To provide theoretical basis and practical guidance for preparing composite rods by direct continuous casting, copper-clad aluminum composite rods of external copper layer diameter 12 mm and inner aluminum core diamet...To provide theoretical basis and practical guidance for preparing composite rods by direct continuous casting, copper-clad aluminum composite rods of external copper layer diameter 12 mm and inner aluminum core diameter 8 mm were manufactured. Orthogonal tests consisted of three factors and three levels were carried out to research the effects of melting copper temperature, continuous casting speed and nitrogen pressure on the performance of composite rods. Results showed that nitrogen pressure is the most important factor in influencing the surface quality; continuous casting speed is the most important factor in influencing copper & aluminum inter diffusion amount. Nitrogen pressure can noticeably improve the surface quality and make the rods easily be drawn out, but the surface quality does not show visible improvement when the nitrogen pressure is above 0.05 MPa. Measured by tests, the compound layer can be divided into three types according to its cladding layer degree: deficient cladding, normal cladding and excess cladding. The diameter of normal copper-clad aluminum composite rods can be successfully drawn less than 0.6 mm without annealing.展开更多
基金financially supported by the Program for New Century Excellent Talents in University(NCET-12-0849)the Fundamental Research Funds for the Central Universities(13ZD12)the National Natural Science Foundation of China(No.51006034)
文摘To provide theoretical basis and practical guidance for preparing composite rods by direct continuous casting, copper-clad aluminum composite rods of external copper layer diameter 12 mm and inner aluminum core diameter 8 mm were manufactured. Orthogonal tests consisted of three factors and three levels were carried out to research the effects of melting copper temperature, continuous casting speed and nitrogen pressure on the performance of composite rods. Results showed that nitrogen pressure is the most important factor in influencing the surface quality; continuous casting speed is the most important factor in influencing copper & aluminum inter diffusion amount. Nitrogen pressure can noticeably improve the surface quality and make the rods easily be drawn out, but the surface quality does not show visible improvement when the nitrogen pressure is above 0.05 MPa. Measured by tests, the compound layer can be divided into three types according to its cladding layer degree: deficient cladding, normal cladding and excess cladding. The diameter of normal copper-clad aluminum composite rods can be successfully drawn less than 0.6 mm without annealing.