The banded texture in films prepared from nematic poly (1,4-benzamide) (PBA)/H_2SO_4 solution by shearing and without shearing has been studied by using microscopy techniques. The kinetic parameters of banded texture ...The banded texture in films prepared from nematic poly (1,4-benzamide) (PBA)/H_2SO_4 solution by shearing and without shearing has been studied by using microscopy techniques. The kinetic parameters of banded texture formation γ_c and τ_b were measured for nematic solution of PBA by using parallel-plate shearing apparatus. The banded texture was also observed in randomly packed domains for nematic solution of PBA on standing without shearing. The properties of banded texture show no difference between the two samples with or without shearing.展开更多
A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair...A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair structure formed between the imidazole of PBI and sulfonic acid of S-L-PPO resulted in lowered swelling ratio.It favors to reduce the vanadium permeation.While,the increased sulfonic acid concentration ensured that proton conductivity was still at a high level.As a result,a better balance between the vanadium ion permeation(6.1×10^-9 cm^2·s^-1)and proton conductivity(50.8 m S·cm^-1)in the S-L-PPO/PBI-10%membrane was achieved.The VRFB performance with S-L-PPO/PBI-10%membrane exhibited an EE of 82.7%,which was higher than those of pristine S-L-PPO(81.8%)and Nafion 212(78.0%)at 120 m A·cm^-2.In addition,the S-LPPO/PBI-10%membrane had a much longer self-discharge duration time(142 h)than that of Nafion 212(23 h).展开更多
Two types of the regular copolymer of poly (1, 4-phenyleneterephthalamide) were synthesized by the low temperature solution polycondensation in NMP-CaCl_2 solvent system, using the piperazine or 2,5-dimethylpiperazine...Two types of the regular copolymer of poly (1, 4-phenyleneterephthalamide) were synthesized by the low temperature solution polycondensation in NMP-CaCl_2 solvent system, using the piperazine or 2,5-dimethylpiperazine as the third components introduced in the main chain of poly (1, 4-phenyleneterephthalamide). The properties of copolymers were characterized by IR, SEM, X-RAY diffraction, polarizing microscopy, TGA and solubilities.Experimental results showed that the copolymers had good solubility and thermal stability, the concentrated sulfuric acid (～98% ) solution of regular PPTA copolymers had liquid crystalline proper-展开更多
Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the...Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the methyl groups in solid PPO is partially restricted, which results in a surprisingly efficient spin diffusion between the aromatic proton and methyl proton characterized by a diffusion time of 150 mu s. The results also show that the aromatic ring in solid PPO is rigid and twisted, which causes all aromatic carbons to be chemically unequivalent.展开更多
文摘The banded texture in films prepared from nematic poly (1,4-benzamide) (PBA)/H_2SO_4 solution by shearing and without shearing has been studied by using microscopy techniques. The kinetic parameters of banded texture formation γ_c and τ_b were measured for nematic solution of PBA by using parallel-plate shearing apparatus. The banded texture was also observed in randomly packed domains for nematic solution of PBA on standing without shearing. The properties of banded texture show no difference between the two samples with or without shearing.
基金supported by the National Natural Science Foundation of China(U1808209)Fundamental Research Funds for the Central Universities(DUT18JC40)Liaoning Province Science and Technology Department(201601037)。
文摘A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair structure formed between the imidazole of PBI and sulfonic acid of S-L-PPO resulted in lowered swelling ratio.It favors to reduce the vanadium permeation.While,the increased sulfonic acid concentration ensured that proton conductivity was still at a high level.As a result,a better balance between the vanadium ion permeation(6.1×10^-9 cm^2·s^-1)and proton conductivity(50.8 m S·cm^-1)in the S-L-PPO/PBI-10%membrane was achieved.The VRFB performance with S-L-PPO/PBI-10%membrane exhibited an EE of 82.7%,which was higher than those of pristine S-L-PPO(81.8%)and Nafion 212(78.0%)at 120 m A·cm^-2.In addition,the S-LPPO/PBI-10%membrane had a much longer self-discharge duration time(142 h)than that of Nafion 212(23 h).
文摘Two types of the regular copolymer of poly (1, 4-phenyleneterephthalamide) were synthesized by the low temperature solution polycondensation in NMP-CaCl_2 solvent system, using the piperazine or 2,5-dimethylpiperazine as the third components introduced in the main chain of poly (1, 4-phenyleneterephthalamide). The properties of copolymers were characterized by IR, SEM, X-RAY diffraction, polarizing microscopy, TGA and solubilities.Experimental results showed that the copolymers had good solubility and thermal stability, the concentrated sulfuric acid (～98% ) solution of regular PPTA copolymers had liquid crystalline proper-
文摘Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the methyl groups in solid PPO is partially restricted, which results in a surprisingly efficient spin diffusion between the aromatic proton and methyl proton characterized by a diffusion time of 150 mu s. The results also show that the aromatic ring in solid PPO is rigid and twisted, which causes all aromatic carbons to be chemically unequivalent.