Both furnace cooled and as-cast eutectoid Zn-Al alloys were investigated under external tensile stress at 100℃. It was observed that the external tensile stress caused decomposition of two metastable phases η'T ...Both furnace cooled and as-cast eutectoid Zn-Al alloys were investigated under external tensile stress at 100℃. It was observed that the external tensile stress caused decomposition of two metastable phases η'T and η'S which derived from both original state of the alloy, and a phase transformation, αf +ε→T' +η， in both furnace cooled and as-cast eutectoid Zn-Al alloys. Also spheroidized structure formed partially during tensile testing. Superplasticity of the alloy has been discussed correlating with the phase transformations and microstructural changes.展开更多
It has been found that the brittle material, monocrystalline silicon, can be machined in ductile mode in nanoscale cutting when the tool cutting edge radius is reduced to nanoscale and the undeformed chip thickness is...It has been found that the brittle material, monocrystalline silicon, can be machined in ductile mode in nanoscale cutting when the tool cutting edge radius is reduced to nanoscale and the undeformed chip thickness is smaller than the tool edge radius. In order to better understand the mechanism of ductile mode cutting of silicon, the molecular dynamics （MD） method is employed to simulate the nanoscale cutting of monocrystalline silicon. The simulated variation of the cutting forces with the tool cutting edge radius is compared with the cutting force results from experimental cutting tests and they show a good agreement. The results also indicate that there is silicon phase transformation from monocrystalline to amorphous in the chip formation zone that can be used to explain the cause of ductile mode cutting. Moreover, from the simulated stress results, the two necessary conditions of ductile mode cutting, the tool cutting edge radius are reduced to nanoscale and the undeformed chip thickness should be smaller than the tool cutting edge radius, have been explained.展开更多
文摘Both furnace cooled and as-cast eutectoid Zn-Al alloys were investigated under external tensile stress at 100℃. It was observed that the external tensile stress caused decomposition of two metastable phases η'T and η'S which derived from both original state of the alloy, and a phase transformation, αf +ε→T' +η， in both furnace cooled and as-cast eutectoid Zn-Al alloys. Also spheroidized structure formed partially during tensile testing. Superplasticity of the alloy has been discussed correlating with the phase transformations and microstructural changes.
基金Selected from Proceedings of the 7th International Conference on Frontiers of DesignManufacturing(ICFDM'2006).
文摘It has been found that the brittle material, monocrystalline silicon, can be machined in ductile mode in nanoscale cutting when the tool cutting edge radius is reduced to nanoscale and the undeformed chip thickness is smaller than the tool edge radius. In order to better understand the mechanism of ductile mode cutting of silicon, the molecular dynamics （MD） method is employed to simulate the nanoscale cutting of monocrystalline silicon. The simulated variation of the cutting forces with the tool cutting edge radius is compared with the cutting force results from experimental cutting tests and they show a good agreement. The results also indicate that there is silicon phase transformation from monocrystalline to amorphous in the chip formation zone that can be used to explain the cause of ductile mode cutting. Moreover, from the simulated stress results, the two necessary conditions of ductile mode cutting, the tool cutting edge radius are reduced to nanoscale and the undeformed chip thickness should be smaller than the tool cutting edge radius, have been explained.