Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of...Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.展开更多
A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of app...A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.展开更多
A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solut...A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solution used in impregnation and Al2O3 concentration, were varied to investigate the effects on catalytic performance of Pt-SO42-/ZrO2-A12O3. The results showed that the PtSZA catalyst exhibited excellent catalytic performance for n-pentane isomerization. Under optimized preparation conditions of calcination temperature of 650°C, reaction time for 3 h, concentration of sulfuric acid solution for 0.5 mol/L, 30% of Al2O3 concentration and 0.3% of Pt concentration, the n-pentane conversion and isopentane selectivity of Pt-SO42-/ZrO2-A12O3 could reach up to 62.17% and 91.60%, respectively.展开更多
文摘Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.
基金supported by the Science and Technique Foundation of Shaaxi Province of China (2008K07-32)the Foundation of Shaanxi Educa- tional Committee of China (08JK228)the Graduate Innovation Fund of Shaanxi University of Science and Technology
文摘A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.
文摘A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solution used in impregnation and Al2O3 concentration, were varied to investigate the effects on catalytic performance of Pt-SO42-/ZrO2-A12O3. The results showed that the PtSZA catalyst exhibited excellent catalytic performance for n-pentane isomerization. Under optimized preparation conditions of calcination temperature of 650°C, reaction time for 3 h, concentration of sulfuric acid solution for 0.5 mol/L, 30% of Al2O3 concentration and 0.3% of Pt concentration, the n-pentane conversion and isopentane selectivity of Pt-SO42-/ZrO2-A12O3 could reach up to 62.17% and 91.60%, respectively.