Immersion experiment results show that corrosion rate of the as deposited RE Ni W P SiC composite coating in HCl solutions increases with the rise of HCl concentration. On the contrary, the corrosion rate of the compo...Immersion experiment results show that corrosion rate of the as deposited RE Ni W P SiC composite coating in HCl solutions increases with the rise of HCl concentration. On the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing HCl concentration. The corrosion rates of the composite coatings in as deposited state and after heat treatment in H 2SO 4 and H 3PO 4 solutions respectively decrease with the rise of H 2SO 4 and H 3PO 4 concentrations. The corrosion rate of the composite coating as deposited in FeCl 3 solutions decreases with increasing FeCl 3 concentration, while the rate of the composite coating after heat treatment increases with the rise of FeCl 3 concentration. The corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions at different concentrations increases with rising concentration. In addition, the corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions respectively is much greater than that of the RE Ni W P SiC composite coating as deposited and after heat treatment in the same corrosion media. [展开更多
The φ pH diagram of Ni B H 2O system was drawn, and the mechanism of electrodepositing Ni B SiC composite coatings was discussed. The results show that the deposition of Ni and B occurs prior to that of H 2 because o...The φ pH diagram of Ni B H 2O system was drawn, and the mechanism of electrodepositing Ni B SiC composite coatings was discussed. The results show that the deposition of Ni and B occurs prior to that of H 2 because of the over potential of H 2 evolution on the Fe substrate. Boron can not singly deposit in aqueous solution. Nickel and boron can co deposit in the form of Ni 4B 3 without evolution of hydrogen when the cathodical potential is kept to be -1.415 ～ -1.700?V.展开更多
文摘Immersion experiment results show that corrosion rate of the as deposited RE Ni W P SiC composite coating in HCl solutions increases with the rise of HCl concentration. On the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing HCl concentration. The corrosion rates of the composite coatings in as deposited state and after heat treatment in H 2SO 4 and H 3PO 4 solutions respectively decrease with the rise of H 2SO 4 and H 3PO 4 concentrations. The corrosion rate of the composite coating as deposited in FeCl 3 solutions decreases with increasing FeCl 3 concentration, while the rate of the composite coating after heat treatment increases with the rise of FeCl 3 concentration. The corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions at different concentrations increases with rising concentration. In addition, the corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions respectively is much greater than that of the RE Ni W P SiC composite coating as deposited and after heat treatment in the same corrosion media. [
文摘The φ pH diagram of Ni B H 2O system was drawn, and the mechanism of electrodepositing Ni B SiC composite coatings was discussed. The results show that the deposition of Ni and B occurs prior to that of H 2 because of the over potential of H 2 evolution on the Fe substrate. Boron can not singly deposit in aqueous solution. Nickel and boron can co deposit in the form of Ni 4B 3 without evolution of hydrogen when the cathodical potential is kept to be -1.415 ～ -1.700?V.
