水热法合成了一个无机-有机杂化的NH_(4)[Cu_(3)^(I)(C_(10)H_(8)N_(2))_(3)Mo_(8)O_(26)]化合物,通过元素分析和单晶X-射线衍射进行了表征。化合物为三斜晶系,P1空间群,晶胞参数a=1.08763(9)nm,b=1.12674(10)nm,c=1.13067(10)nm,α=68....水热法合成了一个无机-有机杂化的NH_(4)[Cu_(3)^(I)(C_(10)H_(8)N_(2))_(3)Mo_(8)O_(26)]化合物,通过元素分析和单晶X-射线衍射进行了表征。化合物为三斜晶系,P1空间群,晶胞参数a=1.08763(9)nm,b=1.12674(10)nm,c=1.13067(10)nm,α=68.4820(10)°,β=83.523(2)°,γ=64.4180(10)°,V=1.16095(2)nm^(3),Z=1,Dc=2.661 g/cm^(3),Mr=1860.73,μ(MoKα)=35.22 cm^(-1),F(000)=888,R=0.0478,wR=0.099。化合物的结构包含2个结晶学上独立的铜原子、不连续的多氧阴离子β-[Mo_(8)O_(2)6]4-和无限扩展的[Cu I(C_(10)H_(8)N_(2))]链。每一个铜原子为类似的{CuN_(2)}配位模式,被4,4’-联吡啶连接成一维沿a轴方向的[Cu(C 10 H 8 N 2)]+链。分子结构中存在氢键和π…π作用。对化合物的热稳定性、荧光性质也进行了研究。展开更多
Negative thermal expansion (NTE) material ZrW2O8 powders were synthesized using co-precipitation route. The precursor of ZrW2O8 was studied by Thermogravimetric and differential scanning calorimetry (TG-DSC). The stru...Negative thermal expansion (NTE) material ZrW2O8 powders were synthesized using co-precipitation route. The precursor of ZrW2O8 was studied by Thermogravimetric and differential scanning calorimetry (TG-DSC). The structure and morphology of the resulting powders were characterized by Powder X-ray diffraction (XRD) and Scanning electron microscopy (SEM), respectively. The results showed that the samples were single phase of α- ZrW2O8 with regular shape. High temperature X-ray diffraction measurement indicated that the thermal expansion coefficient of ZrW2O8 was - 10.35 ×10-6 K-1 in the temperature range from room temperature to 150 ℃, - 3.08 × 10-6 K-1 from 200 ℃ to 600 ℃ and the average value was - 5.38 ×10-6 K-1. At the same time, polyethylene glycol (PEG) was used as dispersant to primary control the size of ZrW2O8.展开更多
文摘水热法合成了一个无机-有机杂化的NH_(4)[Cu_(3)^(I)(C_(10)H_(8)N_(2))_(3)Mo_(8)O_(26)]化合物,通过元素分析和单晶X-射线衍射进行了表征。化合物为三斜晶系,P1空间群,晶胞参数a=1.08763(9)nm,b=1.12674(10)nm,c=1.13067(10)nm,α=68.4820(10)°,β=83.523(2)°,γ=64.4180(10)°,V=1.16095(2)nm^(3),Z=1,Dc=2.661 g/cm^(3),Mr=1860.73,μ(MoKα)=35.22 cm^(-1),F(000)=888,R=0.0478,wR=0.099。化合物的结构包含2个结晶学上独立的铜原子、不连续的多氧阴离子β-[Mo_(8)O_(2)6]4-和无限扩展的[Cu I(C_(10)H_(8)N_(2))]链。每一个铜原子为类似的{CuN_(2)}配位模式,被4,4’-联吡啶连接成一维沿a轴方向的[Cu(C 10 H 8 N 2)]+链。分子结构中存在氢键和π…π作用。对化合物的热稳定性、荧光性质也进行了研究。
文摘Negative thermal expansion (NTE) material ZrW2O8 powders were synthesized using co-precipitation route. The precursor of ZrW2O8 was studied by Thermogravimetric and differential scanning calorimetry (TG-DSC). The structure and morphology of the resulting powders were characterized by Powder X-ray diffraction (XRD) and Scanning electron microscopy (SEM), respectively. The results showed that the samples were single phase of α- ZrW2O8 with regular shape. High temperature X-ray diffraction measurement indicated that the thermal expansion coefficient of ZrW2O8 was - 10.35 ×10-6 K-1 in the temperature range from room temperature to 150 ℃, - 3.08 × 10-6 K-1 from 200 ℃ to 600 ℃ and the average value was - 5.38 ×10-6 K-1. At the same time, polyethylene glycol (PEG) was used as dispersant to primary control the size of ZrW2O8.