Ring opening copolymerization of succinic anhydride (SA) with ethylene oxide (EO)was successfully carried out by using a series of aluminum-based catalyst in 1,4-dioxane at62±2℃. The results showed that in-situ ...Ring opening copolymerization of succinic anhydride (SA) with ethylene oxide (EO)was successfully carried out by using a series of aluminum-based catalyst in 1,4-dioxane at62±2℃. The results showed that in-situ AlR_3-H_2O (R=ethyl, iso-butyl) catalysts gavehigher molecular weight (M_w～10~4), while Al(OR)_3 catalysts gave the higher alternatingcopolymer structure with slightly lower molecular weight. The in-situ AlR_3-H_2O systemshave been evaluated in more detail for the reaction which showed the optimum H_2O/Almolar ratio to be 0.5. The copolymers with different composition (F_(SA)/F_(EO)= 36/64to 45/55 mol/mol) were synthesized by using different monomer feed ratio. The melt-ing point (T_m), glass transition temperature (T_g) and enthalpy of fusion (ΔH_f) of thesecopolymers are depended on the copolymer composition and in the range of 87～102℃,-12～-18℃, and 37～66J/g, respectively. The second heating scan of DSC also in-dicated that the higher alternating copolymer was more easily recrystallized. The onsetdecomposition temperature was more than 300℃ under nitrogen and influenced by thecopolymer composition.展开更多
A novel Pd（ll） organometal catalyst with three-dimensional （3D） cage-like la3d cubic mesoporous structure and high surface area was prepared. In comparison with the corresponding catalyst with two-dimensional （2D...A novel Pd（ll） organometal catalyst with three-dimensional （3D） cage-like la3d cubic mesoporous structure and high surface area was prepared. In comparison with the corresponding catalyst with two-dimensional （2D） P6mm hexagonal mesoporous structure, the as-prepared catalyst exhibited higher activities in the water-medium Suzuki coupling reactions owing to the diminished diffusion limit. It showed comparable efficiencies with the Pd（PPh3）2C12 homogeneous catalyst and could be easily recycled and reused for five times without significant loss of activity.展开更多
文摘Ring opening copolymerization of succinic anhydride (SA) with ethylene oxide (EO)was successfully carried out by using a series of aluminum-based catalyst in 1,4-dioxane at62±2℃. The results showed that in-situ AlR_3-H_2O (R=ethyl, iso-butyl) catalysts gavehigher molecular weight (M_w～10~4), while Al(OR)_3 catalysts gave the higher alternatingcopolymer structure with slightly lower molecular weight. The in-situ AlR_3-H_2O systemshave been evaluated in more detail for the reaction which showed the optimum H_2O/Almolar ratio to be 0.5. The copolymers with different composition (F_(SA)/F_(EO)= 36/64to 45/55 mol/mol) were synthesized by using different monomer feed ratio. The melt-ing point (T_m), glass transition temperature (T_g) and enthalpy of fusion (ΔH_f) of thesecopolymers are depended on the copolymer composition and in the range of 87～102℃,-12～-18℃, and 37～66J/g, respectively. The second heating scan of DSC also in-dicated that the higher alternating copolymer was more easily recrystallized. The onsetdecomposition temperature was more than 300℃ under nitrogen and influenced by thecopolymer composition.
文摘A novel Pd（ll） organometal catalyst with three-dimensional （3D） cage-like la3d cubic mesoporous structure and high surface area was prepared. In comparison with the corresponding catalyst with two-dimensional （2D） P6mm hexagonal mesoporous structure, the as-prepared catalyst exhibited higher activities in the water-medium Suzuki coupling reactions owing to the diminished diffusion limit. It showed comparable efficiencies with the Pd（PPh3）2C12 homogeneous catalyst and could be easily recycled and reused for five times without significant loss of activity.