The effects of operating parameters on oxidative coupling of methane (OCM) over Na-W-Mn/SiO2 catalyst have been studied at elevated pressures of 0.2, 0.3 and 0.4 MPa under low gaseous hourly space velocity (GHSV) ...The effects of operating parameters on oxidative coupling of methane (OCM) over Na-W-Mn/SiO2 catalyst have been studied at elevated pressures of 0.2, 0.3 and 0.4 MPa under low gaseous hourly space velocity (GHSV) and low temperature conditions. Experimental results show that when the operating pressure is increased, C2+ yield slightly decreases, while the maximum ratio of ethylene to ethane remains unchanged. Moreover, it has been found empirically that increase of pressure does not affect the catalyst behavior permanently, the catalyst recovers its original low pressure performance without hysteresis behavior by reducing the pressure. Under the investigated conditions, when oxygen is completely consumed, the increase of GHSV leads to improvement in C2 selectivity, while C3+ and COx selectivities decrease slightly. The C2+ selectivity increases by increase of nitrogen diluent in the feed, but the C3+ hydrocarbons selectivities decrease with increase of nitrogen since it is possible that further dilution at high pressure may reduce the probability of collision between CH3 and C2+ hydrocarbons. During the stability test at high pressure, the catalyst performance remains unchanged throughout the 20 h running. The fresh and used catalysts were characterized using XRD, SEM and N2 adsorption-desorption methods. It was found that the phase transformation of the support from α-cristobalite to tridymite and quartz does not have obvious effect on catalyst performance at high pressure.展开更多
By calcinating commercial silica gel at 1500℃or adding Na2C2O4 and then calcinating at 850℃,α cristobalite was formed.On the basis of the vibration spectroscopy of silica support,Na W Mn/SiO2 catalyst was character...By calcinating commercial silica gel at 1500℃or adding Na2C2O4 and then calcinating at 850℃,α cristobalite was formed.On the basis of the vibration spectroscopy of silica support,Na W Mn/SiO2 catalyst was characterized by Raman spectroscopy.The results show that the structure of support and the interaction among metal components have significant effect on the dispersion and the structure of metal sites,and the tetrahedrally coordinated formed on α cristobalite surface is the most possible site of methane activation with high C2 selectivity.展开更多
Methyl glycolate is a good solvent and can be used as feedstock for the synthesis of some important organic chemicals. Catalytic hydrogenation of dimethyl oxalate (DMO) over copper-silver catalyst supported on silic...Methyl glycolate is a good solvent and can be used as feedstock for the synthesis of some important organic chemicals. Catalytic hydrogenation of dimethyl oxalate (DMO) over copper-silver catalyst supported on silica was studied. The Cu-Ag/SiO2 catalyst supported on silica sol was prepared by homogeneous deposition-precipitation of the mixture of aqueous euprammonia complex and silica sol. The proper active temperature of Cu-Ag/SiO2 catalyst for hydrogenation of DMO was 523-623 K. The most preferable reaction conditions for methyl glycolate (MG) were optimized: temperature at 468-478 K, 40-60 mesh catalyst diameter, H2/DMO ratio 40, and 1.0 h^-1 of LHSV.展开更多
The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent...The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.展开更多
Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS a...Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS analyses and they were tested in partial oxidation of methane(CPO). The catalytic reaction was carried out at atmospheric pressure in a temperature range of 400–800℃ with a feed gas mixture containing methane and oxygen in a molecular ratio CH4/O2=2. The Ni catalyst exhibited 60% methane conversion with 60% selectivity to CO already at 500℃. On the contrary, the Ni–Ce catalyst was inert to CPO up to 700℃. Moreover, the former catalyst reproduced its activity at the descending temperatures maintaining a good stability at 600℃, over a reaction time of 80 h, whereas the latter one completely deactivated. Test of CH4 temperature programmed surface reaction(CH4-TPSR) revealed a higher methane activation temperature(> 100℃) for the Ni–Ce catalyst as compared to the Ni one. Noticeable improvement of the ceria containing catalyst occurred when the reaction test started at a temperature higher than the methane decomposition temperature. In this case, the sample achieved the same catalytic behavior of the Ni catalyst. As confirmed by XPS analyses, the distinct electronic state of the supported nickel was responsible for the differences in catalytic behavior.展开更多
Pd-MoO3/SiO2 catalyst has been prepared using the method of incipient wetness impregnation. The photo absorbing behaviors and chemisorbing properties of the catalyst have been characterized by UV-vis spectra and TPD-M...Pd-MoO3/SiO2 catalyst has been prepared using the method of incipient wetness impregnation. The photo absorbing behaviors and chemisorbing properties of the catalyst have been characterized by UV-vis spectra and TPD-MS experiments. The results indicated that metal Pd loaded on MoOa/SiO2 has a significant effect on the photo absorbing performance of MoOa/SiO2, and an obvious blue shift of the absorption edge is produced. Under UV irradiation, the chemisorption state of CO2 undergoes decomposing process to form CO at 481 K, and a two-site adsorption state of ethane can be formed at around 496 K. Photo-oxidation of ethane using carbon dioxide can mainly produce propanal, ethanol and acetaldehyde in the temperature range of 353-423 K. The presence of metal Pd improves the catalytic activity remarkably.展开更多
The surface species of CO hydrogenation on CeO2-Co/SiO2 catalyst were investigated using the techniques of temperature programmed reaction and transient response method. The results indicated that the formation of H2O...The surface species of CO hydrogenation on CeO2-Co/SiO2 catalyst were investigated using the techniques of temperature programmed reaction and transient response method. The results indicated that the formation of H2O and CO2 was the competitive reaction for the surface oxygen species, CH4 was produced via the hydrogenation of carbon species step by step, and C2 products were formed by the polymerization of surface-active carbon species (-CH2-). Hydrogen assisted the dissociation of CO. The hydrogenation of surface carbon species was the rate-limiting step in the hydrogenation of CO over CeO2-Co/SiO2 catalyst. The investigation of total pressure, gas hourly space velocity (GHSV), and product distribution using nitrogen-rich synthesis gas as feedstock over a laboratory scale fixed-bed reactor indicated that total pressure and GHSV had a significant effect on the catalytic performance of CeO2-Co/SiO2 catalyst. The removal of heat and control of the reaction temperature were extremely critical steps, which required lower GHSV and appropriate CO conversion to avoid the deactivation of the catalyst. The feedstock of nitrogen-rich synthesis gas was favorable to increase the conversion of CO, but there was a shift of product distribution toward the light hydrocarbon. The nitrogen-rich synthesis gas was feasible for F-T synthesis for the utilization of remote natural gas.展开更多
In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation meth...In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species(Mn WO4 and Mn2O3) increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.展开更多
The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis(FTS) without a reduction step. The effect of different citr...The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis(FTS) without a reduction step. The effect of different citric acid(CA):iron nitrate(N) molar ratios and acid types on the FTS performance of catalysts were investigated. The CA:N molar ratios had an important influence on the formation of iron active phases and FTS activity. The iron carbide(FexC), which is known to be one of the iron active phases, was demonstrated by the X-ray diffraction and X-ray photoelectron spectroscopy. Increasing the CA:N molar ratios up to 0.1 increased CO conversion of catalyst to 86.5%, which was then decreased markedly at higher CA:N molar ratios. An excess of CA resulted in carbon residues covering the catalyst surface and declined FTS activity. The optimal catalyst(CA:N molar ratio = 0.1) achieved the highest CO conversion when compared with other autocombustion catalysts as well as reference catalyst prepared by impregnation method, followed by a reduction step. The autocombustion method had the advantage to synthesize more efficient catalysts without a reduction step. More interestingly, iron-based FTS catalysts need induction duration at the initial stage of FTS reaction even after reduction, because metallic iron species need time to be transformed to FexC. But here, even if without reduction, FexC was formed directly by autocombustion and induction period was eliminated during FTS reaction.展开更多
8wt%WO3/SiO2 metathesis (disproportionation) catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-deso...8wt%WO3/SiO2 metathesis (disproportionation) catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy (SEM), X-ray diffraction (XRD), UV-visible diffuse reflectance spectroscopy (DRS) and scanning transmission electron microscopy-high-angle annular dark field (STEM HAADF). The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure: The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.展开更多
Partial oxidation of methane to syngas (POM) over Rh/SiO2 catalyst was investigated using in-situ FT-IR. When methane interacted with 1.0wt%Rh/SiO2 catalyst, it was dissociated to adsorbed hydrogen and CHx species. ...Partial oxidation of methane to syngas (POM) over Rh/SiO2 catalyst was investigated using in-situ FT-IR. When methane interacted with 1.0wt%Rh/SiO2 catalyst, it was dissociated to adsorbed hydrogen and CHx species. The adsorbed hydrogen atoms were transferred to SiO2 surface by "spill-over" and reacted with lattice oxygen to form surface -OH species. POM mechanism was investigated over Rh/SiO2 catalyst using in-situ FT-IR. It was found that CO2 was formed before CO could be detected when CH4 and O2 were introduced over the preoxidized Rh/SiO2 catalyst, whereas CO was detected before CO2 was formed over the prereduced Rh/SiO2 catalyst.展开更多
Copper supported over silica exhibited very high activity and selectivity for the direct synthesis of indole at atmospheric pressure. Under the reaction temperature of 325C,the yield of indole could obtain 88%.
The SiO2-Supported (PPh3)2HPt(μ-CO) (μ-PPh2)M(CO) 4 (M-Cr.Mo, W) complel catalysts catalyzing CO2 hydrogenation are reported.The catalysts exhibited high catalytic activity and selectivity toward oxygenates
The various surface species[H_XRu_3(CO)_9(CCO)]^(2-X)(X=0-2)prepared from impregnation of[PPN]_2[Ru_3(CO)_9(CCO)]on SiO_2-Al_2O_3,SiO_2 and MgO show quite different activities and selectivities for oxygenates and etha...The various surface species[H_XRu_3(CO)_9(CCO)]^(2-X)(X=0-2)prepared from impregnation of[PPN]_2[Ru_3(CO)_9(CCO)]on SiO_2-Al_2O_3,SiO_2 and MgO show quite different activities and selectivities for oxygenates and ethane in ethylene hydroformylation.展开更多
A novel TPPTS-Rh/SiO2 catalyst, prepared by directly modifying a heterogeneous high-surface-area Rh/SiO2 catalyst with water-soluble TPPTS ligands, could decrease the resistance of mass transfer in water/oil biphasic ...A novel TPPTS-Rh/SiO2 catalyst, prepared by directly modifying a heterogeneous high-surface-area Rh/SiO2 catalyst with water-soluble TPPTS ligands, could decrease the resistance of mass transfer in water/oil biphasic media for the hydroformylation of higher olefins. The catalytic performance for hydroformylation on this biphasic TPPTS-Rh/SiO2 catalyst system was higher than those of the traditional biphasic HRhCO(TPPTS)3 systems, owing to the chemical bonds between the highly dispersed Rh metal particles and the TPPTS ligands. The catalyst system is applicable for hydroformylation of higher olefins such as 1-dodecene.展开更多
文摘The effects of operating parameters on oxidative coupling of methane (OCM) over Na-W-Mn/SiO2 catalyst have been studied at elevated pressures of 0.2, 0.3 and 0.4 MPa under low gaseous hourly space velocity (GHSV) and low temperature conditions. Experimental results show that when the operating pressure is increased, C2+ yield slightly decreases, while the maximum ratio of ethylene to ethane remains unchanged. Moreover, it has been found empirically that increase of pressure does not affect the catalyst behavior permanently, the catalyst recovers its original low pressure performance without hysteresis behavior by reducing the pressure. Under the investigated conditions, when oxygen is completely consumed, the increase of GHSV leads to improvement in C2 selectivity, while C3+ and COx selectivities decrease slightly. The C2+ selectivity increases by increase of nitrogen diluent in the feed, but the C3+ hydrocarbons selectivities decrease with increase of nitrogen since it is possible that further dilution at high pressure may reduce the probability of collision between CH3 and C2+ hydrocarbons. During the stability test at high pressure, the catalyst performance remains unchanged throughout the 20 h running. The fresh and used catalysts were characterized using XRD, SEM and N2 adsorption-desorption methods. It was found that the phase transformation of the support from α-cristobalite to tridymite and quartz does not have obvious effect on catalyst performance at high pressure.
文摘By calcinating commercial silica gel at 1500℃or adding Na2C2O4 and then calcinating at 850℃,α cristobalite was formed.On the basis of the vibration spectroscopy of silica support,Na W Mn/SiO2 catalyst was characterized by Raman spectroscopy.The results show that the structure of support and the interaction among metal components have significant effect on the dispersion and the structure of metal sites,and the tetrahedrally coordinated formed on α cristobalite surface is the most possible site of methane activation with high C2 selectivity.
文摘Methyl glycolate is a good solvent and can be used as feedstock for the synthesis of some important organic chemicals. Catalytic hydrogenation of dimethyl oxalate (DMO) over copper-silver catalyst supported on silica was studied. The Cu-Ag/SiO2 catalyst supported on silica sol was prepared by homogeneous deposition-precipitation of the mixture of aqueous euprammonia complex and silica sol. The proper active temperature of Cu-Ag/SiO2 catalyst for hydrogenation of DMO was 523-623 K. The most preferable reaction conditions for methyl glycolate (MG) were optimized: temperature at 468-478 K, 40-60 mesh catalyst diameter, H2/DMO ratio 40, and 1.0 h^-1 of LHSV.
基金Supported by the National Natural Science Foundation of China(21673132).
文摘The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.
基金The Executive Programme for Cooperation between Italy and India (Prot.No.MAE01054762017)。
文摘Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS analyses and they were tested in partial oxidation of methane(CPO). The catalytic reaction was carried out at atmospheric pressure in a temperature range of 400–800℃ with a feed gas mixture containing methane and oxygen in a molecular ratio CH4/O2=2. The Ni catalyst exhibited 60% methane conversion with 60% selectivity to CO already at 500℃. On the contrary, the Ni–Ce catalyst was inert to CPO up to 700℃. Moreover, the former catalyst reproduced its activity at the descending temperatures maintaining a good stability at 600℃, over a reaction time of 80 h, whereas the latter one completely deactivated. Test of CH4 temperature programmed surface reaction(CH4-TPSR) revealed a higher methane activation temperature(> 100℃) for the Ni–Ce catalyst as compared to the Ni one. Noticeable improvement of the ceria containing catalyst occurred when the reaction test started at a temperature higher than the methane decomposition temperature. In this case, the sample achieved the same catalytic behavior of the Ni catalyst. As confirmed by XPS analyses, the distinct electronic state of the supported nickel was responsible for the differences in catalytic behavior.
基金This work was supported by the National Key Basic Research Project of China (No. 2001CCA03600).
文摘Pd-MoO3/SiO2 catalyst has been prepared using the method of incipient wetness impregnation. The photo absorbing behaviors and chemisorbing properties of the catalyst have been characterized by UV-vis spectra and TPD-MS experiments. The results indicated that metal Pd loaded on MoOa/SiO2 has a significant effect on the photo absorbing performance of MoOa/SiO2, and an obvious blue shift of the absorption edge is produced. Under UV irradiation, the chemisorption state of CO2 undergoes decomposing process to form CO at 481 K, and a two-site adsorption state of ethane can be formed at around 496 K. Photo-oxidation of ethane using carbon dioxide can mainly produce propanal, ethanol and acetaldehyde in the temperature range of 353-423 K. The presence of metal Pd improves the catalytic activity remarkably.
基金the National Key Project for Basic Research of China(973 Project)(No.2005CB221402)the China National Petroleum Corporation.
文摘The surface species of CO hydrogenation on CeO2-Co/SiO2 catalyst were investigated using the techniques of temperature programmed reaction and transient response method. The results indicated that the formation of H2O and CO2 was the competitive reaction for the surface oxygen species, CH4 was produced via the hydrogenation of carbon species step by step, and C2 products were formed by the polymerization of surface-active carbon species (-CH2-). Hydrogen assisted the dissociation of CO. The hydrogenation of surface carbon species was the rate-limiting step in the hydrogenation of CO over CeO2-Co/SiO2 catalyst. The investigation of total pressure, gas hourly space velocity (GHSV), and product distribution using nitrogen-rich synthesis gas as feedstock over a laboratory scale fixed-bed reactor indicated that total pressure and GHSV had a significant effect on the catalytic performance of CeO2-Co/SiO2 catalyst. The removal of heat and control of the reaction temperature were extremely critical steps, which required lower GHSV and appropriate CO conversion to avoid the deactivation of the catalyst. The feedstock of nitrogen-rich synthesis gas was favorable to increase the conversion of CO, but there was a shift of product distribution toward the light hydrocarbon. The nitrogen-rich synthesis gas was feasible for F-T synthesis for the utilization of remote natural gas.
基金support from the Ministry of Science and Technology (Nos.2012BAC20B10)the National Natural Science Foundation of China (Nos. 21321061 and 20976109)
文摘In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species(Mn WO4 and Mn2O3) increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.
基金financial support to the Overseas Academic Presentation Scholarship for Graduate Students, Graduate School, Chulalongkorn University
文摘The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis(FTS) without a reduction step. The effect of different citric acid(CA):iron nitrate(N) molar ratios and acid types on the FTS performance of catalysts were investigated. The CA:N molar ratios had an important influence on the formation of iron active phases and FTS activity. The iron carbide(FexC), which is known to be one of the iron active phases, was demonstrated by the X-ray diffraction and X-ray photoelectron spectroscopy. Increasing the CA:N molar ratios up to 0.1 increased CO conversion of catalyst to 86.5%, which was then decreased markedly at higher CA:N molar ratios. An excess of CA resulted in carbon residues covering the catalyst surface and declined FTS activity. The optimal catalyst(CA:N molar ratio = 0.1) achieved the highest CO conversion when compared with other autocombustion catalysts as well as reference catalyst prepared by impregnation method, followed by a reduction step. The autocombustion method had the advantage to synthesize more efficient catalysts without a reduction step. More interestingly, iron-based FTS catalysts need induction duration at the initial stage of FTS reaction even after reduction, because metallic iron species need time to be transformed to FexC. But here, even if without reduction, FexC was formed directly by autocombustion and induction period was eliminated during FTS reaction.
文摘8wt%WO3/SiO2 metathesis (disproportionation) catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy (SEM), X-ray diffraction (XRD), UV-visible diffuse reflectance spectroscopy (DRS) and scanning transmission electron microscopy-high-angle annular dark field (STEM HAADF). The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure: The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.
基金This study was supported by the grant of 2004C31053 from the Ministry of Science and Technology of Zhejiang Province, China, and the grant of Y404305 from the Natural Science Foundation of Zhejiang Province, Chinathe grant of 20673101, 20673102 from National Natural Science Foundation of China.
文摘Partial oxidation of methane to syngas (POM) over Rh/SiO2 catalyst was investigated using in-situ FT-IR. When methane interacted with 1.0wt%Rh/SiO2 catalyst, it was dissociated to adsorbed hydrogen and CHx species. The adsorbed hydrogen atoms were transferred to SiO2 surface by "spill-over" and reacted with lattice oxygen to form surface -OH species. POM mechanism was investigated over Rh/SiO2 catalyst using in-situ FT-IR. It was found that CO2 was formed before CO could be detected when CH4 and O2 were introduced over the preoxidized Rh/SiO2 catalyst, whereas CO was detected before CO2 was formed over the prereduced Rh/SiO2 catalyst.
文摘Copper supported over silica exhibited very high activity and selectivity for the direct synthesis of indole at atmospheric pressure. Under the reaction temperature of 325C,the yield of indole could obtain 88%.
文摘The various surface species[H_XRu_3(CO)_9(CCO)]^(2-X)(X=0-2)prepared from impregnation of[PPN]_2[Ru_3(CO)_9(CCO)]on SiO_2-Al_2O_3,SiO_2 and MgO show quite different activities and selectivities for oxygenates and ethane in ethylene hydroformylation.
文摘A novel TPPTS-Rh/SiO2 catalyst, prepared by directly modifying a heterogeneous high-surface-area Rh/SiO2 catalyst with water-soluble TPPTS ligands, could decrease the resistance of mass transfer in water/oil biphasic media for the hydroformylation of higher olefins. The catalytic performance for hydroformylation on this biphasic TPPTS-Rh/SiO2 catalyst system was higher than those of the traditional biphasic HRhCO(TPPTS)3 systems, owing to the chemical bonds between the highly dispersed Rh metal particles and the TPPTS ligands. The catalyst system is applicable for hydroformylation of higher olefins such as 1-dodecene.