Ultrafine polycaprolactone(PCL)fibers containing watersoluble drug tetracycline hydrochloride(Tet)were prepared by emulsion electrospinning.Sorbitan monooleate(Span80)was added as an essential additive to form stable ...Ultrafine polycaprolactone(PCL)fibers containing watersoluble drug tetracycline hydrochloride(Tet)were prepared by emulsion electrospinning.Sorbitan monooleate(Span80)was added as an essential additive to form stable water/oil emulsions and fabricate fibers with core-sheath structure.Different concentrations of Span80(0-40 g/L)were used to investigate the stability of emulsion and size of dispersed droplets.The scanning electron microscope(SEM)images indicated that the morphology of the fibers with Span80 were beaded-free with diameters of 200-400 nm,and Span80 enhanced the spinnability of electrospinning solution.The laser scanning confocal microscope(LSCM)images indicated that Tet was well encapsulated into the core region of the PCL fibers.The transmission electron microscope(TEM)image showed the formation of core-sheath structure.The loading efficiency(LE)and entrapment efficiency(EE)of Tet were calculated and release profiles in artificial saliva buffer solution(pH=6.8)were also analyzed.The results revealed that LE and EE of fibers with Span80decreased with the increase of its concentration.Fibers with coresheath structure had a longer effective release lifetime than without Span80.The increase of Span80 resulted in higher hydrophilicity of fibers and faster release rate of Tet.展开更多
基金“111 Project” Biomedical Textile Materials Science and Technology,China(No.B07024)
文摘Ultrafine polycaprolactone(PCL)fibers containing watersoluble drug tetracycline hydrochloride(Tet)were prepared by emulsion electrospinning.Sorbitan monooleate(Span80)was added as an essential additive to form stable water/oil emulsions and fabricate fibers with core-sheath structure.Different concentrations of Span80(0-40 g/L)were used to investigate the stability of emulsion and size of dispersed droplets.The scanning electron microscope(SEM)images indicated that the morphology of the fibers with Span80 were beaded-free with diameters of 200-400 nm,and Span80 enhanced the spinnability of electrospinning solution.The laser scanning confocal microscope(LSCM)images indicated that Tet was well encapsulated into the core region of the PCL fibers.The transmission electron microscope(TEM)image showed the formation of core-sheath structure.The loading efficiency(LE)and entrapment efficiency(EE)of Tet were calculated and release profiles in artificial saliva buffer solution(pH=6.8)were also analyzed.The results revealed that LE and EE of fibers with Span80decreased with the increase of its concentration.Fibers with coresheath structure had a longer effective release lifetime than without Span80.The increase of Span80 resulted in higher hydrophilicity of fibers and faster release rate of Tet.