基于试验数据,利用扩展有限元方法(extended finite element method,XFEM)和内聚力模型(cohesive zone model,CZM),对20Cr2Ni3钢顶头表面氧化膜的断裂行为进行了数值分析,研究了氧化膜受力方向和孔洞对裂纹生长行为的影响。结果表明:氧...基于试验数据,利用扩展有限元方法(extended finite element method,XFEM)和内聚力模型(cohesive zone model,CZM),对20Cr2Ni3钢顶头表面氧化膜的断裂行为进行了数值分析,研究了氧化膜受力方向和孔洞对裂纹生长行为的影响。结果表明:氧化膜受力方向影响裂纹扩展路径,外层氧化膜裂纹尖端的J积分和应力强度因子K_I随着θ角(受力方向与氧化膜的夹角)的增大而减小,当θ角增大到90°时裂纹停止生长;外层氧化膜上孔洞使得裂纹尖端的J积分和应力强度因子K_I减小。同时,孔洞的存在使得外力传递到内层氧化膜时产生应力集中和偏移,导致内层裂纹受力不均,减小了受力方向对内层裂纹生长的影响。展开更多
MgH_(2) is considered one of the most promising hydrogen storage materials because of its safety,high efficiency,high hydrogen storage quantity and low cost characteristics.But some shortcomings are still existed:high...MgH_(2) is considered one of the most promising hydrogen storage materials because of its safety,high efficiency,high hydrogen storage quantity and low cost characteristics.But some shortcomings are still existed:high operating temperature and poor hydrogen absorption dynamics,which limit its application.Porous Ni_(3)ZnC_(0.7)/Ni loaded carbon nanotubes microspheres(NZC/Ni@CNT)is prepared by facile filtration and calcination method.Then the different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%)is added to the MgH_(2) by ball milling.Among the three samples with different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%),the MgH_(2)-5 wt%NZC/Ni@CNT composite exhibits the best hydrogen storage performances.After testing,the MgH_(2)-5 wt%NZC/Ni@CNT begins to release hydrogen at around 110℃ and hydrogen absorption capacity reaches 2.34 wt%H_(2) at 80℃ within 60 min.Moreover,the composite can release about 5.36 wt%H_(2) at 300℃.In addition,hydrogen absorption and desorption activation energies of the MgH_(2)-5 wt%NZC/Ni@CNT composite are reduced to 37.28 and 84.22 KJ/mol H_(2),respectively.The in situ generated Mg_(2)NiH_(4)/Mg_(2)Ni can serve as a"hydrogen pump"that plays the main role in providing more activation sites and hydrogen diffusion channels which promotes H_(2) dissociation during hydrogen absorption process.In addition,the evenly dispersed Zn and MgZn2 in Mg and MgH_(2) could provide sites for Mg/MgH_(2) nucleation and hydrogen diffusion channel.This attempt clearly proved that the bimetallic carbide Ni_(3)ZnC_(0.7) is a effective additive for the hydrogen storage performances modification of MgH_(2),and the facile synthesis of the Ni_(3)ZnC_(0.7)/Ni@CNT can provide directions of better designing high performance carbide catalysts for improving MgH_(2).展开更多
文摘基于试验数据,利用扩展有限元方法(extended finite element method,XFEM)和内聚力模型(cohesive zone model,CZM),对20Cr2Ni3钢顶头表面氧化膜的断裂行为进行了数值分析,研究了氧化膜受力方向和孔洞对裂纹生长行为的影响。结果表明:氧化膜受力方向影响裂纹扩展路径,外层氧化膜裂纹尖端的J积分和应力强度因子K_I随着θ角(受力方向与氧化膜的夹角)的增大而减小,当θ角增大到90°时裂纹停止生长;外层氧化膜上孔洞使得裂纹尖端的J积分和应力强度因子K_I减小。同时,孔洞的存在使得外力传递到内层氧化膜时产生应力集中和偏移,导致内层裂纹受力不均,减小了受力方向对内层裂纹生长的影响。
基金supported by research programs of National Natural Science Foundation of China(52101274,51731002)Natural Science Foundation of Shandong Province(No.ZR2020QE011)Youth Top Talent Foundation of Yantai University(2219008).
文摘MgH_(2) is considered one of the most promising hydrogen storage materials because of its safety,high efficiency,high hydrogen storage quantity and low cost characteristics.But some shortcomings are still existed:high operating temperature and poor hydrogen absorption dynamics,which limit its application.Porous Ni_(3)ZnC_(0.7)/Ni loaded carbon nanotubes microspheres(NZC/Ni@CNT)is prepared by facile filtration and calcination method.Then the different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%)is added to the MgH_(2) by ball milling.Among the three samples with different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%),the MgH_(2)-5 wt%NZC/Ni@CNT composite exhibits the best hydrogen storage performances.After testing,the MgH_(2)-5 wt%NZC/Ni@CNT begins to release hydrogen at around 110℃ and hydrogen absorption capacity reaches 2.34 wt%H_(2) at 80℃ within 60 min.Moreover,the composite can release about 5.36 wt%H_(2) at 300℃.In addition,hydrogen absorption and desorption activation energies of the MgH_(2)-5 wt%NZC/Ni@CNT composite are reduced to 37.28 and 84.22 KJ/mol H_(2),respectively.The in situ generated Mg_(2)NiH_(4)/Mg_(2)Ni can serve as a"hydrogen pump"that plays the main role in providing more activation sites and hydrogen diffusion channels which promotes H_(2) dissociation during hydrogen absorption process.In addition,the evenly dispersed Zn and MgZn2 in Mg and MgH_(2) could provide sites for Mg/MgH_(2) nucleation and hydrogen diffusion channel.This attempt clearly proved that the bimetallic carbide Ni_(3)ZnC_(0.7) is a effective additive for the hydrogen storage performances modification of MgH_(2),and the facile synthesis of the Ni_(3)ZnC_(0.7)/Ni@CNT can provide directions of better designing high performance carbide catalysts for improving MgH_(2).