Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique.It was found that the mass gain increased rapidly at the beginn...Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique.It was found that the mass gain increased rapidly at the beginning of exposure and then slowly with time.The corrosion morphologies were observed and the results showed that NaCl deposition resulted in the occurrence of localized corrosion.The composition of corrosion product was analyzed using X-ray photo electron spectroscopy.It was suggested that the corrosion product was a mixture of oxide and hydroxide of magnesium and aluminum.展开更多
The corrosion of metals or alloys under solid NaCl deposit in wet oxygen （water vapor and oxygen） at medium temperature 4013-700℃ causes serious damage and has received considerable attention in recent years. Serie...The corrosion of metals or alloys under solid NaCl deposit in wet oxygen （water vapor and oxygen） at medium temperature 4013-700℃ causes serious damage and has received considerable attention in recent years. Series of mechanistic studies have revealed synergistic interactions between solid NaCl and water vapor, which accelerates the corrosion process. In addition, the overall corrosion process comprises both chemical reactions （oxidation） and electrochemical reactions and their mutual inter- actions depend on the system of interest. Interestingly, the wet oxygen environment was found to modify the reactions of the element Cr, which plays a useful role in corrosion protection in this special environment.展开更多
基金Projects(50671005,50971093)supported by the National Natural Science Foundation of ChinaProject(2007CB613705)supported by the National Basic Research Program of China
文摘Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique.It was found that the mass gain increased rapidly at the beginning of exposure and then slowly with time.The corrosion morphologies were observed and the results showed that NaCl deposition resulted in the occurrence of localized corrosion.The composition of corrosion product was analyzed using X-ray photo electron spectroscopy.It was suggested that the corrosion product was a mixture of oxide and hydroxide of magnesium and aluminum.
基金supported by the National Natural Science Fundation of China (Grant Nos. 50671113 and 50801063)
文摘The corrosion of metals or alloys under solid NaCl deposit in wet oxygen （water vapor and oxygen） at medium temperature 4013-700℃ causes serious damage and has received considerable attention in recent years. Series of mechanistic studies have revealed synergistic interactions between solid NaCl and water vapor, which accelerates the corrosion process. In addition, the overall corrosion process comprises both chemical reactions （oxidation） and electrochemical reactions and their mutual inter- actions depend on the system of interest. Interestingly, the wet oxygen environment was found to modify the reactions of the element Cr, which plays a useful role in corrosion protection in this special environment.
