Rare earth compounds can be used as PVC thermal stabilizers. According to the infrared spectra of the mixture of PVC and some stearates, the mechanism of stabilization of different stearates was studied. The specialty...Rare earth compounds can be used as PVC thermal stabilizers. According to the infrared spectra of the mixture of PVC and some stearates, the mechanism of stabilization of different stearates was studied. The specialty of rare earth stabilizers was found. They can change the conformation of PVC and restrain the elimination of HCl. From this aspect, the unique synergetic effect with other stabilizers of rare earth compounds can be explained.展开更多
A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was ox...A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.展开更多
文摘Rare earth compounds can be used as PVC thermal stabilizers. According to the infrared spectra of the mixture of PVC and some stearates, the mechanism of stabilization of different stearates was studied. The specialty of rare earth stabilizers was found. They can change the conformation of PVC and restrain the elimination of HCl. From this aspect, the unique synergetic effect with other stabilizers of rare earth compounds can be explained.
基金Project supported by the Postdoctoral Foundation of Central South University
文摘A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.