A series of SBA-15 supported bimetallic Rh–Ni catalysts with different weight ratio of Rh/Ni in the range of 0–0.04 were prepared for carbon dioxide reforming of methane. The doping effect of Rh on catalytic activit...A series of SBA-15 supported bimetallic Rh–Ni catalysts with different weight ratio of Rh/Ni in the range of 0–0.04 were prepared for carbon dioxide reforming of methane. The doping effect of Rh on catalytic activity as well as carbon accumulation and removal over the catalysts was studied. The characterization results indicated that the addition of a small amount of Rh promoted the reducibility of Ni particles and decreased the Ni particle size. During the dry reforming reaction, the carbon deposition was originated from CH4 decomposition and CO disproportionation. The Rh–Ni catalyst with small metallic particle size inhibited the carbon formation and exhibited high efficiency in the removal of coke. In comparison with bare Ni-based catalyst, the Rh–Ni bimetallic catalysts showed high activity and stability in the dry reforming of methane.展开更多
A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, T...A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at at- mospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800 ℃ for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.展开更多
A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for pa...A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.展开更多
A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a c...A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor.The stability of the catalyst was tested at 800 ？C.The results indicated that 10wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas.Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6,GHSV = 24000 ml·gcat^-1·h^-1 and the reaction temperature T = 800 ℃,the conversions of CH4 and CO2 were 92.8% and 76.3%,respectively,and the yields of CO and H2 were 99.0% and 82.0%,respectively.The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.展开更多
A series of Ni/SBA-15 catalysts with Ni contents ranging from 5 wt% to 15 wt%, as well as another series of 10%Ni/MgO/SBA-15 catalysts, in which the range of the MgO content was from 1 wt% to 7 wt%, were prepared, and...A series of Ni/SBA-15 catalysts with Ni contents ranging from 5 wt% to 15 wt%, as well as another series of 10%Ni/MgO/SBA-15 catalysts, in which the range of the MgO content was from 1 wt% to 7 wt%, were prepared, and their catalytic performances for the reaction of combined steam and carbon dioxide reforming of methane were investigated in a continuous flow microreactor. The structures of the catalysts were characterized using the XRD, H2-TPR and CO2-TPD techniques. The results indicated that the CO selectivity for this reaction was very close to 100%, and the H2/CO ratio of the product gas could be controlled by changing the H2O/CO2 molar ratio of the feed gas. The simultaneous and plentiful existing of steam and CO2 had a significant influence on the catalytic performance of the 10%Ni/SBA-15 catalyst without modification. After reacting at 850 °C for 120 h over this catalyst, the CH4 conversion dropped from 98% to 85%, and the CO2 conversion decreased from 86% to 53%. However, the 10%Ni/3%MgO/SBA-15 catalyst exhibited a much better catalytic performance, and after reacting for 620 h, the CO2 conversion over this catalyst dropped from 92% to around 77%, while the CH4 conversion was not decreased. Oxidation of the Ni0 species as well as carbon deposition during the reaction were the main reasons for the deactivation of the catalyst without modification. On the other hand, modification by the MgO promoter improved the dispersion of the Ni0 species, and enhanced the CO2 adsorption affinity which in turn depressed the occurring of carbon deposition, and thus retarded the deactivation process.展开更多
基金Supported by the National Natural Science Foundation of China(U1361125,U1261208,21176001,51174254)the Provincial Innovative Group for Processing&Clean Utilization of Coal Resourcethe Innovative Research Team of Anhui University of Technology
基金supported by the National Natural Science Foundation of China(21173050,21371035)
文摘A series of SBA-15 supported bimetallic Rh–Ni catalysts with different weight ratio of Rh/Ni in the range of 0–0.04 were prepared for carbon dioxide reforming of methane. The doping effect of Rh on catalytic activity as well as carbon accumulation and removal over the catalysts was studied. The characterization results indicated that the addition of a small amount of Rh promoted the reducibility of Ni particles and decreased the Ni particle size. During the dry reforming reaction, the carbon deposition was originated from CH4 decomposition and CO disproportionation. The Rh–Ni catalyst with small metallic particle size inhibited the carbon formation and exhibited high efficiency in the removal of coke. In comparison with bare Ni-based catalyst, the Rh–Ni bimetallic catalysts showed high activity and stability in the dry reforming of methane.
基金Financial funds from the Chinese Natural Science Foundation(Project No.20473009)the Beijing Natural Science Foundation(Project No.8062023)+1 种基金the National Basic Research Program of China(Project No.2005CB221405)the National"863"Project of China(No.2006 AA10Z425)are gratefully acknowledged.
文摘A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at at- mospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800 ℃ for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.
基金supported by the National Basic Research Program of China (Project No. 2005CB221405)the National "863" Project of China (No.2006AA10Z425)
文摘A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.
基金supported by the National Basic Research Program of China(Project No.2005CB221405)the National "863" Project of China (No.2006AA10Z425)the Beijing Natural Science Foundation (Project No: 8062023)
文摘A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor.The stability of the catalyst was tested at 800 ？C.The results indicated that 10wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas.Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6,GHSV = 24000 ml·gcat^-1·h^-1 and the reaction temperature T = 800 ℃,the conversions of CH4 and CO2 were 92.8% and 76.3%,respectively,and the yields of CO and H2 were 99.0% and 82.0%,respectively.The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.
基金the National Basic Research Program ofChina (Project No. 2005CB221405)the National "863" Project ofChina (No. 2006AA10Z425)the Beijing Natural Science Foun-dation (Project No: 8062023)
文摘A series of Ni/SBA-15 catalysts with Ni contents ranging from 5 wt% to 15 wt%, as well as another series of 10%Ni/MgO/SBA-15 catalysts, in which the range of the MgO content was from 1 wt% to 7 wt%, were prepared, and their catalytic performances for the reaction of combined steam and carbon dioxide reforming of methane were investigated in a continuous flow microreactor. The structures of the catalysts were characterized using the XRD, H2-TPR and CO2-TPD techniques. The results indicated that the CO selectivity for this reaction was very close to 100%, and the H2/CO ratio of the product gas could be controlled by changing the H2O/CO2 molar ratio of the feed gas. The simultaneous and plentiful existing of steam and CO2 had a significant influence on the catalytic performance of the 10%Ni/SBA-15 catalyst without modification. After reacting at 850 °C for 120 h over this catalyst, the CH4 conversion dropped from 98% to 85%, and the CO2 conversion decreased from 86% to 53%. However, the 10%Ni/3%MgO/SBA-15 catalyst exhibited a much better catalytic performance, and after reacting for 620 h, the CO2 conversion over this catalyst dropped from 92% to around 77%, while the CH4 conversion was not decreased. Oxidation of the Ni0 species as well as carbon deposition during the reaction were the main reasons for the deactivation of the catalyst without modification. On the other hand, modification by the MgO promoter improved the dispersion of the Ni0 species, and enhanced the CO2 adsorption affinity which in turn depressed the occurring of carbon deposition, and thus retarded the deactivation process.