The ion selectivity of electrodeposited nickel hexacyanoferrate （NiHCF） thin films was investigated using electrochemical impedance spectroscopy （EIS） and cyclic voltammetry （CV）. NiHCF thin films were prepared ...The ion selectivity of electrodeposited nickel hexacyanoferrate （NiHCF） thin films was investigated using electrochemical impedance spectroscopy （EIS） and cyclic voltammetry （CV）. NiHCF thin films were prepared by cathodic deposition on Pt and Al substrates. EIS and CV curves were determined in 1 mol/L （KNO3＋C5NO3） and 1 mol/L （NaNO3＋CsNO3） mixture solutions, which were sensitive to the concentration of Cs^＋ in the electrolytes. Experimental results show that all Nyquist impedance plots show depressed semicircles in the high-frequency range changing over into straight lines at lower frequencies. With increasing amounts of Cs^＋, the redox potentials in CV curves shift toward more positive values and the redox peaks broaden; the semicircle radius in corresponding EIS curves and the charge transfer resistance also increase. EIS combining CV is able to provide valuable insights into the ion selectivity of NiHCF thin films. 2008 University of Science and Technology Beijing. All rights reserved.展开更多
基金the National Natural Science Foundation of China(No.20676089)the Scholar Council Foundation of Shanxi Province,China(No.2004-24).
文摘The ion selectivity of electrodeposited nickel hexacyanoferrate （NiHCF） thin films was investigated using electrochemical impedance spectroscopy （EIS） and cyclic voltammetry （CV）. NiHCF thin films were prepared by cathodic deposition on Pt and Al substrates. EIS and CV curves were determined in 1 mol/L （KNO3＋C5NO3） and 1 mol/L （NaNO3＋CsNO3） mixture solutions, which were sensitive to the concentration of Cs^＋ in the electrolytes. Experimental results show that all Nyquist impedance plots show depressed semicircles in the high-frequency range changing over into straight lines at lower frequencies. With increasing amounts of Cs^＋, the redox potentials in CV curves shift toward more positive values and the redox peaks broaden; the semicircle radius in corresponding EIS curves and the charge transfer resistance also increase. EIS combining CV is able to provide valuable insights into the ion selectivity of NiHCF thin films. 2008 University of Science and Technology Beijing. All rights reserved.