Fatigue behaviors of a biocompatible Ni-free Zr60.14Cu22.31Fe4.85Al9.7Ag3 Zr-based bulk metallic glass （BMG） have been studied under three-point-bending test in a simulated body fluid （SBF） at 37 ℃ and compared w...Fatigue behaviors of a biocompatible Ni-free Zr60.14Cu22.31Fe4.85Al9.7Ag3 Zr-based bulk metallic glass （BMG） have been studied under three-point-bending test in a simulated body fluid （SBF） at 37 ℃ and compared with those in air at room temperature （RT）. The BMG shows a high fatigue limit of approximately 366 MPa in SBF, which was slightly lower than that in air （400 MPa）. The fatigue cracks tended to initiate from the defects such as cast-pores, inclusions and corners of the samples and propagate in a similar path in SBF and in air. Three distinct regions, i.e. a crack-initiation region, a stable crack-growth region and an unstable fast-fracture region were clearly observed on the fatigue-fractured surface. Although pitting occurred at the defects where crack initiated, it does not affect significantly the fatigue life of the BMG, because the lifetime in the present BMG is mainly determined by crack propagation. The high corrosion-fatigue limit of the studied BMG results from its excellent corrosion resistance in SBF and intrinsically good toughness.展开更多
Hot compression test of a novel nickel-free white alloy Cu?12Mn?15Zn?1.5Al?0.3Ti?0.14B?0.1Ce (mass fraction, %) was conducted on a Gleeble?1500 machine in the temperature range of 600?800 °C and the strain rate r...Hot compression test of a novel nickel-free white alloy Cu?12Mn?15Zn?1.5Al?0.3Ti?0.14B?0.1Ce (mass fraction, %) was conducted on a Gleeble?1500 machine in the temperature range of 600?800 °C and the strain rate range of 0.01?10 s?1. The constitutive equation and hot processing map of the alloy were built up according to its hot deformation behavior and hot working characteristics. The deformation activation energy of the alloy is 203.005 kJ/mol. An instability region appears in the hot deformation temperature of 600?700 °C and the strain rate range of 0.32?10 s?1 when the true strain of the alloy is up to 0.7. Under the optimal hot deformation condition of 800 °C and 10 s?1 the prepared specimen has good surface quality and interior structure. The designed nickel-free alloy has very similar white chromaticity with the traditional white copper alloy (Cu?15Ni?24Zn?1.5Pb), and the color difference between them is less than 1.5, which can hardly be distinguished by human eyes.展开更多
基金financially supported by the National Nature Science Foundation of China (Grant Nos. 51071072 and 51271081)
文摘Fatigue behaviors of a biocompatible Ni-free Zr60.14Cu22.31Fe4.85Al9.7Ag3 Zr-based bulk metallic glass （BMG） have been studied under three-point-bending test in a simulated body fluid （SBF） at 37 ℃ and compared with those in air at room temperature （RT）. The BMG shows a high fatigue limit of approximately 366 MPa in SBF, which was slightly lower than that in air （400 MPa）. The fatigue cracks tended to initiate from the defects such as cast-pores, inclusions and corners of the samples and propagate in a similar path in SBF and in air. Three distinct regions, i.e. a crack-initiation region, a stable crack-growth region and an unstable fast-fracture region were clearly observed on the fatigue-fractured surface. Although pitting occurred at the defects where crack initiated, it does not affect significantly the fatigue life of the BMG, because the lifetime in the present BMG is mainly determined by crack propagation. The high corrosion-fatigue limit of the studied BMG results from its excellent corrosion resistance in SBF and intrinsically good toughness.
基金Project(51271203)supported by the National Natural Science Foundation of ChinaProject(CX2012B037)supported by the Hunan Provincial Innovation Foundation for Postgraduate,China+1 种基金Project(2013zzts017)supported by the Graduate Degree Thesis Innovation Foundation of Central South University,ChinaProject(2012bjjxj015)supported by the Excellent Doctor Degree Thesis Support Foundation of Central South University,China
文摘Hot compression test of a novel nickel-free white alloy Cu?12Mn?15Zn?1.5Al?0.3Ti?0.14B?0.1Ce (mass fraction, %) was conducted on a Gleeble?1500 machine in the temperature range of 600?800 °C and the strain rate range of 0.01?10 s?1. The constitutive equation and hot processing map of the alloy were built up according to its hot deformation behavior and hot working characteristics. The deformation activation energy of the alloy is 203.005 kJ/mol. An instability region appears in the hot deformation temperature of 600?700 °C and the strain rate range of 0.32?10 s?1 when the true strain of the alloy is up to 0.7. Under the optimal hot deformation condition of 800 °C and 10 s?1 the prepared specimen has good surface quality and interior structure. The designed nickel-free alloy has very similar white chromaticity with the traditional white copper alloy (Cu?15Ni?24Zn?1.5Pb), and the color difference between them is less than 1.5, which can hardly be distinguished by human eyes.