通过简单的溶胶-凝胶辅助静电纺丝法得到(113)晶面优势导向的Na_3V_2(PO_4)_3/C钠离子电池正极材料,并通过对比最佳纺丝条件下分别用聚乙烯吡咯烷酮(PVP)和聚氧化乙烯(PEO)作为晶面导向剂制备的两种Na_3V_2(PO_4)_3电极材料的电化学性能...通过简单的溶胶-凝胶辅助静电纺丝法得到(113)晶面优势导向的Na_3V_2(PO_4)_3/C钠离子电池正极材料,并通过对比最佳纺丝条件下分别用聚乙烯吡咯烷酮(PVP)和聚氧化乙烯(PEO)作为晶面导向剂制备的两种Na_3V_2(PO_4)_3电极材料的电化学性能,证明静电纺丝有利于实现Na_3V_2(PO_4)_3(113)晶面择优取向。在相同的电流密度(0.1 C)下,NVP-PVP和NVP-PEO的首周放电比容量分别为112.5 m A·h/g和96.3 m A·h/g,电池循环50周后,NVP-PVP仍然有98.1 m A·h/g的可逆容量保持,NVP-PEO仅仅只剩下34 m A·h/g的可逆容量保持,而即使循环100周后,NVP-PVP的可逆容量仍然在88.2 m A·h/g。结果表明,PVP静电纺丝有利于构建特定的纳米纤维结构和均一的导电碳网络骨架,进而提升主体材料Na_3V_2(PO_4)_3的电化学性能。展开更多
Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assemb...Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assembling on the surface of Ag2Mo2O7 nanowires. Under visible light irradiation （λ〉420 nm）, the Ag3PO4/Ag/Ag2Mo2O7 com- posite degraded rhodamine B （Rh B） efficiently and showed much higher photocatalytic efficiency than pure AgaPO4, Ag2Mo2O7, or Ag3PO4/Ag2Mo2O7. It was elucidated that the excellent photocatalytic performance of Ag3PO4/Ag/Ag2Mo2O7 for the degradation of Rh B under visible light could be ascribed to the high specific surface area, the extended absorption in the visible light region resulting from the Ag3PO4/Ag loading, and the effi- cient separation of photogenerated electrons and holes through the ternary heterostrucure composed of Ag3PO4, Ag and Ag2Mo2O7.展开更多
采用溶胶凝胶-高温固相法,用不同的钠源制备NASICON结构钠离子电池正极材料Na_3V_2(PO_4)_3.借助扫描电子显微镜(SEM),X射线衍射分析(XRD),电池测试系统及电化学工作站对制备的Na_3V_2(PO_4)_3结构,形貌,电性能和内阻进行表征.研究结果...采用溶胶凝胶-高温固相法,用不同的钠源制备NASICON结构钠离子电池正极材料Na_3V_2(PO_4)_3.借助扫描电子显微镜(SEM),X射线衍射分析(XRD),电池测试系统及电化学工作站对制备的Na_3V_2(PO_4)_3结构,形貌,电性能和内阻进行表征.研究结果表明,以Na_2CO_3为钠源合成Na_3V_2(PO_4)_3有更好的颗粒尺寸,形貌结构完整,充放电性能及循环稳定性更好,阻抗也较小;在2.5~4.0 V电压范围内,以0.2C进行充放电,首次放电比容量达到110.8 m Ah/g,50次循环后容量保持率为85.1%.展开更多
Sodium-ion batteries （SIBs） have attracted increasing attention in the past decades, because of high over-all abundance of precursors, their even geographical distribution, and low cost. Na3V2（PO4）3 （NVP）, atypi...Sodium-ion batteries （SIBs） have attracted increasing attention in the past decades, because of high over-all abundance of precursors, their even geographical distribution, and low cost. Na3V2（PO4）3 （NVP）, atypical sodium super ion conductor （NASlCON）-based electrode material, exhibits pronounced structuralstability, exceptionally high ion conductivity, rendering it a most promising electrode for sodium storage.However. the comparatively low electronic conductivity makes the theoretical capacity of NVP cannot befully accessible even at comparatively low rates, presenting a major drawback for further practical ap-plications, especially when high rate capability is especially important. Thus, many endeavors have beenconformed to increase the surface and intrinsic electrical conductivity of NVP by coating the active mate-rials with a conductive carbon layer, downsizing the NVP particles, combining the NVP particle with vari-ous carbon materials and ion doping strategy. In this review, to get a better understanding on the sodiumstorage in NVP, we firstly present 4 distinct crystal structures in the temperature range of-30℃-225℃ namely α-NVP, β-NVP, β′-NVP and γ-NVP. Moreover, we give an overview of recent approaches to en-hance the surface electrical conductivity and intrinsic electrical conductivity of NVP. Finally, some poten-tial applications of NVP such as in all-climate environment and PHEV, EV fields have been prospected.展开更多
文摘通过简单的溶胶-凝胶辅助静电纺丝法得到(113)晶面优势导向的Na_3V_2(PO_4)_3/C钠离子电池正极材料,并通过对比最佳纺丝条件下分别用聚乙烯吡咯烷酮(PVP)和聚氧化乙烯(PEO)作为晶面导向剂制备的两种Na_3V_2(PO_4)_3电极材料的电化学性能,证明静电纺丝有利于实现Na_3V_2(PO_4)_3(113)晶面择优取向。在相同的电流密度(0.1 C)下,NVP-PVP和NVP-PEO的首周放电比容量分别为112.5 m A·h/g和96.3 m A·h/g,电池循环50周后,NVP-PVP仍然有98.1 m A·h/g的可逆容量保持,NVP-PEO仅仅只剩下34 m A·h/g的可逆容量保持,而即使循环100周后,NVP-PVP的可逆容量仍然在88.2 m A·h/g。结果表明,PVP静电纺丝有利于构建特定的纳米纤维结构和均一的导电碳网络骨架,进而提升主体材料Na_3V_2(PO_4)_3的电化学性能。
基金supported by the National Natural Science Foundation of China(61071040)Leading Academic Discipline Project of Shanghai Municipal Education Commission,China(J50102)Research and Innovation Project of Shanghai Municipal Education Commission,China~~
基金supported by the National Natural Science Foundation of China(No.21407059,No.21576112,No.21407064,and No.21607051)the Science Development Project of Jiangsu Province(BK20140527)+1 种基金the Science and Technology Research Project of the Department of Education of Jilin Province(No.2015220)the Open Subject of the State Key Laboratory of Rare Earth Resource Utilization(RERU2017011)
文摘Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assembling on the surface of Ag2Mo2O7 nanowires. Under visible light irradiation （λ〉420 nm）, the Ag3PO4/Ag/Ag2Mo2O7 com- posite degraded rhodamine B （Rh B） efficiently and showed much higher photocatalytic efficiency than pure AgaPO4, Ag2Mo2O7, or Ag3PO4/Ag2Mo2O7. It was elucidated that the excellent photocatalytic performance of Ag3PO4/Ag/Ag2Mo2O7 for the degradation of Rh B under visible light could be ascribed to the high specific surface area, the extended absorption in the visible light region resulting from the Ag3PO4/Ag loading, and the effi- cient separation of photogenerated electrons and holes through the ternary heterostrucure composed of Ag3PO4, Ag and Ag2Mo2O7.
文摘采用溶胶凝胶-高温固相法,用不同的钠源制备NASICON结构钠离子电池正极材料Na_3V_2(PO_4)_3.借助扫描电子显微镜(SEM),X射线衍射分析(XRD),电池测试系统及电化学工作站对制备的Na_3V_2(PO_4)_3结构,形貌,电性能和内阻进行表征.研究结果表明,以Na_2CO_3为钠源合成Na_3V_2(PO_4)_3有更好的颗粒尺寸,形貌结构完整,充放电性能及循环稳定性更好,阻抗也较小;在2.5~4.0 V电压范围内,以0.2C进行充放电,首次放电比容量达到110.8 m Ah/g,50次循环后容量保持率为85.1%.
基金financial support from the National Natural Science Foundation of China (No.21501171,51403209,21406221,51177156/E0712)
文摘Sodium-ion batteries （SIBs） have attracted increasing attention in the past decades, because of high over-all abundance of precursors, their even geographical distribution, and low cost. Na3V2（PO4）3 （NVP）, atypical sodium super ion conductor （NASlCON）-based electrode material, exhibits pronounced structuralstability, exceptionally high ion conductivity, rendering it a most promising electrode for sodium storage.However. the comparatively low electronic conductivity makes the theoretical capacity of NVP cannot befully accessible even at comparatively low rates, presenting a major drawback for further practical ap-plications, especially when high rate capability is especially important. Thus, many endeavors have beenconformed to increase the surface and intrinsic electrical conductivity of NVP by coating the active mate-rials with a conductive carbon layer, downsizing the NVP particles, combining the NVP particle with vari-ous carbon materials and ion doping strategy. In this review, to get a better understanding on the sodiumstorage in NVP, we firstly present 4 distinct crystal structures in the temperature range of-30℃-225℃ namely α-NVP, β-NVP, β′-NVP and γ-NVP. Moreover, we give an overview of recent approaches to en-hance the surface electrical conductivity and intrinsic electrical conductivity of NVP. Finally, some poten-tial applications of NVP such as in all-climate environment and PHEV, EV fields have been prospected.