Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nano...Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.展开更多
The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds w...The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds were characterized by chemical analysis,X-ray powder dif fraction,FT-IR spectra and thermal analysis.展开更多
A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use o...A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.展开更多
Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. I...Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. In the course of processing, the effects of various molar ratios of ZnCl2/H2O/C2H5OH on the filter paper performance were evaluated. SEMEDX was conducted to analyze the physical configuration of the filter papers. Moreover, FT-IR and XPS were performed to further characterize the BSKP, the pretreated BSKP and the filter paper fibers. The results indicated that the fibers treated by ZnCl2/H2O/C2H5OH were swollen and exhibited slight fibrillation, leading to a looser fiber structure and therefore, enhanced filter paper performance. Air permeability increased from 161.7 L/(m2·s) to 1450.4 L/(m2·s) for the filter papers when the molar ratio of ZnCl2/H2O/C2H5OH was 1:14:1. The optimum molar ratio of ZnCl2/H2O/C2H5OH was found to be 1:14:1, and no significant effect of ZnCl2/H2O/C2H5OH on fibers’ functional groups was detected. These results showed that filtration performance of filter papers was improved when treated with the ZnCl2/H2O/C2H5OH solution.展开更多
The electronic structure and chemical bonding of the title comp- lexes have been studied by an unrestricted INDO program made applicable for the lanthanoid compounds.The results indicated:(1)In coordinated bonds O-Ln ...The electronic structure and chemical bonding of the title comp- lexes have been studied by an unrestricted INDO program made applicable for the lanthanoid compounds.The results indicated:(1)In coordinated bonds O-Ln and N-Ln,5d orbitals of Ln have large contribution in all valence orbitals of Ln and 4f orbitals have very small contribution.(2)The covalent chara- cter and ionic character are almost equal in the chemical bond which is comparatively weak between phen,C_2H_5OH and Ln are mainly ionic with some covalent character.展开更多
To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O ...To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O （152 MOS） single component was prepared by hydrothermal synthesis reaction in MgSO4 solution and NaOH solution. MgO whisker was prepared by heating treatment of the precursor at low heating speed to keep the structure of the precursor not be destroyed. The composition, the morphology and the structure of these whiskers were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicate that the MgO whisker was about 0.5-1.2 μm in diameter and 20-80 μm in length, with an aspect ratio no less than 100.展开更多
The anode material Zn4SO4（OH）6·5H2O for nickle/zinc batteries was synthesized by hydrothermal method and was identified by XRD techniques. TG/DAT measurements reveal that the products lose lattice water at 145 ...The anode material Zn4SO4（OH）6·5H2O for nickle/zinc batteries was synthesized by hydrothermal method and was identified by XRD techniques. TG/DAT measurements reveal that the products lose lattice water at 145 ℃ and decompose to 3ZnO·ZnSO4 at 274 ℃. Cyclic voltammetry and recharging/discharging results show that CV curves have good symmetry, the ratio of oxidation area to reduction area for each curve is about 1, and the peak potential EPa and EPc have little change with the scanning rate. At 50th circle, more than 65% of theoretical capacity is obtained while at the same condition, zinc oxide electrode only remains 35% of theoretical capacity.展开更多
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
文摘Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.
文摘The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds were characterized by chemical analysis,X-ray powder dif fraction,FT-IR spectra and thermal analysis.
基金Supported by the National Natural Science Foundation of China(Nos.20671011,20331010,90406002and90406024)the 111 Project(No.B07012)the Key Laboratory of Structural Chemistry Foundation(No.060017).
文摘A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.
基金the support of the Natural Science Foundation of Heilongjiang Province (Grant No. C2018007)
文摘Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. In the course of processing, the effects of various molar ratios of ZnCl2/H2O/C2H5OH on the filter paper performance were evaluated. SEMEDX was conducted to analyze the physical configuration of the filter papers. Moreover, FT-IR and XPS were performed to further characterize the BSKP, the pretreated BSKP and the filter paper fibers. The results indicated that the fibers treated by ZnCl2/H2O/C2H5OH were swollen and exhibited slight fibrillation, leading to a looser fiber structure and therefore, enhanced filter paper performance. Air permeability increased from 161.7 L/(m2·s) to 1450.4 L/(m2·s) for the filter papers when the molar ratio of ZnCl2/H2O/C2H5OH was 1:14:1. The optimum molar ratio of ZnCl2/H2O/C2H5OH was found to be 1:14:1, and no significant effect of ZnCl2/H2O/C2H5OH on fibers’ functional groups was detected. These results showed that filtration performance of filter papers was improved when treated with the ZnCl2/H2O/C2H5OH solution.
文摘The electronic structure and chemical bonding of the title comp- lexes have been studied by an unrestricted INDO program made applicable for the lanthanoid compounds.The results indicated:(1)In coordinated bonds O-Ln and N-Ln,5d orbitals of Ln have large contribution in all valence orbitals of Ln and 4f orbitals have very small contribution.(2)The covalent chara- cter and ionic character are almost equal in the chemical bond which is comparatively weak between phen,C_2H_5OH and Ln are mainly ionic with some covalent character.
文摘To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O （152 MOS） single component was prepared by hydrothermal synthesis reaction in MgSO4 solution and NaOH solution. MgO whisker was prepared by heating treatment of the precursor at low heating speed to keep the structure of the precursor not be destroyed. The composition, the morphology and the structure of these whiskers were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicate that the MgO whisker was about 0.5-1.2 μm in diameter and 20-80 μm in length, with an aspect ratio no less than 100.
文摘The anode material Zn4SO4（OH）6·5H2O for nickle/zinc batteries was synthesized by hydrothermal method and was identified by XRD techniques. TG/DAT measurements reveal that the products lose lattice water at 145 ℃ and decompose to 3ZnO·ZnSO4 at 274 ℃. Cyclic voltammetry and recharging/discharging results show that CV curves have good symmetry, the ratio of oxidation area to reduction area for each curve is about 1, and the peak potential EPa and EPc have little change with the scanning rate. At 50th circle, more than 65% of theoretical capacity is obtained while at the same condition, zinc oxide electrode only remains 35% of theoretical capacity.