Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions of Ni-39Ti-11Si and Ni-42Ti-8Si (%, mole fraction, the same below), respectively, were fabricated by the laser melting deposition manufacturing process, ...Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions of Ni-39Ti-11Si and Ni-42Ti-8Si (%, mole fraction, the same below), respectively, were fabricated by the laser melting deposition manufacturing process, aiming at studying the effect of Ti, Si contents on microstructure and mechanical properties of the alloys. The Ni-39Ti-11Si alloy consisting of Ti2Ni3Si primary dendrites and Ti2Ni3Si/NiTi eutectic matrix is a conventional hypereutectic Laves phase alloy while the Ni-42Ti-8Si alloy being made up of NiTi primary dendrites uniformly distributed in Ti2Ni3Si/NiTi eutectic is a new hypoeutectic alloy. Mechanical properties of the alloys were investigated by nano-indentation test. The results show that the decrease of Si and the increase of Ti contents change the microstructures of the alloys from hypereutectic to hypoeutectic, which influences the mechanical properties of the alloys remarkably. Corrosion behaviors of the alloys were also evaluated by potentiodynamic anodic polarization curves.展开更多
Ti-Ni-Mo-Si composite coating was fabricated on mild steel by reactive braze coating process with Ti61. 9Ni24. 6Si4. 411409.1 （ wt. % ） powders as the raw materials. Microstr^cture of the coating was characterized b...Ti-Ni-Mo-Si composite coating was fabricated on mild steel by reactive braze coating process with Ti61. 9Ni24. 6Si4. 411409.1 （ wt. % ） powders as the raw materials. Microstr^cture of the coating was characterized by optical microscopy, scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy and micro-hardness tester. Results indicate that the Ti-Ni-Mo-Si composite coating is metallurgically bonded to the mild steel substrate and has high hardness. The microstructure of the coating consists of the reinforcement of Ti5 Si3 and Mo9 Ti4 particles and the matrix of eutectic NiTi2. Due to the poor wettability of NiTi2 liquid at low temperature, TisSi3 and Mo9 Ti4 do not uniformly distribute in the NiTi2 matrix.展开更多
基金Project(50625413) supported by the National Natural Science Foundation of China
文摘Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions of Ni-39Ti-11Si and Ni-42Ti-8Si (%, mole fraction, the same below), respectively, were fabricated by the laser melting deposition manufacturing process, aiming at studying the effect of Ti, Si contents on microstructure and mechanical properties of the alloys. The Ni-39Ti-11Si alloy consisting of Ti2Ni3Si primary dendrites and Ti2Ni3Si/NiTi eutectic matrix is a conventional hypereutectic Laves phase alloy while the Ni-42Ti-8Si alloy being made up of NiTi primary dendrites uniformly distributed in Ti2Ni3Si/NiTi eutectic is a new hypoeutectic alloy. Mechanical properties of the alloys were investigated by nano-indentation test. The results show that the decrease of Si and the increase of Ti contents change the microstructures of the alloys from hypereutectic to hypoeutectic, which influences the mechanical properties of the alloys remarkably. Corrosion behaviors of the alloys were also evaluated by potentiodynamic anodic polarization curves.
文摘Ti-Ni-Mo-Si composite coating was fabricated on mild steel by reactive braze coating process with Ti61. 9Ni24. 6Si4. 411409.1 （ wt. % ） powders as the raw materials. Microstr^cture of the coating was characterized by optical microscopy, scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy and micro-hardness tester. Results indicate that the Ti-Ni-Mo-Si composite coating is metallurgically bonded to the mild steel substrate and has high hardness. The microstructure of the coating consists of the reinforcement of Ti5 Si3 and Mo9 Ti4 particles and the matrix of eutectic NiTi2. Due to the poor wettability of NiTi2 liquid at low temperature, TisSi3 and Mo9 Ti4 do not uniformly distribute in the NiTi2 matrix.