A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O c...A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.展开更多
A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5...A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.展开更多
Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b...Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b =1 194 2(2) nm, c =1 648 0(4) nm, β =117 064(14)°, V =3 644 2(13) nm 3, Z =6, D c=1 901 g/cm 3, I ≥2 σ(I )=2 274, R =0 055 6, R w=0 134 8. GaP 1 is characteristic of the intercalation of disordered fully protonated diethylenetriamine among two dimensional inorganic framework built up from PO 4, GaO 5 and GaO 6 primary structure units. The framework features 3 , 4 , 5 and 8 ring topological connectivity.展开更多
以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌...以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌进行表征,结果表明在700℃下烧结15 h合成的3LiMnPO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径相对较小且分布均匀。电化学性能研究表明,3LiMnPO4·Li3V2(PO4)3在室温0.2 C倍率下首次充放电容量分别为148.2 m Ah/g和141.5 m Ah/g,循环50次后放电容量为136.7 m Ah/g。展开更多
文摘A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.
文摘A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.
文摘Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b =1 194 2(2) nm, c =1 648 0(4) nm, β =117 064(14)°, V =3 644 2(13) nm 3, Z =6, D c=1 901 g/cm 3, I ≥2 σ(I )=2 274, R =0 055 6, R w=0 134 8. GaP 1 is characteristic of the intercalation of disordered fully protonated diethylenetriamine among two dimensional inorganic framework built up from PO 4, GaO 5 and GaO 6 primary structure units. The framework features 3 , 4 , 5 and 8 ring topological connectivity.
文摘以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌进行表征,结果表明在700℃下烧结15 h合成的3LiMnPO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径相对较小且分布均匀。电化学性能研究表明,3LiMnPO4·Li3V2(PO4)3在室温0.2 C倍率下首次充放电容量分别为148.2 m Ah/g和141.5 m Ah/g,循环50次后放电容量为136.7 m Ah/g。