In this work, solid-phase microextraction coupled with gas chromatography–mass spectrometry was developed to determine trace levels of nitrobenzene compounds in water and soil samples. Graphene was chosen as the extr...In this work, solid-phase microextraction coupled with gas chromatography–mass spectrometry was developed to determine trace levels of nitrobenzene compounds in water and soil samples. Graphene was chosen as the extraction material and its composite was coated on a stainless steel wire through sol–gel technique for the solid phase microextraction. The key parameters influencing the extraction efficiency were optimized. Under the optimal conditions, the linearity for the compounds was observed in the range of 0.02–15.0 mg/L for water samples, and 0.2–60.0 mg/kg for soil samples, with the correlation coefficients（r） of 0.9966–0.9987. The limits of detection of the method were 0.0025–0.005 mg/L for water samples, and 0.02–0.04 mg/kg for soil samples. The recoveries for the spiked samples were in the range of 72.0%–113.2%, and the precision, expressed as the relative standard deviations, was less than 12.1%.展开更多
Pt nanoparticles entrapped in ordered mesoporous CMK-3 carbons with p6mm symmetry were prepared using a facile impregnation method, and the resulting materials were characterized using X-ray diffraction spectroscopy, ...Pt nanoparticles entrapped in ordered mesoporous CMK-3 carbons with p6mm symmetry were prepared using a facile impregnation method, and the resulting materials were characterized using X-ray diffraction spectroscopy, N2 adsorption-desorption, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The Pt nanoparticles were highly dispersed in the CMK-3 with 43.7% dispersion. The Pt/CMK-3 catalyst was an effective catalyst for the liquid-phase hydrogenation of nitrobenzene and its derivatives under the experimental conditions studied here. The Pt/CMK-3 catalyst was more active than commercial Pt/C catalyst in most cases. A highest turnover frequency of 43.8 s-1 was measured when the Pt/CMK-3 catalyst was applied for the hydrogenation of 2-methyl-nitrobenzene in ethanol under optimal conditions. It is worthy of note that the Pt/CMK-3 catalyst could be recycled easily, and could be reused at least fourteen times without any loss in activity or selectivity for the hydrogenation of nitrobenzene in ethanol.展开更多
基金Financial support from the National Natural Science Foundation of China(No.31171698)the Innovation Research Group Program of Department of Education of Hebei for Hebei Provincial Universities(No.LJRC009)the Natural Science Foundation of Hebei Province(No.B2012204028)
文摘In this work, solid-phase microextraction coupled with gas chromatography–mass spectrometry was developed to determine trace levels of nitrobenzene compounds in water and soil samples. Graphene was chosen as the extraction material and its composite was coated on a stainless steel wire through sol–gel technique for the solid phase microextraction. The key parameters influencing the extraction efficiency were optimized. Under the optimal conditions, the linearity for the compounds was observed in the range of 0.02–15.0 mg/L for water samples, and 0.2–60.0 mg/kg for soil samples, with the correlation coefficients（r） of 0.9966–0.9987. The limits of detection of the method were 0.0025–0.005 mg/L for water samples, and 0.02–0.04 mg/kg for soil samples. The recoveries for the spiked samples were in the range of 72.0%–113.2%, and the precision, expressed as the relative standard deviations, was less than 12.1%.
基金supported by the National Natural Science Foundation of China(21273076 and 21373089)the Open Research Fund of Top Key Discipline of Chemistry in Zhejiang Provincial Colleges and Key Laboratory of the Ministry of Education for Catalysis Materials(Zhejiang Normal University,ZJHX2013)Shanghai Leading Academic Discipline Project (B409)~~
文摘Pt nanoparticles entrapped in ordered mesoporous CMK-3 carbons with p6mm symmetry were prepared using a facile impregnation method, and the resulting materials were characterized using X-ray diffraction spectroscopy, N2 adsorption-desorption, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The Pt nanoparticles were highly dispersed in the CMK-3 with 43.7% dispersion. The Pt/CMK-3 catalyst was an effective catalyst for the liquid-phase hydrogenation of nitrobenzene and its derivatives under the experimental conditions studied here. The Pt/CMK-3 catalyst was more active than commercial Pt/C catalyst in most cases. A highest turnover frequency of 43.8 s-1 was measured when the Pt/CMK-3 catalyst was applied for the hydrogenation of 2-methyl-nitrobenzene in ethanol under optimal conditions. It is worthy of note that the Pt/CMK-3 catalyst could be recycled easily, and could be reused at least fourteen times without any loss in activity or selectivity for the hydrogenation of nitrobenzene in ethanol.