In-situ synthesized ceramic such as TiC,Cr7C3 and Cr5B3 reinforced Ni-based alloy composite coating was fabricated on the surface of mild steel substrate by reactive braze coating processing with colloidal graphite,Cr...In-situ synthesized ceramic such as TiC,Cr7C3 and Cr5B3 reinforced Ni-based alloy composite coating was fabricated on the surface of mild steel substrate by reactive braze coating processing with colloidal graphite,Cr,Ni,ferro-boron,Si and titanium powders as the raw materials at low temperature of 1000℃,and a new kind of coating materials was developed.By means of SEM,EDS,XRD and surface hardness tester,the microstructures,phases,hardness and wear-resistance of the coating were analyzed,respectively.The results revealed that the coating was mainly composed of the ceramic in-situ synthesized reinforcement phases of TiC,Cr7C3 and Cr5B3 and the binder phases in-situ synthesized of Ni31Si12 and(Ni,Fe)solid solution;The ceramic reinforcement phases of TiC,Cr7C3 and Cr5B3 were randomly distributed in the binder phases of Ni31Si12 and(Ni,Fe)solid solution;The coating had about 15vol%pores and can possibly be applied as a self-lubrication coating;The coating and the substrate were integrated together by metallurgical bonding;The coating had a hardness up to 91-94HR15N.展开更多
The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstruct...The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstructure and morphology of VFS coatings were observed and analyzed by SEM, X-ray diffractometer and microhardness tester. Diffusion coefficient of every element was calculated by using the experimental results. The influence of the interracial diffusion on the microstructure, Vickers hardness and interracial bond strength of the VFS coatings was studied in detail. The experimental results show that there is a metallurgical bond area between the VFS WC-Co coatings and the steel substrate. The VFS coatings are characterized by the gradient hardness of the interface and the high bond strength to the steel substate, both of which are beneficial to the improvement of the wear resistance and corrosion resistance.展开更多
A Ni-Cr-B-Si coating technique was developed and successfully applied on austenite grey iron substrate in a conventional resistance furnace under graphite powder protection. The microstructure, phase distribution, che...A Ni-Cr-B-Si coating technique was developed and successfully applied on austenite grey iron substrate in a conventional resistance furnace under graphite powder protection. The microstructure, phase distribution, chemical composition profile and microhardness along the coating layer depth were investigated. Shear strength of the coating was also tested. Microanalysis shows that the coating is consist of γ-Ni solution and γ-Ni+Ni3B lamellar eutectic, as well as small amount of Cr5B3 particles. Diffusion induced metallurgical bonding occurs at the coating/substrate interfaces, and the higher the temperature, the more sufficient elements diffused, the broader interfusion region and the larger bonding strength, but it has an optimum value. And the bonding strength at the interface can be enable to reach 250-270 MPa, which is nearly the same as that of processed by flame spray. The microhardness along the coating layer depth shows a gradient distribution manner.展开更多
The ultrafine WC-Co composite powder was synthesized by a newly developed rapid route based on in situ reactions. By using the as-synthesized composite powder, the granulation processing was then carried out to prepar...The ultrafine WC-Co composite powder was synthesized by a newly developed rapid route based on in situ reactions. By using the as-synthesized composite powder, the granulation processing was then carried out to prepare the ultrafine-structured thermal spraying feedstock. The influences of the heat-treatment process on density of the feedstock powder, phase constitution and wear resistance of the resultant WC-Co coatings fabricated by high velocity oxy-fuel （HVOF） were investigated. The results showed that increasing the heating temperature and extending the holding time leaded to remarkable increase in the density and flowability of the feedstock powder. As a result, the decarburization of the in-flight particles could be decreased and the wear resistance of coating was significantly enhanced. The present study demonstrated that the developed techniques for the ultrafine powder and its thermal-sprayed coatings had very promising applications in scaling up to produce ultrafine-structured cermet coatings with excellent performance.展开更多
基金supported by Yangjiang science and technology project (0202010067)Yangjiang polytechnic for providing financial assistance.
文摘In-situ synthesized ceramic such as TiC,Cr7C3 and Cr5B3 reinforced Ni-based alloy composite coating was fabricated on the surface of mild steel substrate by reactive braze coating processing with colloidal graphite,Cr,Ni,ferro-boron,Si and titanium powders as the raw materials at low temperature of 1000℃,and a new kind of coating materials was developed.By means of SEM,EDS,XRD and surface hardness tester,the microstructures,phases,hardness and wear-resistance of the coating were analyzed,respectively.The results revealed that the coating was mainly composed of the ceramic in-situ synthesized reinforcement phases of TiC,Cr7C3 and Cr5B3 and the binder phases in-situ synthesized of Ni31Si12 and(Ni,Fe)solid solution;The ceramic reinforcement phases of TiC,Cr7C3 and Cr5B3 were randomly distributed in the binder phases of Ni31Si12 and(Ni,Fe)solid solution;The coating had about 15vol%pores and can possibly be applied as a self-lubrication coating;The coating and the substrate were integrated together by metallurgical bonding;The coating had a hardness up to 91-94HR15N.
文摘The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstructure and morphology of VFS coatings were observed and analyzed by SEM, X-ray diffractometer and microhardness tester. Diffusion coefficient of every element was calculated by using the experimental results. The influence of the interracial diffusion on the microstructure, Vickers hardness and interracial bond strength of the VFS coatings was studied in detail. The experimental results show that there is a metallurgical bond area between the VFS WC-Co coatings and the steel substrate. The VFS coatings are characterized by the gradient hardness of the interface and the high bond strength to the steel substate, both of which are beneficial to the improvement of the wear resistance and corrosion resistance.
基金The paper is supported by country-level Spark Plan in 2003,project No.: 2003EA690034.
文摘A Ni-Cr-B-Si coating technique was developed and successfully applied on austenite grey iron substrate in a conventional resistance furnace under graphite powder protection. The microstructure, phase distribution, chemical composition profile and microhardness along the coating layer depth were investigated. Shear strength of the coating was also tested. Microanalysis shows that the coating is consist of γ-Ni solution and γ-Ni+Ni3B lamellar eutectic, as well as small amount of Cr5B3 particles. Diffusion induced metallurgical bonding occurs at the coating/substrate interfaces, and the higher the temperature, the more sufficient elements diffused, the broader interfusion region and the larger bonding strength, but it has an optimum value. And the bonding strength at the interface can be enable to reach 250-270 MPa, which is nearly the same as that of processed by flame spray. The microhardness along the coating layer depth shows a gradient distribution manner.
基金supported by the National Natural Science Foundation of China(No.51174009)the Beijing Key Program of Natural Science Foundation(No.2131001)+1 种基金the National Key Program for Fundamental Research and Development(No.2011CB612207)the National High-tech R&D Program of China(No.SS2013AA031401)
文摘The ultrafine WC-Co composite powder was synthesized by a newly developed rapid route based on in situ reactions. By using the as-synthesized composite powder, the granulation processing was then carried out to prepare the ultrafine-structured thermal spraying feedstock. The influences of the heat-treatment process on density of the feedstock powder, phase constitution and wear resistance of the resultant WC-Co coatings fabricated by high velocity oxy-fuel （HVOF） were investigated. The results showed that increasing the heating temperature and extending the holding time leaded to remarkable increase in the density and flowability of the feedstock powder. As a result, the decarburization of the in-flight particles could be decreased and the wear resistance of coating was significantly enhanced. The present study demonstrated that the developed techniques for the ultrafine powder and its thermal-sprayed coatings had very promising applications in scaling up to produce ultrafine-structured cermet coatings with excellent performance.