The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the...The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the coating oxidized in ambient air at 1000 °C for 25-250 h were investigated using SEM, X-ray diffraction and optical microscope methods. The results show that the copper with single phase Ni2Al3 coating possesses the best high temperature oxidation resistance, and the mass gain of the coating is 1/15 that of pure copper and 1/2 that of nickel coating, respectively. The specimen surface after being oxidized for 25 h still comprises Ni2Al3 phase. However, when the time of oxidizing treatment increases to 50 h, the Ni Al phase is formed. It is also found that the Ni2Al3 phase completely turns into Ni Al phase after oxidizing treatment for 100 h and above. The Ni Al coating shows excellent high temperature oxidation resistance when oxidation time is 250 h.展开更多
(Ni,Pd)AI coating, prepared by low pressure pack cementation on the Ni-base superalloy M38 where Pd-20 wt pct Ni alloy was predeposited, consists of a single β-(Ni,Pd)AI phase. The initial isothermal oxidation behavi...(Ni,Pd)AI coating, prepared by low pressure pack cementation on the Ni-base superalloy M38 where Pd-20 wt pct Ni alloy was predeposited, consists of a single β-(Ni,Pd)AI phase. The initial isothermal oxidation behavior of (Ni,Pd)AI coating was investigated by TGA, XRD, SEM/EDS at 800-1100℃. Results show that oxidation kinetics accord preferably with parabolic law at 800, 900 and 1100℃, but not at 1000℃. θ-AI203 was observed at 800-1100℃. It is found that Pd plays an important role in accelerating the diffusion of Ti from the substrate to the coating surface in the aluminide coating.展开更多
The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning elect...The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning electrical microscope (SEM), X-ray diffraction(XRD) and energy dispersive spectrum(EDS). The results showed that the corrosion of all composite coatings was accelerated under NaCl deposits, and the corrosion products were rather porous with poor adherence to the matrix. Al2O3 particles in the coatings can refine the grain size and improve the high temperature corrosion resistance of the coatings. Within the test scope, the more Al2O3 particles in the coatings, the lower corrosion rates could be obtained, and the corrosion mechanism was also discussed.展开更多
In the present investigation, Ni_（50）Ti_（25）Al_（25）（at.%） mechanically alloyed powder is deposited on carbon steel substrate.Before the coating process, the substrate is heated to temperature ranging from room...In the present investigation, Ni_（50）Ti_（25）Al_（25）（at.%） mechanically alloyed powder is deposited on carbon steel substrate.Before the coating process, the substrate is heated to temperature ranging from room temperature to 400℃. The microstructure, porosity, microhardness, adhesion strength, and corrosion behavior of the coating are investigated at different substrate temperatures. Results show that coating porosity is lower on high temperature surface. Microhardness and adhesion strength of the deposition layer on the substrate without preheating have lower values than with preheating. The polarization test result shows that corrosion performance of the coating is dependent on micro cracks and porosities and the increasing of substrate temperature can improve the quality of coating and corrosion performance.展开更多
Pure nickel and Ni/Ti3Si（AI）C2 composite coatings were prepared by electrodeposition method from an additive-free nickel Watt＇s bath and were characterized by X-ray diffraction, laser confocal microscopy and scanni...Pure nickel and Ni/Ti3Si（AI）C2 composite coatings were prepared by electrodeposition method from an additive-free nickel Watt＇s bath and were characterized by X-ray diffraction, laser confocal microscopy and scanning electron microscopy. The effect of current and Ti3Si（AI）C2 concentration in the solution on the composition, grain size, preferred orientation and surface morphology of the electrodeposited coatings were investigated. （200）-oriented Ni coatings could be deposited at high current （62.5 mA）, while （220）-oriented Ni coatings could be obtained at low current （25 mA）. However, the presence of Ti3Si（Al）C2 particles disturbed the surface texture of Ni crystallites in the composite coatings. Based on the simulated morphology and the observed microstructure, the mechanisms for the change of preferred orientation and crystallite shapes in the presence of Ti3Si（Al）C2 particles were discussed. Moreover, microhardness and friction properties of pure nickel and Ni/Ti3Si（Al）C2 composite coatings were also compared.展开更多
基金Projects(CKJB201205,QKJB201202,YJK201307)supported by the Nanjing Institute of Technology,China
文摘The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the coating oxidized in ambient air at 1000 °C for 25-250 h were investigated using SEM, X-ray diffraction and optical microscope methods. The results show that the copper with single phase Ni2Al3 coating possesses the best high temperature oxidation resistance, and the mass gain of the coating is 1/15 that of pure copper and 1/2 that of nickel coating, respectively. The specimen surface after being oxidized for 25 h still comprises Ni2Al3 phase. However, when the time of oxidizing treatment increases to 50 h, the Ni Al phase is formed. It is also found that the Ni2Al3 phase completely turns into Ni Al phase after oxidizing treatment for 100 h and above. The Ni Al coating shows excellent high temperature oxidation resistance when oxidation time is 250 h.
文摘(Ni,Pd)AI coating, prepared by low pressure pack cementation on the Ni-base superalloy M38 where Pd-20 wt pct Ni alloy was predeposited, consists of a single β-(Ni,Pd)AI phase. The initial isothermal oxidation behavior of (Ni,Pd)AI coating was investigated by TGA, XRD, SEM/EDS at 800-1100℃. Results show that oxidation kinetics accord preferably with parabolic law at 800, 900 and 1100℃, but not at 1000℃. θ-AI203 was observed at 800-1100℃. It is found that Pd plays an important role in accelerating the diffusion of Ti from the substrate to the coating surface in the aluminide coating.
文摘The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning electrical microscope (SEM), X-ray diffraction(XRD) and energy dispersive spectrum(EDS). The results showed that the corrosion of all composite coatings was accelerated under NaCl deposits, and the corrosion products were rather porous with poor adherence to the matrix. Al2O3 particles in the coatings can refine the grain size and improve the high temperature corrosion resistance of the coatings. Within the test scope, the more Al2O3 particles in the coatings, the lower corrosion rates could be obtained, and the corrosion mechanism was also discussed.
文摘In the present investigation, Ni_（50）Ti_（25）Al_（25）（at.%） mechanically alloyed powder is deposited on carbon steel substrate.Before the coating process, the substrate is heated to temperature ranging from room temperature to 400℃. The microstructure, porosity, microhardness, adhesion strength, and corrosion behavior of the coating are investigated at different substrate temperatures. Results show that coating porosity is lower on high temperature surface. Microhardness and adhesion strength of the deposition layer on the substrate without preheating have lower values than with preheating. The polarization test result shows that corrosion performance of the coating is dependent on micro cracks and porosities and the increasing of substrate temperature can improve the quality of coating and corrosion performance.
基金supported by the National Outstanding Young Scientist Foundation for Y. C. Zhou, Natural Sciences Foundation of China under Grant Nos. 50232040, 50302011, 90403027, 50772114 and 50832008
文摘Pure nickel and Ni/Ti3Si（AI）C2 composite coatings were prepared by electrodeposition method from an additive-free nickel Watt＇s bath and were characterized by X-ray diffraction, laser confocal microscopy and scanning electron microscopy. The effect of current and Ti3Si（AI）C2 concentration in the solution on the composition, grain size, preferred orientation and surface morphology of the electrodeposited coatings were investigated. （200）-oriented Ni coatings could be deposited at high current （62.5 mA）, while （220）-oriented Ni coatings could be obtained at low current （25 mA）. However, the presence of Ti3Si（Al）C2 particles disturbed the surface texture of Ni crystallites in the composite coatings. Based on the simulated morphology and the observed microstructure, the mechanisms for the change of preferred orientation and crystallite shapes in the presence of Ti3Si（Al）C2 particles were discussed. Moreover, microhardness and friction properties of pure nickel and Ni/Ti3Si（Al）C2 composite coatings were also compared.