Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-mi...Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-milling method for highly active and selective hydrogenation of CO_(2) to value-added hydrocarbons.When reacted at 320℃,1.0 MPa and 9600 mL h^(-1) g_(cat)^(-1),the selectivity to light olefin(C_(2)^(=)-C_(4)^(=)) and C_(5)+ species achieves 57.3% and 22.3%,respectively,at a CO_(2) co nversion of 31.4%,which is superior to previous Fe-based catalysts.The CO_(2) activation can be promoted by the CoFe phase formed by reactive ball milling of the Fe-Co_(3)O_(4) mixture,and the in-situ Co_(2)C and Fe_(5)C_(2) formed during hydrogenation are beneficial for the C-C coupling reaction.The initial C-C coupling is related to the combination of CO species with the surface carbon of Fe/Co carbides,and the sustained C-C coupling is maintained by self-recovery of defective carbides.This new strategy contributes to the development of efficient catalysts for the hydrogenation of CO_(2) to value-added hydrocarbons.展开更多
化石燃料的燃烧导致大气中二氧化碳(CO_(2))的浓度迅速上升,并引发了严重的能源、环境危机。由可再生电力驱动的电催化CO_(2)还原为增值化学品和燃料是解决当前化石燃料枯竭的一种有效方法。采用“一锅法”制备了磷(P)修饰的高分散性“...化石燃料的燃烧导致大气中二氧化碳(CO_(2))的浓度迅速上升,并引发了严重的能源、环境危机。由可再生电力驱动的电催化CO_(2)还原为增值化学品和燃料是解决当前化石燃料枯竭的一种有效方法。采用“一锅法”制备了磷(P)修饰的高分散性“钴-氮-碳”(Co-N-C/P)催化剂,通过扫描电子显微镜(SEM)、X射线衍射(XRD)、拉曼光谱(Raman)和X射线光电子能谱(XPS)等手段对催化剂的形貌、元素分布、缺陷程度、表面元素价态及配位结构进行了表征,并考察了其在H型电解槽中电催化CO_(2)还原为CO的性能。测试结果表明,所制备的Co-N-C/P催化剂在-0.9 V vs.RHE的外加电位下具有97.0%的CO法拉第效率(FE_(CO)),电流密度为4.58 mA/cm^(2),并可以进行26 h的稳定性测试。与Co-N-C催化剂相比,P的掺杂更有利于Co原子在碳黑基底上的良好分散,相应的FE_(CO)提高了约38.9%,说明P的掺杂有效提高了Co-N-C催化剂的电催化CO_(2)还原为CO的性能。展开更多
基金supported by the National Natural Science Foundation of China (22008098, 21978156, 42002040)the Program for Innovative Research Team (in Science and Technology) in University of Henan Province (21IRTSTHN004)+1 种基金the Program for Science & Technology Innovation Talents in Universities of Henan Province (22HASTIT008)the Foundation of State Key Laboratory of High-efficiency Utilization of Coal and Green Chemical Engineering (2022-K34)。
文摘Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-milling method for highly active and selective hydrogenation of CO_(2) to value-added hydrocarbons.When reacted at 320℃,1.0 MPa and 9600 mL h^(-1) g_(cat)^(-1),the selectivity to light olefin(C_(2)^(=)-C_(4)^(=)) and C_(5)+ species achieves 57.3% and 22.3%,respectively,at a CO_(2) co nversion of 31.4%,which is superior to previous Fe-based catalysts.The CO_(2) activation can be promoted by the CoFe phase formed by reactive ball milling of the Fe-Co_(3)O_(4) mixture,and the in-situ Co_(2)C and Fe_(5)C_(2) formed during hydrogenation are beneficial for the C-C coupling reaction.The initial C-C coupling is related to the combination of CO species with the surface carbon of Fe/Co carbides,and the sustained C-C coupling is maintained by self-recovery of defective carbides.This new strategy contributes to the development of efficient catalysts for the hydrogenation of CO_(2) to value-added hydrocarbons.
文摘化石燃料的燃烧导致大气中二氧化碳(CO_(2))的浓度迅速上升,并引发了严重的能源、环境危机。由可再生电力驱动的电催化CO_(2)还原为增值化学品和燃料是解决当前化石燃料枯竭的一种有效方法。采用“一锅法”制备了磷(P)修饰的高分散性“钴-氮-碳”(Co-N-C/P)催化剂,通过扫描电子显微镜(SEM)、X射线衍射(XRD)、拉曼光谱(Raman)和X射线光电子能谱(XPS)等手段对催化剂的形貌、元素分布、缺陷程度、表面元素价态及配位结构进行了表征,并考察了其在H型电解槽中电催化CO_(2)还原为CO的性能。测试结果表明,所制备的Co-N-C/P催化剂在-0.9 V vs.RHE的外加电位下具有97.0%的CO法拉第效率(FE_(CO)),电流密度为4.58 mA/cm^(2),并可以进行26 h的稳定性测试。与Co-N-C催化剂相比,P的掺杂更有利于Co原子在碳黑基底上的良好分散,相应的FE_(CO)提高了约38.9%,说明P的掺杂有效提高了Co-N-C催化剂的电催化CO_(2)还原为CO的性能。