Extrusion-calendering method was developed to prepare single-polymer composites（SPCs） of ultrahigh molecular weight polyethylene（ UHMWPE） fabric reinforcing low density polyethylene（LDPE）.Differential scanning c...Extrusion-calendering method was developed to prepare single-polymer composites（SPCs） of ultrahigh molecular weight polyethylene（ UHMWPE） fabric reinforcing low density polyethylene（LDPE）.Differential scanning calorimeter（DSC） experiments were executed to determine the setup of extrusion temperature.Effects of the die temperature on the tensile and interfacial performances of SPCs were studied through the tensile and T-peel tests,respectively. The results showed that both tensile strength and modulus increased initially and decreased afterwards as the temperature increased. The peak values of tensile strength and modulus of PE SPCs,which are 10. 8 and 3. 5 times as high as those of the unreinforced LDPE respectively,were obtained at 150 ℃. Higher temperatures also give a positive effect on peel strength. Scanning electron microscopy（ SEM） and camera were also used to observe the morphology of the SPCs samples.展开更多
Over the past decades, two-dimensional（2D） nanomaterials possessing planar layered architecture and unique electronic structures have been being quickly developed, due to their wide potential application in the fiel...Over the past decades, two-dimensional（2D） nanomaterials possessing planar layered architecture and unique electronic structures have been being quickly developed, due to their wide potential application in the fields of chemistry, physics, and materials science. As a new family of 2D nanomaterials, 2D polymerbased nanosheets, featuring excellent characters, such as tunable framework structures, light weight, flexibility, high specific surface, and good semiconducting properties, have been emerging as one kind of promising functional materials for optoelectronics, gas separation, catalysis and sensing, etc. In this review, the recent progress in synthetic approach and characterization of 2D polymer-based nanosheets were summarized, and their current advances in electrochemical energy storage and conversion including second batteries, supercapacitors, oxygen reduction and hydrogen evolution were discussed systematically.展开更多
基金Supported by the National Natural Science Foundation of China(51403019)
文摘Extrusion-calendering method was developed to prepare single-polymer composites（SPCs） of ultrahigh molecular weight polyethylene（ UHMWPE） fabric reinforcing low density polyethylene（LDPE）.Differential scanning calorimeter（DSC） experiments were executed to determine the setup of extrusion temperature.Effects of the die temperature on the tensile and interfacial performances of SPCs were studied through the tensile and T-peel tests,respectively. The results showed that both tensile strength and modulus increased initially and decreased afterwards as the temperature increased. The peak values of tensile strength and modulus of PE SPCs,which are 10. 8 and 3. 5 times as high as those of the unreinforced LDPE respectively,were obtained at 150 ℃. Higher temperatures also give a positive effect on peel strength. Scanning electron microscopy（ SEM） and camera were also used to observe the morphology of the SPCs samples.
基金financially supported by the National Natural Science Foundation of China(51403126,21574080,61306018 and 21504057)Shanghai Committee of Science and Technology(15JC1490500,16JC1400703,and 17ZR1441700)+1 种基金Open Project Program of the State Key Laboratory of Photocatalysis on Energy and Environment(SKLPEE-KF201702,Fuzhou University)State Key Laboratory of Supramolecular Structure and Materials(sklssm201732,Jinlin University)
文摘Over the past decades, two-dimensional（2D） nanomaterials possessing planar layered architecture and unique electronic structures have been being quickly developed, due to their wide potential application in the fields of chemistry, physics, and materials science. As a new family of 2D nanomaterials, 2D polymerbased nanosheets, featuring excellent characters, such as tunable framework structures, light weight, flexibility, high specific surface, and good semiconducting properties, have been emerging as one kind of promising functional materials for optoelectronics, gas separation, catalysis and sensing, etc. In this review, the recent progress in synthetic approach and characterization of 2D polymer-based nanosheets were summarized, and their current advances in electrochemical energy storage and conversion including second batteries, supercapacitors, oxygen reduction and hydrogen evolution were discussed systematically.