The stress corrosion cracking (SCC) behaviour of X-70 pipeline steel in near-neutral pH solutions was studied via slow strain rate testing (SSRT). The results showed that the cracking mode of X-70 pipeline steel in ne...The stress corrosion cracking (SCC) behaviour of X-70 pipeline steel in near-neutral pH solutions was studied via slow strain rate testing (SSRT). The results showed that the cracking mode of X-70 pipeline steel in near-neutral pH solutions was transgranular at different temperatures and applied potentials with the feature of quasi-cleavage. The pH value of the solution decreased with increasing the addition of CO2, which increased the susceptibility to SCC. SCC susceptibility increased as the applied potential moved towards the cathodic direction, suggesting that hydrogen induced cracking (HIC) dominated the cracking process at cathodic potentials. The slight decrease of pH values with decreasing temperature of the solution increased the susceptibility to SCC, which attributed to the change of solubility of CO2 in the solution at different temperatures. The propagating directions of SCC cracks were different at different potentials. At rather negative cathodic potentials, the cracks were almost perpendicular to the tensile axis, while at free corrosion potential and near anodic potentials, cracks were nearly at 45 degree, and in the range of moderate cathodic potentials both propagating directions could be observed.展开更多
The cracking behaviour of X-70 pipeline steel in near-neutral pH solutions was studied under different modes of cyclic loading. The crack propagation process of X-70 pipeline steel under low frequency cyclic loading c...The cracking behaviour of X-70 pipeline steel in near-neutral pH solutions was studied under different modes of cyclic loading. The crack propagation process of X-70 pipeline steel under low frequency cyclic loading condition was controlled mainly by stress corrosion cracking （SCC） mechanism. Under mixed-mode cyclic loading, both higher tensile stress and shear stress made cracks easier to propagate. Applied cathodic potentials and high content of carbon dioxide in solutions also promoted the propagation of cracks. The propagation directions of cracks were different under different cyclic loading conditions. Under mode I （pure tensile stress） cyclic loading condition, cracks were straight and perpendicular to the tensile stress axis, while under mixed-mode 1/111 （tensile/shear stress） cyclic loading,cracks were sinuous and did not propagate in the direction perpendicular to the main tensile stress axis. Under the mixed-mode cyclic loading, cracks were much easier to propagate, suggesting that shear stress intensified the role of tensile stress. In addition, shear stress promoted the interaction between cracks, resulting in easier coalescence of cracks.展开更多
The passive film-induced stress and the susceptibility to SCC of 7050 aluminum alloy in 3.5%sodium chloride solution at various pH values were investigated by slow strain rate testing（SSRT） and flowing stress differ...The passive film-induced stress and the susceptibility to SCC of 7050 aluminum alloy in 3.5%sodium chloride solution at various pH values were investigated by slow strain rate testing（SSRT） and flowing stress differential method.The results showed that the passive film-induced stress and the susceptibility to SCC decreased with increasing pH values when pH≤7,while they increased with increasing pH values when pH7.However,the corrosion type was interpreted as exfoliation corrosion when pH=l and 14,and there was no film formed on the surface of the specimens.The whole variation plots of film-induced stress and the SCC susceptibility with pH values were both presented as a valley shape.The symbol and amount of the film-induced stress were related to the compositions of the passive film,which were analyzed using X-ray photoelectron spectroscopy（XPS）.展开更多
Constant load tests in NS4 solution purged with N2-5%CO2 gas mixture were conducted on American Petroleum Institute （API） X80 pipeline steel applied in the 2nd West-East （;as Pipeline project with and without prelo...Constant load tests in NS4 solution purged with N2-5%CO2 gas mixture were conducted on American Petroleum Institute （API） X80 pipeline steel applied in the 2nd West-East （;as Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation.展开更多
This paper provides a review of the differences between high pH and near-neutral pH stress corrosion cracking of pipeline steels, influencing factors, and mechanisms. The characteristics and historical information on ...This paper provides a review of the differences between high pH and near-neutral pH stress corrosion cracking of pipeline steels, influencing factors, and mechanisms. The characteristics and historical information on both forms of SCC are discussed. The prospect for research in the future is also presented.展开更多
基金This work was supported by the Special Funds for the Major State Basic Research Projects G19990650 in China,also supported by the Science and Technology Commission of Shanghai Municipality via projects 025258036 and 02ZE14031.
文摘The stress corrosion cracking (SCC) behaviour of X-70 pipeline steel in near-neutral pH solutions was studied via slow strain rate testing (SSRT). The results showed that the cracking mode of X-70 pipeline steel in near-neutral pH solutions was transgranular at different temperatures and applied potentials with the feature of quasi-cleavage. The pH value of the solution decreased with increasing the addition of CO2, which increased the susceptibility to SCC. SCC susceptibility increased as the applied potential moved towards the cathodic direction, suggesting that hydrogen induced cracking (HIC) dominated the cracking process at cathodic potentials. The slight decrease of pH values with decreasing temperature of the solution increased the susceptibility to SCC, which attributed to the change of solubility of CO2 in the solution at different temperatures. The propagating directions of SCC cracks were different at different potentials. At rather negative cathodic potentials, the cracks were almost perpendicular to the tensile axis, while at free corrosion potential and near anodic potentials, cracks were nearly at 45 degree, and in the range of moderate cathodic potentials both propagating directions could be observed.
基金This work was supported by the Special Funds for the Major State Basic Research Projects in China(No.G19990650)also supported by the Science and Technology Comm is—sion of Shanghai Municipality(Projects Nos.025258036 and 02ZE14031
文摘The cracking behaviour of X-70 pipeline steel in near-neutral pH solutions was studied under different modes of cyclic loading. The crack propagation process of X-70 pipeline steel under low frequency cyclic loading condition was controlled mainly by stress corrosion cracking （SCC） mechanism. Under mixed-mode cyclic loading, both higher tensile stress and shear stress made cracks easier to propagate. Applied cathodic potentials and high content of carbon dioxide in solutions also promoted the propagation of cracks. The propagation directions of cracks were different under different cyclic loading conditions. Under mode I （pure tensile stress） cyclic loading condition, cracks were straight and perpendicular to the tensile stress axis, while under mixed-mode 1/111 （tensile/shear stress） cyclic loading,cracks were sinuous and did not propagate in the direction perpendicular to the main tensile stress axis. Under the mixed-mode cyclic loading, cracks were much easier to propagate, suggesting that shear stress intensified the role of tensile stress. In addition, shear stress promoted the interaction between cracks, resulting in easier coalescence of cracks.
基金Funded by the National Natural Science Foundation of China(No.51371039)
文摘The passive film-induced stress and the susceptibility to SCC of 7050 aluminum alloy in 3.5%sodium chloride solution at various pH values were investigated by slow strain rate testing（SSRT） and flowing stress differential method.The results showed that the passive film-induced stress and the susceptibility to SCC decreased with increasing pH values when pH≤7,while they increased with increasing pH values when pH7.However,the corrosion type was interpreted as exfoliation corrosion when pH=l and 14,and there was no film formed on the surface of the specimens.The whole variation plots of film-induced stress and the SCC susceptibility with pH values were both presented as a valley shape.The symbol and amount of the film-induced stress were related to the compositions of the passive film,which were analyzed using X-ray photoelectron spectroscopy（XPS）.
基金supported by the National Natural Science Foundation of China (Grant No. 51025104)
文摘Constant load tests in NS4 solution purged with N2-5%CO2 gas mixture were conducted on American Petroleum Institute （API） X80 pipeline steel applied in the 2nd West-East （;as Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation.
文摘This paper provides a review of the differences between high pH and near-neutral pH stress corrosion cracking of pipeline steels, influencing factors, and mechanisms. The characteristics and historical information on both forms of SCC are discussed. The prospect for research in the future is also presented.