In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unit...In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unity at 1180 - 900cm-1 range because of the existence of anomalous dispersion. The optical losses of hollow waveguides were calculated,the predicted losses at 940cm-1are 0. 65 and 0. 081B/ m as the inner diameter of fiber is 0. 5 and 1. 0mm respectively. The glasses can be used as the cladding materials of hol-low waveguides for transmitting CO2 laser from the measurements of characteristic temperatures, coefficient of expansion and chemical durability.展开更多
The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B2O3-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope (FTIR), differential therma...The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B2O3-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope (FTIR), differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% (mass fraction) Al2O3-doped glass ceramics sintered at 725 °C have better properties of density ρ=2.72 g/cm3, dielectric constant εr=6.78, dielectric loss tan δ=2.6×10-3 (measured at 9.8 GHz), which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.展开更多
文摘In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unity at 1180 - 900cm-1 range because of the existence of anomalous dispersion. The optical losses of hollow waveguides were calculated,the predicted losses at 940cm-1are 0. 65 and 0. 081B/ m as the inner diameter of fiber is 0. 5 and 1. 0mm respectively. The glasses can be used as the cladding materials of hol-low waveguides for transmitting CO2 laser from the measurements of characteristic temperatures, coefficient of expansion and chemical durability.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institution, China
文摘The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B2O3-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope (FTIR), differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% (mass fraction) Al2O3-doped glass ceramics sintered at 725 °C have better properties of density ρ=2.72 g/cm3, dielectric constant εr=6.78, dielectric loss tan δ=2.6×10-3 (measured at 9.8 GHz), which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.