The phase component and Curie tempemture of Nd4(Fe1-xCrx)77.5B18.5 (0 <x <0.25) alloys have been studied. X-ray diffraction analysis shows the presence of α-Fe and Fe3B phases in the samples with x < 0.1 and...The phase component and Curie tempemture of Nd4(Fe1-xCrx)77.5B18.5 (0 <x <0.25) alloys have been studied. X-ray diffraction analysis shows the presence of α-Fe and Fe3B phases in the samples with x < 0.1 and the presence of α-Fe, Nd2Fe14B and Fe2B phases in the samples with x > 0.1. The magnetic measurement shows that Curie temperutures of Fe3B and Nd2Fe14B phases decrease with increasing Cr content. The influence of the substitution of Cr for Fe was discussed.展开更多
The Curie temperature increases but crystallization temperature decreases with the in- crease of Ga content,x,of amorphous(Fe_(1-x)Ga_x)_(77.5)Nd_4B_(18.5) alloys.The average magnetic moment of Fe atoms is almost a co...The Curie temperature increases but crystallization temperature decreases with the in- crease of Ga content,x,of amorphous(Fe_(1-x)Ga_x)_(77.5)Nd_4B_(18.5) alloys.The average magnetic moment of Fe atoms is almost a constant.By X-ray diffraction and ther- momagnetic measurements,the crystalline phases of the alloys,an unknown phase and α-(Fe,Ga)besides Fe_3 B as major one,were identified.The relationship between room temperature coercive field and Ga.content was also studied.展开更多
文摘The phase component and Curie tempemture of Nd4(Fe1-xCrx)77.5B18.5 (0 <x <0.25) alloys have been studied. X-ray diffraction analysis shows the presence of α-Fe and Fe3B phases in the samples with x < 0.1 and the presence of α-Fe, Nd2Fe14B and Fe2B phases in the samples with x > 0.1. The magnetic measurement shows that Curie temperutures of Fe3B and Nd2Fe14B phases decrease with increasing Cr content. The influence of the substitution of Cr for Fe was discussed.
文摘The Curie temperature increases but crystallization temperature decreases with the in- crease of Ga content,x,of amorphous(Fe_(1-x)Ga_x)_(77.5)Nd_4B_(18.5) alloys.The average magnetic moment of Fe atoms is almost a constant.By X-ray diffraction and ther- momagnetic measurements,the crystalline phases of the alloys,an unknown phase and α-(Fe,Ga)besides Fe_3 B as major one,were identified.The relationship between room temperature coercive field and Ga.content was also studied.