The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an en...The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy dispersive analytical X ray system(SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 ℃ spalled severely during cooling, while after the stainless steel was coated with the Ni La 2O 3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La 2O 3 modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni La 2O 3 composite film.展开更多
Mn/Ni composite oxides as active electrode materials for supercapacitors were prepared by solid-state reaction through the reduction of KMnO4 with manganese acetate and nickel acetate at low temperature. The products ...Mn/Ni composite oxides as active electrode materials for supercapacitors were prepared by solid-state reaction through the reduction of KMnO4 with manganese acetate and nickel acetate at low temperature. The products were characterized by X-ray diffractometry(XRD) and transmission electron microscopy(TEM). The electrochemical characterizations were performed by cyclic voltammetry (CV) and constant current charge-discharge in a three-electrode system. The effects of different potential windows, scan rates, and cycle numbers on the capacitance behavior of Mn0.8Ni0.2Ox composite oxide were also investigated. The results show that the composite oxides are of nano-size and amorphous structure. With increasing the molar ratio of Ni, the specific capacitance goes through a maximum at molar fraction of Ni of 20%. The specific capacitance of Mn0.8Ni0.2Ox composite oxide is 194.5 F/g at constant current discharge of 5 mA.展开更多
文摘The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy dispersive analytical X ray system(SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 ℃ spalled severely during cooling, while after the stainless steel was coated with the Ni La 2O 3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La 2O 3 modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni La 2O 3 composite film.
基金Project(20060390889) supported by China Postdoctoral Science FoundationProject (2006FJ4236) supported by Hunan Postdoctoral Scientific Program
文摘Mn/Ni composite oxides as active electrode materials for supercapacitors were prepared by solid-state reaction through the reduction of KMnO4 with manganese acetate and nickel acetate at low temperature. The products were characterized by X-ray diffractometry(XRD) and transmission electron microscopy(TEM). The electrochemical characterizations were performed by cyclic voltammetry (CV) and constant current charge-discharge in a three-electrode system. The effects of different potential windows, scan rates, and cycle numbers on the capacitance behavior of Mn0.8Ni0.2Ox composite oxide were also investigated. The results show that the composite oxides are of nano-size and amorphous structure. With increasing the molar ratio of Ni, the specific capacitance goes through a maximum at molar fraction of Ni of 20%. The specific capacitance of Mn0.8Ni0.2Ox composite oxide is 194.5 F/g at constant current discharge of 5 mA.