Magnesium and magnesium alloy foils have great potential for application in battery anodes,electromagnetic shielding,optics and acoustics,and biology because of their excellent specific damping,internal dissipation co...Magnesium and magnesium alloy foils have great potential for application in battery anodes,electromagnetic shielding,optics and acoustics,and biology because of their excellent specific damping,internal dissipation coefficients,magnetic and electrical conductivities,as well as high theoretical specific capacity.However,magnesium alloys exhibit poor deformation ability due to their hexagonal close-packed crystal structure.Preparing magnesium and magnesium alloy foils with thicknesses of less than 0.1 mm is difficult because of surface oxidation and grain growth at high temperatures or severe anisotropy after cold rolling that leads to cracks.Numerous methods have been applied to prepare magnesium alloy foils.They include warm rolling,cold rolling,accumulative roll bonding,electric plastic rolling,and on-line heating rolling.Defects of magnesium and magnesium alloy foils during preparation,such as edge cracks and breakage,are important factors for consideration.Herein,the current status of the research on magnesium and magnesium alloy foils is summarized from the aspects of foil preparation,defect control,performance characterization,and application prospects.The advantages and disadvantages of different preparation methods and defect(edge cracks and breakage)mechanisms in the preparation of foils are identified.展开更多
In order to expand the application of the electrodeposited Ni-Fe alloy foil,their mechanical and magnetic properties were studied after heat treatment.The development of grain growth during annealing was in-situ onlin...In order to expand the application of the electrodeposited Ni-Fe alloy foil,their mechanical and magnetic properties were studied after heat treatment.The development of grain growth during annealing was in-situ online investigated using a heating stage microscope,and the texture was analyzed via X-ray diffraction（XRD）and electron back-scattered diffraction（EBSD）.The results indicated that abnormal grain growth usually occurred during annealing at 1000-1050°C.The{111}oriented grains preferentially grew as the annealing temperature and holding time increased.The plasticities of the electrodeposited Ni-Fe alloy foils after heat treatment were better than those of the original samples.The excellent ductility was obtained without a loss in magnetic properties after annealing at 1100°C for 6h.展开更多
Ni-Fe alloy was electrodeposited on the surface of polyacrylonitrile （PAN）-based carbon fibers, and catalytic graphitization effect of the heat-treated carbon fibers was investigated by X-ray diffractometry and Rama...Ni-Fe alloy was electrodeposited on the surface of polyacrylonitrile （PAN）-based carbon fibers, and catalytic graphitization effect of the heat-treated carbon fibers was investigated by X-ray diffractometry and Raman spectra. It is found that Ni-Fe alloy exhibits significant catalytic effect on the graphitization of the carbon fibers at low temperatures. The degree of graphitization of the carbon fibers coated with Ni-Fe alloy （57.91% Fe, mass fraction） reaches 69.0% through heat treatment at 1 250 °C. However, the degree of graphitization of the carbon fibers without Ni-Fe alloy is only 30.1% after being heat-treated at 2 800 °C. The catalytic effect of Ni-Fe alloy on graphitization of carbon fibers is better than that of Ni or Fe at the same temperature, indicating that Ni and Fe elements have synergic catalytic function. Furthermore, Fe content in the Ni-Fe alloy also influences catalytic effect. The catalytic graphitization of Ni-Fe alloy follows the dissolution-precipitation mechanism.展开更多
Nanocrystalline Ni-Fe FCC alloy coatings with Fe content of 1.3%-39%（mass fraction） were fabricated on the nickel substrates using a DC electrodeposition technique. The crystal structure, lattice strain, grain size ...Nanocrystalline Ni-Fe FCC alloy coatings with Fe content of 1.3%-39%（mass fraction） were fabricated on the nickel substrates using a DC electrodeposition technique. The crystal structure, lattice strain, grain size and lattice constant of the Ni-Fe alloy coatings were studied by X-ray diffraction technique. The chemical composition and surface morphology of the FCC Ni-Fe alloy coatings were investigated with the energy dispersive X-ray spectroscopy（EDS） and atomic force microscopy（AFM）. The results show that the Fe content of the Ni-Fe alloy coatings has a great influence on the preferred orientation, grain size, lattice constant and lattice strain. FCC Ni-Fe alloy coatings exhibit preferred orientations of（200） or（200）（111）. With an increase of Fe content, the preferred growth orientation of（200） plane is weakened gradually, while the preferred growth orientation of（111） increases. An increase of the Fe content in the range of 1.3%-25%（mass fraction） results in a significant grain refinement of the coatings. Increasing the Fe content beyond 25% does not decrease the grain size of FCC Ni-Fe alloys further. The lattice strain increases with increasing the Fe content in the FCC Ni-Fe alloys. Since the alloys with Fe content not less than 25% has similar grain size（~11 nm）, the increase in the lattice strain with the increase of Fe content cannot be attributed to the change in the grain size.展开更多
The ductility loss and threshold stress intensity,K_(IH)during hydrogen charging were measured for pure Ni and four Ni-Fe fcc alloys.The results show that ductility loss in 40Ni60Fe alloy and K_(IH)a 50Ni50Fe alloy ha...The ductility loss and threshold stress intensity,K_(IH)during hydrogen charging were measured for pure Ni and four Ni-Fe fcc alloys.The results show that ductility loss in 40Ni60Fe alloy and K_(IH)a 50Ni50Fe alloy have a minimum value.The variations of the amounts of hydride, hydrogen evolution and dislocation structure with composition have been investigated.The va- riation of hydrogen embrittlement susceptibility with composition measured by ductility loss and by K_(IH)or K_(IH)/K_C can be explained by means of the synthetical effects of amount of hydride,solutionized hydrogen and the extent of dislocation planarity on hydrogen embrittlement susceptibility.展开更多
The connection characteristics of rapidly solidified Cu-40%Co alloy foils were studied using a self-developed micro-type energy-storage welding machine. The results show that the microstructure of the alloy foils is c...The connection characteristics of rapidly solidified Cu-40%Co alloy foils were studied using a self-developed micro-type energy-storage welding machine. The results show that the microstructure of the alloy foils is characterized by uni form and fine equiaxed grains,whose maximum grain size is 1.8 μm. Under the o ptimum energy,the regular flat nugget is formed,low voltage and high capacitan ce are favorable for obtaining the perfect connection joints,whereas high volta ge and low capacitance are likely to result in the surface burn of the alloy foi ls. With the increase of welding energy,the spot welding joint will be transfor med from regular flat nugget to nugget-free one,and the microstructure tends t o coarsen. The welding parameters recommended are: welding voltage 80100 V,(electric) capacitance 1 8002 500 μF,and welding force 48 N.展开更多
Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride- sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulp...Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride- sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulphate and saccharin concentration on composition and current efficiency were investigated in detail. The morphology and the microstructure of deposits were analyzed by SEM and XRD, respectively. The results indicated that the optimum parameters were current density 3-4 A/dm2, pH 2-3, temperature 40-50?C, cobalt sulphate 20 g/l and saccharin 2-3 g/l. Chemical analysis of the deposits by EDS revealed anomalous Ni-Co codeposition occured in this system. The SEM showed that hydroxide particles were not present on the surface and that fine-grain, smooth and compact Ni-Co alloy deposits were obtained. The crystallographic structures of Ni-Co alloy foils were the fcc Ni solid solution. The Ni-Co alloy foils with Co content 17.3-37.2 wt% and thickness of 20-45 μm were bright with low residual stress and super toughness.展开更多
An alternative to conventional process for the preparation of soft magnetic metal foils of Fe,Fe-Ni,Fe-Co and Fe-Ni-Co by electroforming was described.The microstructure and magnetic properties were observed.The resul...An alternative to conventional process for the preparation of soft magnetic metal foils of Fe,Fe-Ni,Fe-Co and Fe-Ni-Co by electroforming was described.The microstructure and magnetic properties were observed.The results showed that the crystal size of the iron-based alloy foil is less than 10μm,while that of nickel-based alloy foil is about 2μm.Moreover,the electroformed Fe-Ni foil has better magnetic properties than the conventional milled permalloy 1J79 foil.展开更多
Scanning electron microscopy and X-ray energy dispersive spectrum analysis show that the clusters of intermetallic AlFeSi particle are distributed on or near the aluminum foil stock surfaces heterogeneously. 3D finite...Scanning electron microscopy and X-ray energy dispersive spectrum analysis show that the clusters of intermetallic AlFeSi particle are distributed on or near the aluminum foil stock surfaces heterogeneously. 3D finite element modeling shows that these clusters of hard particles induce the fracture of the nano-scale lubricant oil film at first and further lead to severe deformation in the nearby aluminum foil substrate along the rolling direction. Consequently, the optical property in this region differs from that in the surroundings, resulting in surface defects.展开更多
The superplasticity and diffusion bonding of IN718 superalloy were studied in this article. The strain rate sensitivity index m was obtained at different temperatures and various initial strain rates using the tensile...The superplasticity and diffusion bonding of IN718 superalloy were studied in this article. The strain rate sensitivity index m was obtained at different temperatures and various initial strain rates using the tensile speed mutation method; m reached its maximum value 0.53 at an initial strain rate of 1×10^-4s^-1 at 1253K. The diffusion bonding parameters, including the bonding temperature T, pressure p, and time t, affected the mechanism of joints. When the bonded specimen with 25μm thick nickel foil interlayer was tensile at room temperature, the shear fracture of the joints with nickel foil interlayer took place at the IN718 part. Microstructure study was carried out with the bonded samples. The microstructure shows an excellent bonding at the interfaces. The optimum parameters for the diffusion bonding are： T = 1273-1323K, p = 20-30MPa, t = 45-60min.展开更多
基金financially supported by the National Key Research and Development Program of China(Nos.2022 YFB3709300 and 2021YFB3701000)the National Natural Science Foundation of China(Nos.52271090 and 52071036)+1 种基金the Guangdong Major Project of Basic and Applied Basic Research(No.2020B0301030006)the Independent Research Project of State Key Laboratory of Mechanical Transmissions(Nos.SKLMT-ZZKT-2022Z01 and S KLMT-ZZKT-2022M12)。
文摘Magnesium and magnesium alloy foils have great potential for application in battery anodes,electromagnetic shielding,optics and acoustics,and biology because of their excellent specific damping,internal dissipation coefficients,magnetic and electrical conductivities,as well as high theoretical specific capacity.However,magnesium alloys exhibit poor deformation ability due to their hexagonal close-packed crystal structure.Preparing magnesium and magnesium alloy foils with thicknesses of less than 0.1 mm is difficult because of surface oxidation and grain growth at high temperatures or severe anisotropy after cold rolling that leads to cracks.Numerous methods have been applied to prepare magnesium alloy foils.They include warm rolling,cold rolling,accumulative roll bonding,electric plastic rolling,and on-line heating rolling.Defects of magnesium and magnesium alloy foils during preparation,such as edge cracks and breakage,are important factors for consideration.Herein,the current status of the research on magnesium and magnesium alloy foils is summarized from the aspects of foil preparation,defect control,performance characterization,and application prospects.The advantages and disadvantages of different preparation methods and defect(edge cracks and breakage)mechanisms in the preparation of foils are identified.
基金funded by National Natural Science Foundation of China(51234001)
文摘In order to expand the application of the electrodeposited Ni-Fe alloy foil,their mechanical and magnetic properties were studied after heat treatment.The development of grain growth during annealing was in-situ online investigated using a heating stage microscope,and the texture was analyzed via X-ray diffraction（XRD）and electron back-scattered diffraction（EBSD）.The results indicated that abnormal grain growth usually occurred during annealing at 1000-1050°C.The{111}oriented grains preferentially grew as the annealing temperature and holding time increased.The plasticities of the electrodeposited Ni-Fe alloy foils after heat treatment were better than those of the original samples.The excellent ductility was obtained without a loss in magnetic properties after annealing at 1100°C for 6h.
基金Project (2006CB600903) supported by the National Basic Research Program of ChinaProject (2010GK3208) supported by Science and Technology Program of Hunan Province, China
文摘Ni-Fe alloy was electrodeposited on the surface of polyacrylonitrile （PAN）-based carbon fibers, and catalytic graphitization effect of the heat-treated carbon fibers was investigated by X-ray diffractometry and Raman spectra. It is found that Ni-Fe alloy exhibits significant catalytic effect on the graphitization of the carbon fibers at low temperatures. The degree of graphitization of the carbon fibers coated with Ni-Fe alloy （57.91% Fe, mass fraction） reaches 69.0% through heat treatment at 1 250 °C. However, the degree of graphitization of the carbon fibers without Ni-Fe alloy is only 30.1% after being heat-treated at 2 800 °C. The catalytic effect of Ni-Fe alloy on graphitization of carbon fibers is better than that of Ni or Fe at the same temperature, indicating that Ni and Fe elements have synergic catalytic function. Furthermore, Fe content in the Ni-Fe alloy also influences catalytic effect. The catalytic graphitization of Ni-Fe alloy follows the dissolution-precipitation mechanism.
基金Project(51021063)supported by the National Natural Science Fund for Innovation Group of ChinaProject(2012M521540)supported by China Post Doctoral Science Foundation+1 种基金Project(2013RS4027)supported by the Post Doctoral Scientific Foundation of Hunan Province,ChinaProject(CSUZC2013023)supported by the Precious Apparatus Open Share Foundation of Central South University,China
文摘Nanocrystalline Ni-Fe FCC alloy coatings with Fe content of 1.3%-39%（mass fraction） were fabricated on the nickel substrates using a DC electrodeposition technique. The crystal structure, lattice strain, grain size and lattice constant of the Ni-Fe alloy coatings were studied by X-ray diffraction technique. The chemical composition and surface morphology of the FCC Ni-Fe alloy coatings were investigated with the energy dispersive X-ray spectroscopy（EDS） and atomic force microscopy（AFM）. The results show that the Fe content of the Ni-Fe alloy coatings has a great influence on the preferred orientation, grain size, lattice constant and lattice strain. FCC Ni-Fe alloy coatings exhibit preferred orientations of（200） or（200）（111）. With an increase of Fe content, the preferred growth orientation of（200） plane is weakened gradually, while the preferred growth orientation of（111） increases. An increase of the Fe content in the range of 1.3%-25%（mass fraction） results in a significant grain refinement of the coatings. Increasing the Fe content beyond 25% does not decrease the grain size of FCC Ni-Fe alloys further. The lattice strain increases with increasing the Fe content in the FCC Ni-Fe alloys. Since the alloys with Fe content not less than 25% has similar grain size（~11 nm）, the increase in the lattice strain with the increase of Fe content cannot be attributed to the change in the grain size.
文摘The ductility loss and threshold stress intensity,K_(IH)during hydrogen charging were measured for pure Ni and four Ni-Fe fcc alloys.The results show that ductility loss in 40Ni60Fe alloy and K_(IH)a 50Ni50Fe alloy have a minimum value.The variations of the amounts of hydride, hydrogen evolution and dislocation structure with composition have been investigated.The va- riation of hydrogen embrittlement susceptibility with composition measured by ductility loss and by K_(IH)or K_(IH)/K_C can be explained by means of the synthetical effects of amount of hydride,solutionized hydrogen and the extent of dislocation planarity on hydrogen embrittlement susceptibility.
文摘The connection characteristics of rapidly solidified Cu-40%Co alloy foils were studied using a self-developed micro-type energy-storage welding machine. The results show that the microstructure of the alloy foils is characterized by uni form and fine equiaxed grains,whose maximum grain size is 1.8 μm. Under the o ptimum energy,the regular flat nugget is formed,low voltage and high capacitan ce are favorable for obtaining the perfect connection joints,whereas high volta ge and low capacitance are likely to result in the surface burn of the alloy foi ls. With the increase of welding energy,the spot welding joint will be transfor med from regular flat nugget to nugget-free one,and the microstructure tends t o coarsen. The welding parameters recommended are: welding voltage 80100 V,(electric) capacitance 1 8002 500 μF,and welding force 48 N.
文摘Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride- sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulphate and saccharin concentration on composition and current efficiency were investigated in detail. The morphology and the microstructure of deposits were analyzed by SEM and XRD, respectively. The results indicated that the optimum parameters were current density 3-4 A/dm2, pH 2-3, temperature 40-50?C, cobalt sulphate 20 g/l and saccharin 2-3 g/l. Chemical analysis of the deposits by EDS revealed anomalous Ni-Co codeposition occured in this system. The SEM showed that hydroxide particles were not present on the surface and that fine-grain, smooth and compact Ni-Co alloy deposits were obtained. The crystallographic structures of Ni-Co alloy foils were the fcc Ni solid solution. The Ni-Co alloy foils with Co content 17.3-37.2 wt% and thickness of 20-45 μm were bright with low residual stress and super toughness.
基金Sponsored by National Science Foundation for Distinguished Young Scholars of China(50225415)
文摘An alternative to conventional process for the preparation of soft magnetic metal foils of Fe,Fe-Ni,Fe-Co and Fe-Ni-Co by electroforming was described.The microstructure and magnetic properties were observed.The results showed that the crystal size of the iron-based alloy foil is less than 10μm,while that of nickel-based alloy foil is about 2μm.Moreover,the electroformed Fe-Ni foil has better magnetic properties than the conventional milled permalloy 1J79 foil.
基金Project(51074117)supported by the National Natural Science Foundation of ChinaProject(2009CDA044)supported by the Foundation for Distinguished Young Scientists of Hubei Province,ChinaProjects(201104493,20100471161)supported by the China Postdoctoral Science Foundation
文摘Scanning electron microscopy and X-ray energy dispersive spectrum analysis show that the clusters of intermetallic AlFeSi particle are distributed on or near the aluminum foil stock surfaces heterogeneously. 3D finite element modeling shows that these clusters of hard particles induce the fracture of the nano-scale lubricant oil film at first and further lead to severe deformation in the nearby aluminum foil substrate along the rolling direction. Consequently, the optical property in this region differs from that in the surroundings, resulting in surface defects.
文摘The superplasticity and diffusion bonding of IN718 superalloy were studied in this article. The strain rate sensitivity index m was obtained at different temperatures and various initial strain rates using the tensile speed mutation method; m reached its maximum value 0.53 at an initial strain rate of 1×10^-4s^-1 at 1253K. The diffusion bonding parameters, including the bonding temperature T, pressure p, and time t, affected the mechanism of joints. When the bonded specimen with 25μm thick nickel foil interlayer was tensile at room temperature, the shear fracture of the joints with nickel foil interlayer took place at the IN718 part. Microstructure study was carried out with the bonded samples. The microstructure shows an excellent bonding at the interfaces. The optimum parameters for the diffusion bonding are： T = 1273-1323K, p = 20-30MPa, t = 45-60min.