WC-8% Co） substrates by multi-arc ion plating process using two Ti-Al-Zr alloy targets and one pure Cr target. As a result of bila...CrN/（Ti,Al,Zr,Cr） N bilayer films were successfully deposited on cemented carbide（ WC-8% Co） substrates by multi-arc ion plating process using two Ti-Al-Zr alloy targets and one pure Cr target. As a result of bilayered structure and addition of alloying elements（ e. g. Al and Cr）,the films exhibited excellent high temperature oxidation resistance under both short-term isothermal（ up to 800 ℃） and long-term cyclic（ up to 600 ℃） exposure conditions. Combined with pre-established outstanding tribological properties（ e. g. maximum hardness of 4 000HV0. 01 and maximum adhesion strength over 200 N）,these observations make such films quite a promising candidate to extend the cutting tool life span and boost the performance in high-productivity,high-speed and high-feed cutting or in dry machining conditions.展开更多
基金Project(1091249-1-00)supported by the Bureau of Science and Technology of Shenyang City,China
文摘In order to investigate the microstructure of TiN and TiAlN coatings and their effect on the wear resistance of Mg alloy, TiN and TiAlN coatings were deposited on AZ91 magnesium alloy by multi-arc ion plating technology.TiN and Ti70Al30N coatings were prepared on the substrate,respectively,which exhibited dark golden color and compact microstructure.The microstructures of TiN and Ti70Al30N coatings were investigated by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).The micro-hardness and wear resistance of TiN and Ti70Al30N coatings were investigated in comparison with the uncoated AZ91 alloy. The XRD peaks assigned to TiN and TiAlN phases are found.The hardness of TiN coatings is two times as high as that of AZ91 alloy, and Ti70Al30N coating exhibits the highest hardness.The wear resistance of the hard coatings increases obviously as result of their high hardness.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11875295 and 11535003)Provincial Science and Technology Major Project of Anhui Province,China(Grant No.17030801035)Key Program of 13th Five-year Plan,CASHIPS,China(Grant No.KP-2017-25)
文摘To obtain large-volume non-thermal arc plasma(NTAP), a multiple NTAP generator with three pairs of electrodes has been developed. The arc plasma characteristics, including dynamic process, spatial distribution, and rotation velocity in the discharge zone, were investigated by high speed photograph and image processing methods. The results showed that the dynamic behaviors and spatial distribution of the arc plasma were strongly related to the electrode configuration.A swirl flow of multi-arc plasma was formed by adjusting the electrode configuration, and a steady luminance area was clearly observed in the center of the discharge zone. Moreover, the size of the luminance area increased by decreasing the gas flow rate. The electrical connection in series could be formed between/among these arc columns with their respective driving power supplies in the multi-arc dynamic evolution process. An approximately periodical process of acceleration and deceleration of the arc rotation velocity was observed in the multi-arc generator with swirl flow configuration. In general, the mean velocity of arc rotation was higher in the multi-arc generator with swirl flow configuration when a pair of electrodes driven by a power supply were opposite to each other rather than adjacent.
基金This project is supported by National Natural Science Foundation of China(No.50375164)Visitor Scholar Project of State Key Laboratory of Mechanical Transmission in Chongqing University,China.
文摘After 32CrMoV is selected to manufacture nitrided gears coated with TiN by multi-arc ion plating, all of these uncoated gears and coated gears run in the gearbox under the same initial conditions so as to compare their difference concerning properties and microstructure. Experiment results indicate that tooth surface of the coated-TiN gears does not suffer surface abnormalities in meshed zone. Instead, the gears with nitrided case exhibit an abrasion mark on the meshed zone of tooth surface, which results in more weight loss of nitrided gears. The morphology of the surface suggests TiN film with more than 2 000 HV is so dense and smooth that coated-TiN gears have higher wear resistance compared with the uncoated gears. The microstructure of coated-TiN gears is finer, hardness is higher and its distribution of coated-TiN gears is more reliable than uncoated ones, which makes nitride layer combined with TiN film tightly. Consequently, the wear-resistance of gears has been dramatically promoted.
基金supported by the China Ministry of Industry and Information Technology (No. 2009ZX04012-032)Basic Research Fund of Central Universities
文摘CrTiAIN coatings were prepared by using a home-made industrial scale multi-arc ion plating system. The coatings were found to be composites of face-center-cubic CrN and TiN. The surface roughness, microhardness, and tribological properties of the films were significantly affected by the nitrogen pressure and dc-pulsed bias voltage applied to the substrate. The CrTiA1N coatings with the smoothest surfaces were obtained at optimum conditions of nitrogen pressure of 5.0 Pa and bias voltage of -200 V. The samples were found to exhibit a hardness of 2900 HV0.05 with an average friction coefficient of 0.16 and wear rate of 1.5× 10^-16 m^3/N.m against cemented carbide.
基金supported by National Natural Science Foundation of China(No.11875295)the National Key R&D Program of China(No.2019YFC0119000)。
文摘The enhanced volume of thermal plasma is produced by a multi-arc thermal plasma generator with three pairs of discharge electrodes driven by three directed current power suppliers.Combined with a high-speed camera and an oscilloscope,which acquire optical and electric signals synchronously,the dynamic behavior of different kinds of multi-arc discharge adjusted by the electrode arrangement is investigated.Also,the spatial distributions and instability of the arc discharge are analyzed in four electrode configurations using the gray value statistical method.It is found that the cathodic arcs mainly show a contracting state,while the anodic arcs have a trend of transition from shrinkage to a diffusion-like state with the increase of the discharge current.As a result of the adjustment of the electrode configuration,a high temperature region formed in the center of the discharge region in configurations of adjacent electrodes with opposite flow distribution and opposite electrodes with swirl flow distribution due to severe fluctuation of arcs.The discharge voltage rises with increased discharge current in this novel multi-arc plasma generator.It is also found that anode ablation mainly occurs on the conical surface at the copper electrode tip,while cathode erosion mainly occurs on the surface of the inserted tungsten and the nearby copper.
文摘After Rodinia supercontinent was disintegrated in Late Proterozoic, an ocean, namely, Tethys Ocean, occurred between Gondwana continental group and Pan-Cathaysian continental group from Late Proterozoic to Mesozoic. From Early Paleozoic to Mesozoic, Tethys Ocean was subducted toward Pan-Cathaysian block group, which results in backarc expansion, arc-land collision and forearc accretion. When the backarc basin expands and reaches the small oceanic basin, ophiolite melange will be generated. As accretion had already occurred in the south of the continental margin in the earlier stage, the succeeding backarc expansion and the frontal arc position were migrated toward south correspondingly. Therefore, multiple ophiolite belts and magmatic rock belts occurred, and show a trend of decreasing age from north toward south. As the continental margin was split and migrated toward south and reached a high latitude position, i.e., with the shortening and subduction of oceanic crust, the sedimentary bodies at high latitude was accreted continuously toward low latitude area together with the formation of oceanic island, mixing of cold-type and warm-type organism was generated. Moreover,blocks split and separated from Pan-Cathaysian or Gondwana continental group cannot traverse the oceanic median ridge and joins with another continental block. As a result, the Kunlun belt on the SW margin of the Pan-Cathaysian land was resulted from the multi-arc orogenesis such as the backarc seabed expansion, arc-arc collision, arc-land collision oceanic bed, and the continuous southward accretion process.
基金Project(50235030) supported by the National Natural Science Foundation of China Project(G1999065009) supported by the National Basic Research Program of China Project(2003AA331130) supported by the Hi-tech Research and Development Program of China
文摘The multi-arc ion plating technology was employed to prepare the molybdenum films with thickness of 3 μm on the AISI 1045 steel. The wear and scuffing tests were carried out on the ball-on-disc tester. AFM and SEM equipped with EDS were adopted to observe and analyze the morphologies and element compositions of surface,cross-section and worn scar of the Mo film. The phase structure was studied by XRD and the bonding strength between Mo film and substrate was measured by scratching tester. The tribological experiments show that the Mo film possesses a good wear-resistance and an excellent anti-scuffing property. The failure mechanism of Mo film under extreme condition is flaking off.
文摘This paper presents the formation of Cr-O thin films on an iron substrate by multi-arc ion plating, which are intended to be used as a thermal radiation absorbent in electronic vacuum devices. Only oxygen was used as a reaction gas during deposition, the Cr-O thin film, must have high adhesion and low outgassing rate. The scratch test shows that the critical load, for an applicable Cr-O thin film deposited in oxygen atmosphere alone at a pressure of 8×10<sup>-1</sup> Pa, was as high as 6kg.
文摘NCoCrAlSiYHf and CoNiCrAlTaY coatings which belong to protective Al 2O 3 scale forming type were deposited by multi arc ion plating technique . The effect of deposition process parameters on qualities of the coatings was discussed. The high temperature oxidation performances isothermal oxidation with 950℃ / 500h and 1100℃ / 100h were studied. And also, the hot corrosion performances at 700℃ and 800℃, with molten mixed salt composed of 75%wt Na 2SO 4 and 25%wt NaCl were investigated. Then the high temperature protection decaying mechanisms were proposed.
基金financially supported by Natural Science Foundation of Liaoning Province of China(No.2014020096)Shenyang Science and Technology Plan Project of Liaoning Province of China(No.F14-231-119 )Shenyang Yongyuan Guanghui Machinery Factory Transverse Project of Liaoning Province of China(No.201521010100051)
文摘CrN/（Ti,Al,Zr,Cr） N bilayer films were successfully deposited on cemented carbide（ WC-8% Co） substrates by multi-arc ion plating process using two Ti-Al-Zr alloy targets and one pure Cr target. As a result of bilayered structure and addition of alloying elements（ e. g. Al and Cr）,the films exhibited excellent high temperature oxidation resistance under both short-term isothermal（ up to 800 ℃） and long-term cyclic（ up to 600 ℃） exposure conditions. Combined with pre-established outstanding tribological properties（ e. g. maximum hardness of 4 000HV0. 01 and maximum adhesion strength over 200 N）,these observations make such films quite a promising candidate to extend the cutting tool life span and boost the performance in high-productivity,high-speed and high-feed cutting or in dry machining conditions.