Mo-C codoped TiO2 films were prepared by RF magnetron cosputtering. Ultraviolet-visible spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray Analysis and X-Ray Diffraction w...Mo-C codoped TiO2 films were prepared by RF magnetron cosputtering. Ultraviolet-visible spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray Analysis and X-Ray Diffraction were used to study the influences of codoping on energy gap, surface morphology, valence states of elements, ions content and crystal structure, respectively. The concentration of photogenerated carriers was measured by studying photocurrent density, while catalytic property was evaluated by observing degradation rate of methylene blue under visible light. A Mo-doped TiO2 film, whose content of Mo had been optimized in advance, was prepared and later used for subsequent comparisons with codoped samples. The result indicates that Mo-C codoping could curtail the energy gap and shift the absorption edge toward visible range. Under the illumination of visible light, codoped TiO2 films give rise to stronger photocurrent due to smaller band gaps. It is also found that Mo, C codoping results in a porous surface, whose area declines gradually with increasing carbon content. Carbon and Molybdenum doses were delicately optimized. Under the illumination of visible light, sample doped with 9.78at% carbon and 0.36at% Mo presents the strongest photocurrent which is about 8 times larger than undoped TiO2 films, and about 6 times larger than samples doped with Mo only.展开更多
Antimony selenide(Sb2Se3) films are widely used in phase change memory and solar cells due to their stable switching effect and excellent photovoltaic properties. These properties of the films are affected by the film...Antimony selenide(Sb2Se3) films are widely used in phase change memory and solar cells due to their stable switching effect and excellent photovoltaic properties. These properties of the films are affected by the film thickness. A method combining the advantages of Levenberg–Marquardt method and spectral fitting method(LM–SFM) is presented to study the dependence of refractive index(RI), absorption coefficient, optical band gap, Wemple–Di Domenico parameters, dielectric constant and optical electronegativity of the Sb2Se3films on their thickness. The results show that the RI and absorption coefficient of the Sb2Se3films increase with the increase of film thickness, while the optical band gap decreases with the increase of film thickness. Finally, the reasons why the optical and electrical properties of the film change with its thickness are explained by x-ray diffractometer(XRD), energy dispersive x-ray spectrometer(EDS), Mott–Davis state density model and Raman microstructure analysis.展开更多
Six novel rod-like magnetic liquid crystals have been prepared, in which trans-bicyclohexyl or trans-cyclohexylphenyl and biphenylcarboxylic acid phenyl ester mesogenic cores with n-propyl and n-pentyl substituents we...Six novel rod-like magnetic liquid crystals have been prepared, in which trans-bicyclohexyl or trans-cyclohexylphenyl and biphenylcarboxylic acid phenyl ester mesogenic cores with n-propyl and n-pentyl substituents were terminated by 4-hydroxyl- TEMPO (TEMPO = 2,2,6,6-tetramethylpiperidine-l-oxy). Their structures were confirmed by elemental analysis, IR and MS. Determined by SQUID, EPR, DSC and HS-POM (heat stage polarizing optical microscope), the six compounds all have both magnetic and liquid crystalline properties; their temperature ranges of mesophase were from 16.0 to 24.8 ℃, and the magnetic liquid crystal molecules could obviously improve the response sensitivity of liquid crystal materials.展开更多
A new photoresponsive D--A dye, mPS, has been designed and synthesized. Compared to the parent dye PS, IPCE values in the region from 400 nm to 560 nm was greatly improved upon changing the attaching group from the p...A new photoresponsive D--A dye, mPS, has been designed and synthesized. Compared to the parent dye PS, IPCE values in the region from 400 nm to 560 nm was greatly improved upon changing the attaching group from the p- position to the o- position of the p-conjugation bridge. A solar cell based on mPS generated a remarkably high overall yield of 5.4% under irradiation of 80.0 mW cm-2 white light from a Xe lamp. Compared with PS, the overall yield ?increased by 64%.展开更多
Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,w...Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.展开更多
In recent years,transparent and flexible materials have been widely pursued in electronics and optoelectronics fields for usage as planar electrodes,energy conversion components and sensing units.As the most widely ap...In recent years,transparent and flexible materials have been widely pursued in electronics and optoelectronics fields for usage as planar electrodes,energy conversion components and sensing units.As the most widely applied semiconductor material,the related progress in silicon is of great significance although with large difficulty.Herein,we report a one-step method to achieve flexible and transparent silicon nanowires aerogel membrane.A competitive carrier kinetics involving interfacial trapped carriers and the valence electrons transition is demonstrated,according to the photoelectric performance of a sandwiched graphene/silicon nanowires membrane/AI device,i.e.,rapidly positive photoresponse dominated by laser excited^ee-carriers generation(〜500 ms)and subsequent slow negative photocurrent evolution due to laser heating involved multi-levels process(>10 s).These results contribute to fabrication of silicon nanowire self-assembly structures and also the exploration of their optoelectrical properties in flexible and transparent devices.展开更多
Two conjugated ethynyl-linked oligomers,oligo(benzodithiophene-ethynylene-benzothiadiazole)(O1)and oligo(benzodithiophene-ethynylene-carbazole)(O2),were synthesized by Sonogashira coupling reaction.Their de-grees of p...Two conjugated ethynyl-linked oligomers,oligo(benzodithiophene-ethynylene-benzothiadiazole)(O1)and oligo(benzodithiophene-ethynylene-carbazole)(O2),were synthesized by Sonogashira coupling reaction.Their de-grees of polymerization were 7 and 10,respectively.Their photophysical and electrochemical properties were in-vestigated.O1 exhibitd two strong absorption bands at 404 nm and 483 nm,and O2 at 401 nm and 429 nm.The re-sults of UV-Vis,cyclic voltammetry(CV)and theoretical calculations showed that O1 has a narrower band gap than O2.The conductivities of O1 and O2 were 1.05×10^(−15) and 6.98×10^(−16) S/cm,respectively,and would increase to 1.23×10^(−10) and 1.05×10^(−10) S/cm after doping with iodine.展开更多
An effective method based on laser etching and driving layer strategy was proposed to prepare patterned Ag nanoparticles(Ag NPs)on fluorine-doped tin oxide(FTO)/glass substrate and thus to enhance the photoelectric pr...An effective method based on laser etching and driving layer strategy was proposed to prepare patterned Ag nanoparticles(Ag NPs)on fluorine-doped tin oxide(FTO)/glass substrate and thus to enhance the photoelectric properties.This method successively included depositing an aluminum-doped zinc oxide(AZO)driving layer,laser etching,depositing an Ag layer,furnace annealing and laser removal.Different AZO and Ag layer thicknesses were adopted,and the surface morphology,crystal structure and photoelectric properties were investigated.An Ag NPs/FTO/glass sample without an AZO driving layer was prepared for comparison.It was found that furnace annealing of the Ag layer combined with the AZO driving layer,rather than that without the AZO driving layer,was more conducive to generating patterned Ag NPs.Using a 20-nmthick AZO layer and a 150-nm-thick Ag layer led to the formation of uniformly distributed Ag NPs being aligned along the laser-etched grooves to form a pattern.The as-obtained sample had the best comprehensive photoelectric property with an average transmittance of 79.95%,a sheet resistance of 7.11Ω/sq and the highest figure of merit of 1.50×10^(-2)Ω^(-1),confirming the feasibility of the proposed method and providing enlightenment for related researches of transparent conductive oxide-based films.展开更多
We give the first report on the experimental investigation of a p-β-FeSi2/n-4H-SiC heterojunction. A β-/%FeSiE/n-4H-SiC heterojunction near-infrared photodiode was fabricated on 4H-SiC substrate by magnetron sputter...We give the first report on the experimental investigation of a p-β-FeSi2/n-4H-SiC heterojunction. A β-/%FeSiE/n-4H-SiC heterojunction near-infrared photodiode was fabricated on 4H-SiC substrate by magnetron sputtering and rapid thermal annealing (RTA). Sharp film-substrate interfaces were confirmed by scanning elec-tron microscopy (SEM). The current density-voltage and photoresponse characteristics were measured. The measurements showed that the device exhibited good rectifying properties. The photocurrent density was about 1.82 mA/cm^2 at a bias voltage of -1 V under illumination by a 5 mW, 1.31 μm laser, and the dark current density was approximately 0.537 mA/cm^2. The detectivity was estimated to be 8.8×10^9 cmHzl/2/W at 1.31 μm. All of the measurements were made at room temperature. The results suggest that the p-β-FeSiE/n-4H-SiC heterojunctions can be used as near-infrared photodiodes that are applicable to optically-activated SiC-based devices.展开更多
Indium doped ZnS (ZnS:In) films were prepared on glass substrate using thermal evaporation technol- ogy. It was found that the structural, optical and electrical properties of ZnS:ln films strongly depend on the s...Indium doped ZnS (ZnS:In) films were prepared on glass substrate using thermal evaporation technol- ogy. It was found that the structural, optical and electrical properties of ZnS:ln films strongly depend on the substrate temperature (Ts). By X-ray diffraction (XRD), atomic force microscopy (AFM), transmittance spectroscopy, and electric performance measurements, the effect of Ts on ZnS:In film is studied in detail. It reveals that Ts has impor- tant effect on ZnS grain size, crystallinity, lattice disorder, etc., which further leads to the obvious influence on its optical and electrical performance. Under the optimized Ts, the performance, especially the conductivity, achieved in this work is far higher than that reported for other n-type ZnS films.展开更多
In the present work,the comparative study of the electric response of Sn_(2)P_(2)S_(6) films to the visible light action was carried out without and under external electric field.The light flux modulated by a chopper ...In the present work,the comparative study of the electric response of Sn_(2)P_(2)S_(6) films to the visible light action was carried out without and under external electric field.The light flux modulated by a chopper induces the integral response comprising time-dependent photoelectric and photovoltaic components.It was shown that spontaneous polarization influences the electric response characteristics.展开更多
With the rapid development of indium tin oxide(ITO)in the electronic display industry,choosing which raw powders to prepare high-quality ITO targets has always been a controversial topic.In the work,in order to clearl...With the rapid development of indium tin oxide(ITO)in the electronic display industry,choosing which raw powders to prepare high-quality ITO targets has always been a controversial topic.In the work,in order to clearly understand the effect of the raw powders on the microstructure and properties of ITO targets and thin films,tin-doped indium oxide(dITO)and In_(2)O_3-SnO_(2)mixed(mITO)powders were chosen to prepare ITO targets for depositing the films and a comparative study on their microstructure and properties was conducted.It is found that,(1)dITO targets possess a higher solid solubility of tin in indium oxide and more uniform elemental distribution,while there are a higher density,a finer grain size and a higher mass ratio of In_(2)O_3 to SnO_(2)for the mITO targets;(2)dITO films with more coarser columnar grains and a rougher surface prefer to grow along the[100]direction in an Ar atmosphere;(3)the conductive property of ITO films only depends on the doping amount of tin and is independent of the raw powders and the preparation process of the target source;(4)dITO films possess the superior optical property and narrower optical band gap;(5)the etching property of mITO films is superior to that of dITO films due to the lower solid solubility of tin in indium oxide.展开更多
As natural one-dimensional confined electron transport channels and photonpropagation paths, nanowires (NWs) display unmatched properties and hugepotential for application in diverse fields. The ability to construct a...As natural one-dimensional confined electron transport channels and photonpropagation paths, nanowires (NWs) display unmatched properties and hugepotential for application in diverse fields. The ability to construct a nanoscalefunctional system would enable significant advances in the currently desiredminiaturized device integration. To date, the basic properties of all types ofnanowire crystals, including metallic NWs, as well as group IV-related, III-V/II-VI compounds, and metal oxide NWs, are well understood. Regarding futurework, compositional (ie, doping and alloying) and structural (defect andheterostructure) designs to flexibly realize custom-made functionality areemphasized. Along this line, recent progress is reviewed, including the basicproperties (nanowire mechanics, electronics, and photonics) and applicationssuch as photodetectors and chemical/biological sensors. A review of the correlationsbetween the compositional/structural configuration of nanowires and thecorresponding functionality is also presented. The future development directionof this field is concluded and highlighted at the end.展开更多
Two-dimensional materials,especially graphene-like emerging single-element materials two-dimensional(2D)Xenes,have attracted great research interest since the advent of the graphene.In this review paper,12 kinds of di...Two-dimensional materials,especially graphene-like emerging single-element materials two-dimensional(2D)Xenes,have attracted great research interest since the advent of the graphene.In this review paper,12 kinds of different Xenes were introduced according to the group and element quality,and their main synthesis methods are outlined.The advantages and limitations of the synthesis methods are analyzed in detail.By summarizing the current photoelectronic properties of 2D Xenes materials,it is found that Xenes in the same group have similar properties,such as the buckling properties of the fourth group and the anisotropy of the fifth group.In addition,the performance of photoelectronic applications based on 2D Xenes materials are summarized,and some possible methods are proposed to improve the perfor-mance of future 2D Xenes material photoelectronic devices.展开更多
Maximizing wave function overlap(WFO)within type-II superlattices(T2SL)is demonstrated to be important for improving their photoelectric properties,such as optical transition strength and quantum efficiency,which,howe...Maximizing wave function overlap(WFO)within type-II superlattices(T2SL)is demonstrated to be important for improving their photoelectric properties,such as optical transition strength and quantum efficiency,which,however,remains a great challenge for now.Herein,the dual strategy of modulating growth temperature and inserting ultrathin AlAs barrier into the AlSb layers is presented to enhance the WFO in InAs/AlSb T2SL.The charge distributions and strain states indicate that moderate growth temperature of 470°C promotes the As-Sb exchange at AlSb-on-InAs(AOI)interfaces,which would introduce skew of energy band structure towards InAs-on-AlSb(IOA)interface.Such band structure could drive electrons and holes to the IOA interfaces simultaneously,thus resulting in the enhanced WFO.On this basis,insertion of relatively thick(0.3 nm)AlAs layers is found to squeeze more holes towards adjacent interfaces,boosting the WFO further.The InAs/AlSb superlattices with optimized WFO reveal better optical performance,where the peak intensity shows 50%improvement in the PL spectra than the original one.Moreover,a dual-miniband radiative transition mechanism appears in the InAs/AlSb superlattice with relatively thick AlAs intercalation,which helps broaden the wavelength range of the superlattice.展开更多
基金Funded by Chinese National Key Scientific Projects(No.2012CB934303)the Guizhou Education Foundation(KY[2015]332)
文摘Mo-C codoped TiO2 films were prepared by RF magnetron cosputtering. Ultraviolet-visible spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray Analysis and X-Ray Diffraction were used to study the influences of codoping on energy gap, surface morphology, valence states of elements, ions content and crystal structure, respectively. The concentration of photogenerated carriers was measured by studying photocurrent density, while catalytic property was evaluated by observing degradation rate of methylene blue under visible light. A Mo-doped TiO2 film, whose content of Mo had been optimized in advance, was prepared and later used for subsequent comparisons with codoped samples. The result indicates that Mo-C codoping could curtail the energy gap and shift the absorption edge toward visible range. Under the illumination of visible light, codoped TiO2 films give rise to stronger photocurrent due to smaller band gaps. It is also found that Mo, C codoping results in a porous surface, whose area declines gradually with increasing carbon content. Carbon and Molybdenum doses were delicately optimized. Under the illumination of visible light, sample doped with 9.78at% carbon and 0.36at% Mo presents the strongest photocurrent which is about 8 times larger than undoped TiO2 films, and about 6 times larger than samples doped with Mo only.
基金supported by the National Natural Science Foundation of China (Grant Nos. 62075109, 62135011, 62075107, and 61935006)K. C. Wong Magna Fund in Ningbo University。
文摘Antimony selenide(Sb2Se3) films are widely used in phase change memory and solar cells due to their stable switching effect and excellent photovoltaic properties. These properties of the films are affected by the film thickness. A method combining the advantages of Levenberg–Marquardt method and spectral fitting method(LM–SFM) is presented to study the dependence of refractive index(RI), absorption coefficient, optical band gap, Wemple–Di Domenico parameters, dielectric constant and optical electronegativity of the Sb2Se3films on their thickness. The results show that the RI and absorption coefficient of the Sb2Se3films increase with the increase of film thickness, while the optical band gap decreases with the increase of film thickness. Finally, the reasons why the optical and electrical properties of the film change with its thickness are explained by x-ray diffractometer(XRD), energy dispersive x-ray spectrometer(EDS), Mott–Davis state density model and Raman microstructure analysis.
基金supported by Natural Science Foundation of Shaanxi Province Educational Department(No.07JK426)Science Foundation of Xianyang Normal University(No.07XSYK219).
文摘Six novel rod-like magnetic liquid crystals have been prepared, in which trans-bicyclohexyl or trans-cyclohexylphenyl and biphenylcarboxylic acid phenyl ester mesogenic cores with n-propyl and n-pentyl substituents were terminated by 4-hydroxyl- TEMPO (TEMPO = 2,2,6,6-tetramethylpiperidine-l-oxy). Their structures were confirmed by elemental analysis, IR and MS. Determined by SQUID, EPR, DSC and HS-POM (heat stage polarizing optical microscope), the six compounds all have both magnetic and liquid crystalline properties; their temperature ranges of mesophase were from 16.0 to 24.8 ℃, and the magnetic liquid crystal molecules could obviously improve the response sensitivity of liquid crystal materials.
基金supported by the State Key Program of Fundamental Research(G1998061308,and 2002AA3024030).
文摘A new photoresponsive D--A dye, mPS, has been designed and synthesized. Compared to the parent dye PS, IPCE values in the region from 400 nm to 560 nm was greatly improved upon changing the attaching group from the p- position to the o- position of the p-conjugation bridge. A solar cell based on mPS generated a remarkably high overall yield of 5.4% under irradiation of 80.0 mW cm-2 white light from a Xe lamp. Compared with PS, the overall yield ?increased by 64%.
基金Funded by the National Natural Science Foundation of China (No. 60372002)
文摘Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.
基金supported by the National Natural Science Foundation of China(Nos.U1801255,91963210,and 51772339).
文摘In recent years,transparent and flexible materials have been widely pursued in electronics and optoelectronics fields for usage as planar electrodes,energy conversion components and sensing units.As the most widely applied semiconductor material,the related progress in silicon is of great significance although with large difficulty.Herein,we report a one-step method to achieve flexible and transparent silicon nanowires aerogel membrane.A competitive carrier kinetics involving interfacial trapped carriers and the valence electrons transition is demonstrated,according to the photoelectric performance of a sandwiched graphene/silicon nanowires membrane/AI device,i.e.,rapidly positive photoresponse dominated by laser excited^ee-carriers generation(〜500 ms)and subsequent slow negative photocurrent evolution due to laser heating involved multi-levels process(>10 s).These results contribute to fabrication of silicon nanowire self-assembly structures and also the exploration of their optoelectrical properties in flexible and transparent devices.
基金The authors are grateful to financial support from the National Natural Science Foundation of China(Nos.20872035,21076078),and the East China University of Science and Technology.
文摘Two conjugated ethynyl-linked oligomers,oligo(benzodithiophene-ethynylene-benzothiadiazole)(O1)and oligo(benzodithiophene-ethynylene-carbazole)(O2),were synthesized by Sonogashira coupling reaction.Their de-grees of polymerization were 7 and 10,respectively.Their photophysical and electrochemical properties were in-vestigated.O1 exhibitd two strong absorption bands at 404 nm and 483 nm,and O2 at 401 nm and 429 nm.The re-sults of UV-Vis,cyclic voltammetry(CV)and theoretical calculations showed that O1 has a narrower band gap than O2.The conductivities of O1 and O2 were 1.05×10^(−15) and 6.98×10^(−16) S/cm,respectively,and would increase to 1.23×10^(−10) and 1.05×10^(−10) S/cm after doping with iodine.
基金supported by the National Natural Science Foundation of China(Nos.51805220 and 61405078)the Jiangsu University Study-abroad Fund(No.UJS-2017-013)support of the Young Backbone Teacher Cultivating Project of Jiangsu University(No.5521220008)。
文摘An effective method based on laser etching and driving layer strategy was proposed to prepare patterned Ag nanoparticles(Ag NPs)on fluorine-doped tin oxide(FTO)/glass substrate and thus to enhance the photoelectric properties.This method successively included depositing an aluminum-doped zinc oxide(AZO)driving layer,laser etching,depositing an Ag layer,furnace annealing and laser removal.Different AZO and Ag layer thicknesses were adopted,and the surface morphology,crystal structure and photoelectric properties were investigated.An Ag NPs/FTO/glass sample without an AZO driving layer was prepared for comparison.It was found that furnace annealing of the Ag layer combined with the AZO driving layer,rather than that without the AZO driving layer,was more conducive to generating patterned Ag NPs.Using a 20-nmthick AZO layer and a 150-nm-thick Ag layer led to the formation of uniformly distributed Ag NPs being aligned along the laser-etched grooves to form a pattern.The as-obtained sample had the best comprehensive photoelectric property with an average transmittance of 79.95%,a sheet resistance of 7.11Ω/sq and the highest figure of merit of 1.50×10^(-2)Ω^(-1),confirming the feasibility of the proposed method and providing enlightenment for related researches of transparent conductive oxide-based films.
基金Project supported by the National Natural Science Foundation of China(No.51177134)
文摘We give the first report on the experimental investigation of a p-β-FeSi2/n-4H-SiC heterojunction. A β-/%FeSiE/n-4H-SiC heterojunction near-infrared photodiode was fabricated on 4H-SiC substrate by magnetron sputtering and rapid thermal annealing (RTA). Sharp film-substrate interfaces were confirmed by scanning elec-tron microscopy (SEM). The current density-voltage and photoresponse characteristics were measured. The measurements showed that the device exhibited good rectifying properties. The photocurrent density was about 1.82 mA/cm^2 at a bias voltage of -1 V under illumination by a 5 mW, 1.31 μm laser, and the dark current density was approximately 0.537 mA/cm^2. The detectivity was estimated to be 8.8×10^9 cmHzl/2/W at 1.31 μm. All of the measurements were made at room temperature. The results suggest that the p-β-FeSiE/n-4H-SiC heterojunctions can be used as near-infrared photodiodes that are applicable to optically-activated SiC-based devices.
基金Project supported by the National Natural Science Foundation of China(No.61366006)the National Natural Science Foundation of Fujian Province(No.2009J05146)
文摘Indium doped ZnS (ZnS:In) films were prepared on glass substrate using thermal evaporation technol- ogy. It was found that the structural, optical and electrical properties of ZnS:ln films strongly depend on the substrate temperature (Ts). By X-ray diffraction (XRD), atomic force microscopy (AFM), transmittance spectroscopy, and electric performance measurements, the effect of Ts on ZnS:In film is studied in detail. It reveals that Ts has impor- tant effect on ZnS grain size, crystallinity, lattice disorder, etc., which further leads to the obvious influence on its optical and electrical performance. Under the optimized Ts, the performance, especially the conductivity, achieved in this work is far higher than that reported for other n-type ZnS films.
基金This work was supported by Russian Science Foundation(Grant No.15-19-00138).
文摘In the present work,the comparative study of the electric response of Sn_(2)P_(2)S_(6) films to the visible light action was carried out without and under external electric field.The light flux modulated by a chopper induces the integral response comprising time-dependent photoelectric and photovoltaic components.It was shown that spontaneous polarization influences the electric response characteristics.
基金financially supported by the National Key R&D Program of China(No.2017YFB0305401)the National Natural Science Foundation of China(Nos.51874369 and 51871249)the Huxiang Young Talents Plan(No.2018RS3007)。
文摘With the rapid development of indium tin oxide(ITO)in the electronic display industry,choosing which raw powders to prepare high-quality ITO targets has always been a controversial topic.In the work,in order to clearly understand the effect of the raw powders on the microstructure and properties of ITO targets and thin films,tin-doped indium oxide(dITO)and In_(2)O_3-SnO_(2)mixed(mITO)powders were chosen to prepare ITO targets for depositing the films and a comparative study on their microstructure and properties was conducted.It is found that,(1)dITO targets possess a higher solid solubility of tin in indium oxide and more uniform elemental distribution,while there are a higher density,a finer grain size and a higher mass ratio of In_(2)O_3 to SnO_(2)for the mITO targets;(2)dITO films with more coarser columnar grains and a rougher surface prefer to grow along the[100]direction in an Ar atmosphere;(3)the conductive property of ITO films only depends on the doping amount of tin and is independent of the raw powders and the preparation process of the target source;(4)dITO films possess the superior optical property and narrower optical band gap;(5)the etching property of mITO films is superior to that of dITO films due to the lower solid solubility of tin in indium oxide.
基金This work was financially supported by the National Natural Science Foundation of China(Grants U1801255 and 51772339)Fundamental Research Funds for the Central Universities(No.18lgpy05).
文摘As natural one-dimensional confined electron transport channels and photonpropagation paths, nanowires (NWs) display unmatched properties and hugepotential for application in diverse fields. The ability to construct a nanoscalefunctional system would enable significant advances in the currently desiredminiaturized device integration. To date, the basic properties of all types ofnanowire crystals, including metallic NWs, as well as group IV-related, III-V/II-VI compounds, and metal oxide NWs, are well understood. Regarding futurework, compositional (ie, doping and alloying) and structural (defect andheterostructure) designs to flexibly realize custom-made functionality areemphasized. Along this line, recent progress is reviewed, including the basicproperties (nanowire mechanics, electronics, and photonics) and applicationssuch as photodetectors and chemical/biological sensors. A review of the correlationsbetween the compositional/structural configuration of nanowires and thecorresponding functionality is also presented. The future development directionof this field is concluded and highlighted at the end.
基金supported by the Guangdong Natu-ral Science Foundation of China(No.2019A1515010007)the Sci-ence and Technology Innovation Commission of Shenzhen(No.JCYJ20190808175605495)+1 种基金the Key Research Platforms and Projects of Universities in Guangdong Province(No.2020ZDZX3075)the Dongguan Social Science and Technology Development Project(No.2019507140172).
文摘Two-dimensional materials,especially graphene-like emerging single-element materials two-dimensional(2D)Xenes,have attracted great research interest since the advent of the graphene.In this review paper,12 kinds of different Xenes were introduced according to the group and element quality,and their main synthesis methods are outlined.The advantages and limitations of the synthesis methods are analyzed in detail.By summarizing the current photoelectronic properties of 2D Xenes materials,it is found that Xenes in the same group have similar properties,such as the buckling properties of the fourth group and the anisotropy of the fifth group.In addition,the performance of photoelectronic applications based on 2D Xenes materials are summarized,and some possible methods are proposed to improve the perfor-mance of future 2D Xenes material photoelectronic devices.
基金supported by the National Natural Science Foundation of China(Nos.51725101,11727807,51672050,61790581,and 22088101)the Ministry of Science and Technology of China(No.2018YFA0209102)Infrastructure and Facility Construction Project of Zhejiang Laboratory.
文摘Maximizing wave function overlap(WFO)within type-II superlattices(T2SL)is demonstrated to be important for improving their photoelectric properties,such as optical transition strength and quantum efficiency,which,however,remains a great challenge for now.Herein,the dual strategy of modulating growth temperature and inserting ultrathin AlAs barrier into the AlSb layers is presented to enhance the WFO in InAs/AlSb T2SL.The charge distributions and strain states indicate that moderate growth temperature of 470°C promotes the As-Sb exchange at AlSb-on-InAs(AOI)interfaces,which would introduce skew of energy band structure towards InAs-on-AlSb(IOA)interface.Such band structure could drive electrons and holes to the IOA interfaces simultaneously,thus resulting in the enhanced WFO.On this basis,insertion of relatively thick(0.3 nm)AlAs layers is found to squeeze more holes towards adjacent interfaces,boosting the WFO further.The InAs/AlSb superlattices with optimized WFO reveal better optical performance,where the peak intensity shows 50%improvement in the PL spectra than the original one.Moreover,a dual-miniband radiative transition mechanism appears in the InAs/AlSb superlattice with relatively thick AlAs intercalation,which helps broaden the wavelength range of the superlattice.