The （ 200 ） dominated Nd： LuVO4 films were fabricated successfully on polished SlOE under different ambient gases and different oxygen pressures. By XRD, it is shown that a film with good crystallization is deposit...The （ 200 ） dominated Nd： LuVO4 films were fabricated successfully on polished SlOE under different ambient gases and different oxygen pressures. By XRD, it is shown that a film with good crystallization is deposited under oxygen and the optimal pressure is 20 Pa. The surface morphology of Nd：LuVO4 films was observed by AFM, and it is found that oxygen pressure influences the surface morphology of Nd ：LuVO4 films. The ratio of content of Nd：LuVO4 films was estimated according to the yields of Lu and V by using RBS spectra, this ratio is in good agreement with the target composition. The effective index refractive of every mode is 2.0044, 1.7098, measured by prism coupler method.展开更多
文摘The （ 200 ） dominated Nd： LuVO4 films were fabricated successfully on polished SlOE under different ambient gases and different oxygen pressures. By XRD, it is shown that a film with good crystallization is deposited under oxygen and the optimal pressure is 20 Pa. The surface morphology of Nd：LuVO4 films was observed by AFM, and it is found that oxygen pressure influences the surface morphology of Nd ：LuVO4 films. The ratio of content of Nd：LuVO4 films was estimated according to the yields of Lu and V by using RBS spectra, this ratio is in good agreement with the target composition. The effective index refractive of every mode is 2.0044, 1.7098, measured by prism coupler method.